Silica Refractory Brick for Glass Furnace

Ref Price:
Loading Port:
Shanghai
Payment Terms:
TT OR LC
Min Order Qty:
15 m.t.
Supply Capability:
30000 m.t./month

OKorder Service Pledge

Quality Product

Order On-line Tracking

Timely Delivery

OKorder Service Pledge

Credit Rating

Credit Services

Credit Purchasing

Share to:

Product Description:

General Information

The silica brick can be widely used in coke oven, hot blast furnace, glass furnace and carbon furnace. In glass industry, it is mainly employed to build the doghouse crown, suspended wall of channel, top crown and inlet sealing. In metallurgy industry, it is adopted as the nozzle brick.

 

Features

1.High purity

2.Long service life

3.Accurate size tolerance

4.Pure color

5. Luster appearance

6..Good thermal conductivity
7.Good creep resistance

Applications

1. Doghouse crown, suspended wall of channel, top crown and inlet sealing of glass furnace

2. High temperature part of coke oven.

 

Physical and chemical index

Item

BG-94

BG-95

BG-96A

BG-96B

Chemical composition

SiO2

≥94

≥95

≥96

≥96

Fe2O3

≤1.5

≤1.5

≤0.8

≤0.7

Al2O3+TiO2+R2O

≤1.0

≤0.5

≤0.7

Refractoriness °C

1710

1710

1710

1710

Apparent Porosity%

≤22

≤21

≤21

≤21

Bulk Density g/cm3

≥1.8

≥1.8

≥1.8

≥1.8

True Density,g/cm3

≤2.38

≤2.38

≤2.34

≤2.34

Cold Crushing Strength Mpa

≥24.5

≥29.4

≥35

≥35

0.2Mpa Refractoriness Under Load T0.6 °C

≥1630

≥1650

≥1680

≥1680

Permanent Linear Change On Reheating

(%)1500°CX2h

0~+0.3

0~+0.3

0~+0.3

0~+0.3

20-1000°C Thermal Expansich10-6/°C

1.25

1.25

1.25

1.25

Thermal Conductivity (W/MK) 1000°C

1.74

1.74

1.44

1.44

 

 

Silica firebrickSilica firebrick


 

Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:Can iron oxide be used as refractory material?
Iron oxide can not be used as refractory material, but it can be used as refractory additive. Iron oxide can be used as pigment
Q:Why will expand when heated brick
Because the production of raw materials are silica brick, brick with SiO2 content of not less than 95% of silica as raw materials, adding mineralizer and binder, through mixing, molding, drying, sintering and other processes in the system
Q:How to improve the thermal conductivity of the coke silicabrick rate?
The content of SiO2 is 98.23% crystalline silica as raw material, with sulfite pulp liquid as binder, millscale and lime as mineralizer, by Jin Hongshi (TiO2) as additive, can improve the rate of thermal conductivity of silica brick for coke oven. When the rutile content is 1.5%, the coefficient of thermal conductivity of silica brick for coke oven is 2.66W/ (m.k).
Q:How to judge the quality of brick, clay brick, high alumina brick furnace from the appearance?
Mainly from the impurities to determine how much, generally less impurity single color brick.
Q:Why is the new trend of the high thermal conductivity of silica brick
The high thermal conductivity of silica brick all inherits the advantages of traditional coke oven silica brick, on the basis of further highlight the characteristics of high thermal conductivity.
Q:Such purpose and scope please give me detailed points thank you because I am learning stage
Acidic silica brick refractory material, has good acid resistance and slag erosion, softening temperature is as high as 1640 to 1670 DEG C, in the long-term use volume is relatively stable under high temperature. The silica mineral phase is mainly composed of tridymite and cristobalite, there is a small amount of quartz and glass. Tridymite and cristobalite and quartz remaining at low temperature due to phase change, volume changes greatly, so the brick thermal stability at low temperature is very poor. In use, under 800 degrees Celsius, slowly heating and cooling, so as not to produce cracks. The use of temperature in blast furnace so should not be below 800 DEG on. The properties and process of silica crystal with SiO2 transformation is closely related, therefore, the proportion of it is one of the important quality indexes of silica brick. General requirements below 2.38, high quality silica brick should be less than 2.35. The true density is small, reflecting a large number of scale quartz and square quartz in the brick, the residual quartz is small, so the residual line expansion is small, and the strength is decreased in useThe raw materials for the manufacture of silica brick. The higher the SiO2 content of silica raw material, the higher the refractoriness. The most harmful impurities are Al2O3, K2O, Na2O and so on. They seriously reduce the refractoriness of refractory products. Brick with SiO2 content of not less than 96% of silica as raw materials, adding mineralizer (e.g. millscale, lime) and binder (such as molasses, sulfite pulp waste liquid), after mixing, molding, drying, sintering and other processes in the system.
Q:Why in the production of the brick to detect the volume density
Density is the property of material, different density of materials, density of the same kind of material is not up to standard, affecting performance.
Q:Glass kiln brick for physical and chemical indicators?
Glass kiln with high quality silica brick with silicon oxide content, low melt index, mainly used for glass kiln crown, parapet, wall hanging, small furnace arch superstructure and regenerator.
Q:What is the effect of the content of silicon nitride in silicon nitride bonded silicon carbide brick on the use of electrobath? Thank you
Small fluctuations in the chemical composition do not have a significant effect on use. The key is the operation of the electrolyzer in production to determine whether the side wall will be damaged.
Q:Why is the highest brick coke oven temperature measuring point temperature not exceeding 1450
That is because the brick load softening point the maximum temperature is 1450 degrees.

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range