Product Description:

General Information

CMAX silica brick using high quality silica as raw material to ensure superior performance of silica bricks, the raw materials is high quality dinas rock with SiO2 of 99% min. Its unique structure helps ease forming. Moreover, advantages of complete transformation after sintering and lower residual quartz enable to produce super-duty silica bricks.    

 

Performance:

The silica bricks for glass furnace is characterized by high purity, less impurity, good corrosion resistance, higher bulk density, complete phase transformation, lower residual quartz, high RUL, lower thermal expansion and stable volume at high temperature. This leads to increase in service life of glass furnace and reduction in energy consumption. These products have found wide application in crown and key areas and been highly appreciated by clients.

 
Application
CMAX Silica bricks are commonly applied in

Coke oven

Hot blast stoves

Glass furnace


Technical Data

  ITEM

For Hot-Blast Stoves

                   For Glass Furnace

  S-94

S-95

  S-95B

  G-94

  G-95A

  G-95B

  G-96A

  G-96B

  SiO2, %

  ≥ 94

  ≥ 95

  ≥ 95

  ≥ 94

  ≥ 95

  ≥ 95

  ≥ 96

  ≥ 96

  Fe2O3, %

  ≤ 1.5

  ≤ 0.5

  ≤ 1

  ≤ 1.5

  ≤ 1.2

  ≤ 1.2

  ≤ 0.8

  ≤ 1

  Residual Quartz, %

  ≤ 1

  ≤ 1

  ≤ 1

  ≤ 1

  Apparent Porosity

  ≤ 23

  ≤ 23(24)

  ≤ 21(23)

  ≤ 24

  ≤ 22(24)

  ≤ 22(24)

  ≤ 22(24)

  ≤ 22(24)

  True Density, g/cm 3

≤ 2.35

  ≤ 2.34

  ≤ 2.33

  ≤ 2.35

  ≤ 2.35

  ≤ 2.34

  ≤ 2.34

  Cold Crushing Strength, Mpa

  ≥ 29.4

  ≥ 30(27)

  ≥ 30(20)

  ≥ 30

  ≥ 30(35)

  ≥ 30(35)

  ≥ 30(35)

  ≥ 30(35)

  Refractoriness Under Load, º C

  ≥ 1650

  ≥ 1600

≥ 1630 

  ≥ 1660

  ≥ 1650

  ≥ 1680

  ≥ 1670

  Permanent Linear Change, %

  1500º CX4h, ± 0.2

  1450º CX2h, ± 0.5

 Refractory Silica Brick for Glass Furnace G-94

 

Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:Common bond brick?
Lime should contain a lot of active CaO, I decompose CaCO3 and MgCO3 not more than 5%, Al2O3+Fe2O3+SiO2 no more than 5%. When the content of large particles, burned Ca-CO3 and over burned lime, the product produced caves, affecting the quality of products.
Q:Brick
The silica mineral phase is mainly composed of tridymite and cristobalite, there is a small amount of quartz and glass. Tridymite and cristobalite and quartz remaining at low temperature due to phase change, volume changes greatly, so the brick thermal stability at low temperature is very poor. In use, under 800 degrees Celsius, slowly heating and cooling, so as not to produce cracks. The use of temperature in blast furnace so should not be below 800 DEG on.
Q:The introduction of silica brick?
An acid refractory consisting mainly of quartz and square quartz and a small amount of residual quartz and glass.More than 94% silica content. True density 2.35g/cm3. With acid resistance, slag erosion performance. Higher high temperature strength. The softening start temperature is 1620~1670 degrees. Long term use at high temperature without deformation. The thermal shock resistance is low (the heat exchange in water is 1~4 times). The natural silica is used as the raw material, and a proper amount of mineralizer is used to promote the transformation of quartz into quartz in the body. Slowly sintered at 1350~1430 DEG C in the reducing atmosphere. When heating up to 1450 degrees, the total volume of 1.5~2.2% expands, and the residual expansion can close the kerf and ensure the airtight and structural strength of the masonry.
Q:Why is the new trend of the high thermal conductivity of silica brick
The high thermal conductivity of silica brick all inherits the advantages of traditional coke oven silica brick, on the basis of further highlight the characteristics of high thermal conductivity.
Q:The hot blast stove when the temperature did not rise against the brick interface decreased
How to keep the brick masonry temperature not lower than 600 DEG C, while the exhaust temperature is not higher than 400 DEG C.
Q:Can not use it two brick
Acidic silica brick refractory material, has good ability in acid slag erosion
Q:The United States of our brick anti-dumping duties?
At present of our brick anti-dumping rate is 73.10%
Q:The difference between clay refractory bricks and refractory brick in the application.
Brick bearing soft temperature and close to the melting point, high temperature strength, can be in high temperature (above 1400 degrees) under the condition of long-term use, but the anti alkali erosion ability, thermal shock stability is the worst, a scrap. The brick is generally used in the coke oven, glass kiln. Other industries basically do not use.
Q:The formula in the refractory brick, and firing curve, who knows?
Iron scale powder 0.45-0.55%, cement 0.9-1.1%, lime milk 6.5-7.5%, pulp 1.95-2.2%, the silica powder, perlite will be added to the wet mill in proportion, and then add iron scale powder, cement, dry roller 1-2 minutes later
Q:Common bond brick
Manufacturing for silica brick binder hi-li sulfate pulp waste liquid and lime milk. When lime milk is used as a bond, it acts as a plasticizer. To increase the strength of lime brick in the drying process, as mineralizer in the firing, promote the transformation of quartz.

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range