Product Description:

General Information of Magnesite Brick

It is made with sintered magnesia and refractory level chrome ore as raw materials. The space between refractory grains is bonded with silicate. The domestic so called magnesia –Chrome bricks .

The refractoriness of magnesia chrome bricks are more than 2000°C,and the refractory under load is a above 1550°C.Good steady volume in high temperature , the performance of meeting sudden cold and sudden hot is better than magnesia bricks.

 

Product features:

1. High refractoriness, excellent anti-oxidation, high strength, perfect thermal 

Stability;

2. Resist the erosion and spall, high abrasion- resistance strength ,

3. Difficult to oxidation and hydration,

4. can be used for long time


Image of Magnesite Brick

Semi - Rebounded Chrome Magnesite Bricks For Metallurgical

Semi - Rebounded Chrome Magnesite Bricks For Metallurgical




Application of Magnesite Brick

Open hearth futnace

Non-ferrous furnace


FAQ

Q2: What`s the lead time for my order?

A2: It depends on customers’ requirements and our production schedule. And usually we need 30-60 days for refractory bricks,10-25 days for unshaped refractory materials and 10-20 days for ceramic fiber blankets.

 

Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:How many kinds of refractory bricks are there?
Magnesia chrome brick: Hang kiln, used for firing zone, the disadvantage is the poor thermal shock resistance, plus six Cr price is highly toxic, the production and use of the national magnesia chrome brick is gradually reduced, the brick production unit as soon as possible to find alternatives.
Q:With different capacitance magnesia brick brick?
Burnt magnesia brick is made of high quality sintered magnesia as main raw materials, paper pulp as binder. After mixing and high pressure molding, it is fired in a high temperature tunnel kiln over 1550 degrees celsius. It has good thermal stability, corrosion resistance and spalling resistance. Widely used in converter, arc furnace and other industrial furnace lining refractory.
Q:What is the difference between magnesia chrome brick and direct bonded magnesia chrome brick?
The magnesium chromium brick with the direct bonded magnesia chrome brick is different: 1 with the purity of magnesia (raw materials) 2: the sintering temperature of common magnesia chrome brick sintering temperature at 1550 DEG ~1600 DEG, direct the magnesium chromium brick sintering temperature is over 1700 DEG C, because of its more than 1700 DEG C, magnesia chrome brick microstructure occurred change, and periclase chromium ore directly combined, so called direct bonded magnesia chrome brick
Q:Refractory brick, high alumina brick, magnesia chrome brick, magnesia brick, clay brick, which type of high temperature refractory brick?
High alumina brick clay brick up to 1700 degrees above 1500 degrees -1750 degrees of magnesia brick and magnesia chrome brick 1500-1650 degrees.
Q:What are the differences between magnesium chrome bricks, such as direct bonding, re bonding, semi bonding, CO sintering and chemical bonding? Hope expert advice..
The process of firing magnesia chrome bricks is roughly the same as that of magnesia bricks. In order to eliminate the brick during firing, due to MgO and Cr2O3, Al2O3
Q:What are the environmental hazards of magnesia chrome refractory bricks?
Nowadays, the use of magnesia chrome bricks, especially in cement kilns in the construction industry, has been required to be free of chromium, and the cement products shall not be tested with chromium.
Q:Process for producing magnesia chrome brick?
The process of firing magnesia chrome bricks is roughly the same as that of magnesia bricks. In order to remove the bricks during sintering, due to MgO and Cr2O3, Al2O3 or direct bonding of magnesia chrome bricks
Q:What is a half combination of magnesia chrome bricks?
Direct binding for magnesium magnesium rock stone or periclase spinel crystals, silicate phases were isolated in the grain asked. Half combined with thermal shock resistance than magnesia chrome brick direct bonded magnesia chrome brick, and about half combined with the characteristics of magnesia chrome brick, some physical and chemical indicators. I don't understand, I know there is a production of magnesia chrome brick factory technicians understand this, is known as gold refractory material factory.
Q:What are the types of magnesia chrome bricks for industrial use?
1. burned magnesia chrome bricks 2. magnesia chrome bricks 3. semi bonded magnesia chrome brick and magnesia chrome brick generally is the three
Q:What are the main raw materials of magnesia chrome bricks?
Magnesium alloys are alloys based on magnesium and other elements. Its characteristics are: small density (1.8g/cm3 magnesium alloy or so), high specific strength, high modulus of elasticity, good heat dissipation, good shock resistance, greater impact load capacity than aluminum alloy, good resistance to organic and alkaline corrosion. The main alloying elements are aluminum, zinc, manganese, cerium, thorium, and a small amount of zirconium or cadmium.

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range