Product Description:

Application: aluminum electrolysis bath side wall, the chemical industry reaction tank, a variety of high temperature abrasion resistant lining board, outlet bricks, furnace heating furnace and the aluminum liquid conveying pipe.

Features: has the advantages of long service life, high hardness, high temperature strength, liquid aluminum erosion and thermal erosion abrasion resistance, anti acid and alkali, corrosion resistance, low linear expansion rate higher characteristic, thermal conductivity.

 

Product name
 
Silicon nitride bonded

silicon carbide products 
 
Chemical composition (%)

 

SiC  ≥ 72.0
 

Si3N4 ≥ 21.0
 

Fe2O3 ≤ 0.3
 

Si ≤ 0.3
 

Display the porosity (%)    
 ≤ 16.0
 

The volume density(g/cm3) 
 ≥ 2.68
 

Compressive strength at room temperature (Mpa)
 ≥ 180.0
 
Flexural strength

(Mpa) 
  

Normalatmospheric temperature

 
 ≥ 45.0
 

1400℃  ≥ 55.0
 

Thermal conductivityλ(W/m·K)

 
The experimental temperature

650℃
 19.5
 

 
The experimental temperature

1000℃
 17.2
 

Coefficient of temperature conductivity

α(cm2/s) 

 
The experimental temperature

650℃
 0.064
 

 
The experimental temperature

1000℃
 0.053
 

Linear expansion rate
 α30—1000
 4.02×10-6(k-1)
 

 α30—1100
 4.06×10-6(k-1)
 

 

Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:How much is the bending temperature aluminum silicon carbide brick for torpedo car
High alumina brick is made of superfine alumina, fused corundum and fused mullite as main refractory materials.
Q:Use of high alumina refractory bricks?
High alumina refractory brick in Al2O3 more, close to neutral refractory material, can resist acid slag and alkaline slag erosion, because it contains SiO2, so alkaline slag ability than acid resistance slag ability less.It is widely used in building blast furnace, hot blast furnace, furnace top, blast furnace, reverberatory furnace and rotary kiln lining. In addition, high alumina bricks are widely used as furnace regenerative checker, pouring system for plug nozzle, etc..
Q:How does the physicochemical index change when the high alumina brick is used at high temperature?
If the range of softening temperature exceeds the load, the constants of other physical and chemical indexes will also increase or decrease.
Q:How can the refractory brick blast furnace be pulverized and pulverized enough not to be taken away by the wind?
Because the hot air outlet of the top burning hot blast furnace is high, the installation requirement of the hot air manifold is high, and the requirement of the strength of the pillar structure is higher, so the rectangular arrangement of the hot blast stove is arranged. The top burning hot blast stove is located on the furnace top because of burner and hot air valve,Therefore, operation, maintenance and installation all require mechanization and automation. Also, because these water cooled valves are mounted with a high elevation,Therefore, the demand for cooling water supply pressure should be improved accordingly, the use of large top burning hot blast stove, the key lies in the design of high-power high-efficiency short flame burner. The top combustion hot blast furnace absorbs the advantages of internal combustion and external combustion hot blast stoves, and overcomes some of their shortcomings,Its structure can meet the requirements of modern blast furnace for high temperature, high pressure and large scale development,Combustion capacity, while meeting production requirements, has been successfully reduced by many devices,
Q:High alumina brick 80 with which high aluminum cement?
In order to maintain a reasonable comprehensive lining, should adopt high quality aluminum refractory mud, such as Sichuan resistance card phosphate refractory mud, refractory clay, high alumina refractory mud PA-80 LN-75, if you use the card volume of Sichuan resistant refractory clay masonry, the effect is better.
Q:How much is one ton of high alumina refractory brick?
High alumina refractory brick according to the different content of AL2O3 is divided into grade, grade one and grade two, and grade three high aluminum brick, Zhengzhou Kang Hui refractories factory price in 800-1900 yuan / ton, stable quality, are exported to the domestic and foreign markets.
Q:Which thermal shock stability of clay brick and high alumina brick is good?
Generally, the thermal shock resistance of high alumina brick products is worse than that of clay brick products
Q:Aluminum content 38. silicon content 55 What refractory bricks?
High alumina brick:The mineral composition of the high alumina brick is determined by the bauxite used. The mineral composition of the clinker is usually mullite, corundum and glass. The theoretical composition of mullite is Al2O371.8%, SiO2 28.2%, and its melting decomposition temperature is 1840 DEG C. With acicular crystal, network cross structure, high temperature state showed better strength. Corundum in the form of alpha -Al2O3, melting point of 2050 degrees, hardness of Mohs 9, showing a granular and columnar crystal, has good chemical stability, acid, alkaline slag have a certain resistance. Based on the composition of mullite minerals, the phase composition of high alumina brick can be judged according to the content of Al2O3. When the bricks are below Al2O3 71.8%, the base of the composition is mullite and SiO2, such as grade LZ-48 bricks. Because it contains a large number of SiO2 formed in the liquid phase under high temperature is 20% ~ 30%; brick in Al2O3 more than 71.8%, the excess Al2O3 formed corundum crystal under high temperature, while generating 2 high temperature phase, eutectic temperature rise by the low content of Al2O3 brick 1595 C to 1840 C, such as grade LZ-75 brick. In fact, it is impossible to produce a complete phase equilibrium in the process of production, but the glass phase is very small, and there is no more than 10% in the partial gap of the Yu Jing phase
Q:The difference between aluminium refractory and magnesia refractory
Magnesia refractory belongs to alkaline refractory materials refers to refractory products such as magnesia magnesia brick magnesium iron spinel magnesium aluminum spinel magnesia ramming materials and other products of raw materials is the main crystal phase is periclase magnesia products
Q:What is the difference between high alumina brick and clay brick?
There must be a difference. They vary in color from the amount of aluminum, the weight, the temperature, and the color. For example: 75 high aluminum and 43 clay bricks, 75 single weight 4.5kg or more. 43 3.65kg or so, the use of temperature 75, high aluminum in about 1520, 43 of brick 1430 or so, the color of 75 pan white, 43 of the Loess color. In short, the difference is great.

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range