Refractory Silica Brick for Glass Furnace G-97B

Ref Price:
Loading Port:
Tianjin
Payment Terms:
TT OR LC
Min Order Qty:
15 m.t
Supply Capability:
30000 m.t/month

OKorder Service Pledge

Quality Product

Order On-line Tracking

Timely Delivery

OKorder Service Pledge

Credit Rating

Credit Services

Credit Purchasing

Share to:

Product Description:

General Information

CMAX silica brick using high quality silica as raw material to ensure superior performance of silica bricks, the raw materials is high quality dinas rock with SiO2 of 99% min. Its unique structure helps ease forming. Moreover, advantages of complete transformation after sintering and lower residual quartz enable to produce super-duty silica bricks.    

 

Performance:

The silica bricks for glass furnace is characterized by high purity, less impurity, good corrosion resistance, higher bulk density, complete phase transformation, lower residual quartz, high RUL, lower thermal expansion and stable volume at high temperature. This leads to increase in service life of glass furnace and reduction in energy consumption. These products have found wide application in crown and key areas and been highly appreciated by clients.

 
Application
CMAX Silica bricks are commonly applied in

Coke oven

Hot blast stoves

Glass furnace


Technical Data

  ITEM

For Hot-Blast Stoves

                   For Glass Furnace

  S-94

S-95

  S-95B

  G-94

  G-95A

  G-95B

  G-96A

  G-96B

  SiO2, %

  ≥ 94

  ≥ 95

  ≥ 95

  ≥ 94

  ≥ 95

  ≥ 95

  ≥ 96

  ≥ 96

  Fe2O3, %

  ≤ 1.5

  ≤ 0.5

  ≤ 1

  ≤ 1.5

  ≤ 1.2

  ≤ 1.2

  ≤ 0.8

  ≤ 1

  Residual Quartz, %

  ≤ 1

  ≤ 1

  ≤ 1

  ≤ 1

  Apparent Porosity

  ≤ 23

  ≤ 23(24)

  ≤ 21(23)

  ≤ 24

  ≤ 22(24)

  ≤ 22(24)

  ≤ 22(24)

  ≤ 22(24)

  True Density, g/cm 3

≤ 2.35

  ≤ 2.34

  ≤ 2.33

  ≤ 2.35

  ≤ 2.35

  ≤ 2.34

  ≤ 2.34

  Cold Crushing Strength, Mpa

  ≥ 29.4

  ≥ 30(27)

  ≥ 30(20)

  ≥ 30

  ≥ 30(35)

  ≥ 30(35)

  ≥ 30(35)

  ≥ 30(35)

  Refractoriness Under Load, º C

  ≥ 1650

  ≥ 1600

≥ 1630 

  ≥ 1660

  ≥ 1650

  ≥ 1680

  ≥ 1670

  Permanent Linear Change, %

  1500º CX4h, ± 0.2

  1450º CX2h, ± 0.5

 Refractory Silica Brick for Glass Furnace G-97B

 

Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:What role does silica play in refractories?
The production of clay brick refractory clay raw material is natural, its main mineral is kaolinite (formula Al2O3 - 2SiO2 - 2H2O), clay brick containing SiO2 in 45% ~ 65%, belongs to the weak acid refractory materials, have a certain ability to resist acid slag, but easy to be alkaline slag erosion.
Q:Brick
An acid refractory consisting mainly of quartz and square quartz and a small amount of residual quartz and glass.More than 94% silica content. True density 2.35g/cm3. With acid resistance, slag erosion performance. Higher high temperature strength. The softening start temperature is 1620~1670 degrees. Long term use at high temperature without deformation. The thermal shock resistance is low (the heat exchange in water is 1~4 times). The natural silica is used as the raw material, and a proper amount of mineralizer is used to promote the transformation of quartz into quartz in the body. Slowly sintered at 1350~1430 DEG C in the reducing atmosphere. When heating up to 1450 degrees, the total volume of 1.5~2.2% expands, and the residual expansion can close the kerf and ensure the airtight and structural strength of the masonry.
Q:The hot blast stove when the temperature did not rise against the brick interface decreased
How to keep the brick masonry temperature not lower than 600 DEG C, while the exhaust temperature is not higher than 400 DEG C.
Q:Glass kiln brick for physical and chemical indicators?
Glass kiln with high quality silica brick with silicon oxide content, low melt index, mainly used for glass kiln crown, parapet, wall hanging, small furnace arch superstructure and regenerator.
Q:Such purpose and scope please give me detailed points thank you
Mainly used for coke oven carbonization chamber and the combustion chamber wall, open hearth furnace regenerator and a sediment chamber, soaking furnace, glass furnace, refractory materials and ceramic brick kiln, kiln vault and other load-bearing parts. Also used for high temperature bearing part of hot blast stove and acid open hearth furnace.
Q:How much is the highest melting point of silicon?
. True density 2.35g/cm3. With acid resistance, slag erosion performance. Higher high temperature strength. The softening start temperature is 1620~1670 degrees. Long term use at high temperature without deformation. The thermal shock resistance is low (the heat exchange in water is 1~4 times). The natural silica is used as the raw material, and a proper amount of mineralizer is used to promote the transformation of quartz into quartz in the body. Slowly sintered at 1350~1430 DEG C in the reducing atmosphere. The total volume of heating to 1450 DEG about 1.5~2.2% expansion, the residual expansion will make cutting seam sealing, ensure masonry tightness and good structure strength, so that the brick load softening temperature will reach 1750 degrees Celsius above 1620 degrees in the case of the highest melting point.
Q:Why is the highest brick coke oven temperature measuring point temperature not exceeding 1450
That is because the brick load softening point the maximum temperature is 1450 degrees.
Q:What is the effect of the content of silicon nitride in silicon nitride bonded silicon carbide brick on the use of electrobath? Thank you
Small fluctuations in the chemical composition do not have a significant effect on use. The key is the operation of the electrolyzer in production to determine whether the side wall will be damaged.
Q:The production of brick, the ingredients of why join the waste brick?
Too much addition will reduce the refractory and mechanical strength, increase porosity, so the amount of waste brick should not be too much.
Q:Such purpose and scope please give me detailed points thank you because I am learning stage
Mainly used for coke oven carbonization chamber and the combustion chamber wall, open hearth furnace regenerator and a sediment chamber, soaking furnace, glass furnace, refractory materials and ceramic brick kiln, kiln vault and other load-bearing parts. Also used for high temperature bearing part of hot blast stove and acid open hearth furnace.

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range