ROTARY KILN BAUXITE 87 WITH HIGH AL2O3 CONTENT

Ref Price:
Loading Port:
China Main Port
Payment Terms:
TT OR LC
Min Order Qty:
-
Supply Capability:
-

OKorder Service Pledge

Quality Product

Order On-line Tracking

Timely Delivery

OKorder Service Pledge

Credit Rating

Credit Services

Credit Purchasing

Share to:

Product Description:

Specification of Calcined Bauxite

Item

Al2O3

(min)

Fe2O3

(max)

TiO2

(max)

SiO2

(max)

KO2+NaO2

(min)

CaO+MgO

(min)

Bulk Density(g/cm3)

70

70%

2.5%

2.9min

75

75%

3.0%

4.0%

8%

0.3%

0.6%

2.7min

80

80%

3.0%

4.0%

8%

0.3%

0.6%

2.8min

85

85%

2%

4.0%

8%

0.3%

0.6%

3.0min

86

86%

2%

4.0%

8%

0.3%

0.6%

3.2min

87

87%

2%

4.0%

7%

0.3%

0.6%

3.2min

88

88%

1.8%

4.0%

7%

0.25%

0.6%

3.25min

90

90%

1.8%

4.0%

7%

0.25%

0.6%

3.25min


Packaging & Shipping

In 1MT jumbo bag or as the buyer request.

We ship the cargo in 20' GP containers,each container loads 25MT/20bags.


Application of Calcined Bauxite

1.aluminium industry


2.precision casting


3 refractory materials


4.aluminum silicate refractory fiber for fiber blanket, refractory brick .


5. refractory cement


Bauxite is an aluminium ore and is the main source of aluminium.


Bauxite is used in cement, chemicals, face makeup, soda cans, dishwashers, siding for houses.


Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:Which plant need to make refractory mould?
Q:What do refractory materials include?
What refractories are included? Refractories include AZS brick, corundum brick, direct-bonded magnesia-chrome, carborundum brick, silicon nitride bonded silicon carbide brick, non-oxide refractory materials such as nitride, silicides, sulfides, borides and carbides, oxidation calcium, chromium oxide, aluminum oxide, magnesium oxide and beryllium oxide.
Q:What is the definition and classification of amorphous fire resistance materials?
9.8. brick made of refractory bone material and powder material can be used directly or after adding appropriate liquid formulation Refractory paint. Refractory slinging material 6. Prefabricated cubes, bonding agent or other additives. fire-resistance sparying material compround additives. Refractory pressed into the material, binder. Refractory ramming material 3, The material is a new fire proof material without calcination Heavy aggregate and lightweight aggregate: Inorganic binding agent and organic bond, its fire resistance is not less than 1580. Refractory castables 2 mouldable refractory Classification according to the type of bonding agent: 1. Classification according to refractory aggregate. According to the production and construction method, refractory mud or refractory mire, with a certain proportion of the mixture
Q:What are the main components of refractory cement?
SiO powder is often used. Ultra-fine powder refers to less than 1 / zm particles which are made by hydrolysis of ethyl silicate or made from recycled dust in the smelting process of ferro-silicon alloy. Non-cement castable refractory are castable refractory material which contains no cement instead it relies on the coagulation and combination by adding ultra-fine powder or sol (see refractory castable), and it is an amorphous material with high activity. Silica sol is made through Ion-exchange of sodium silicate after Na ions are removed. The easiest method is to prepare by reaction of aluminum metal with hydrochloric acid or alchlor. It is a thermodynamically unstable system which has certain requirements for ultra-fine powder and sol. It is different from non-cement refractory castable, Cr2zrOz and etc. It has low impurity content, and can bond with itself, so it has good binding strength. Ultrafine powder used in non-cement castables are SiO2, Al2O3, Cr2zrOz, etc. Such recycled SiO2 powder has an average particle diameter of 0.5 pm, therefore when adding the gelling agent (electrolyte), it can coagulate and give the products some bonding strength. Non-cement castable refractory is made up of refractory aggregate and powder and it is round. Since the use of superfine powder or sol as binder. The size of sol particles are of 0.1 ~ 1 m. Non-cement refractory castable takes oxide or synthetic compound ultra-fine powder or oxide sol-gel which is similar to the chemical composition of material in tungsten castable. There are several ways to prepare alumina sol. The sol used are mainly alumina oxide and silica sol. The surface area is large, and it helps to improve high-temperature structural strength. Non-cement castable refractories rely on oxide ultra-fine powder or sol to coagulate and combinate. It is a refractory castable (also known as chemical bonding castable) which uses chemical binder instead of cement for combination.
Q:What is refractory aggregate?
It includes two categories: coarse aggregate and fine aggregate.
Q:who knows the fire endurance of fireproof coating?
fireproof coating of different thickness differs in its fire endurance. Let me intrduce you as follows: The amount of time of 0.5 hours refractory thickness 0.45mm 0.79kg / m21 hr 0.9 mm 1.5kg / m21.5 hour 1.4 mm 2.3kg / m22 hr 2.0 mm 3.3kg / m22.5 h 2.8 mm 4.6 kg / m2
Q:What are the new refractories? What are the features? How about their application and development?
In metallurgy, in what position should it be used, in order to make the best. Answers are as following. In iron, steelmaking or converter. When questioning, pay attention to the ways. Answers: Try to use synthetic refractory materials.
Q:What are the fire protection standards of insulation materials?
This question is, like this. The combustion performance of thermal insulation materials for exterior walls of all civil buildings, within the scope of fire design auditing and fire control acceptance, should be brought into the auditing and acceptance. As for the "Management Regulations on Supervisions of Fire Prevention and Control for Building Projects" (Ministry of Public Order No. 106) , all civil buildings which are out of the scope of Article 13 and 14 are included in the random check. Before the release of new standard, it must be strictly implemented the Article II of the "Fire prevention Interim Provisions on civil external wall insulation system and external wall decorative" ([2009] No. 46), namely, the insulation materials of civil buildings must use materials with A-level combustion performance.
Q:What's meaning of CN of fire-resistant material?
The commonly used preparation methodsinclude shock compression, high-pressure pyrolysis, ion implantation, reactive sputtering, plasma chemical vapor deposition, electrochemicaldeposition, ion beam sputtering, , low-energy ion radiation, pulsed arc discharge,pulsed laser inducing, etc. But the compounding result of superhard materialis not ideal due to deposition of amorphous CN film, nanometer level sizedC3N4 crystalline grain set in the amorphous film and few large graincrystal.
Q:Who know what kind of fire shutter fire rating are there?
The fire resistance limit of high steel structure reduces the loss of fire, achieves remarkable results. The specification is mae in order to unify the application technical requirements of the design, construction method and quality standard of the steel structure fire retardant coating, and ensure the application effect, safety. The specifications is formulated in accordance with national engineering construction of the relevant policies and "giving priority to prevention, combining fire prevention and fire extinguishing. investigated characteristics of steel structure fire in China, summed up the experience of fire resistant coating for steel structure, and absorb domestic and foreign advanced technology and scientific achievement in fire retardant coatings for steel structures, and repeatedly solicited the relevant scientific research and design, production of construction, colleges and universities, public security department

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range