Refractory Raw Materials-Silicon Fume SF-92

Ref Price:
Loading Port:
Tianjin
Payment Terms:
TT OR LC
Min Order Qty:
50 m.t.
Supply Capability:
5000 m.t./month

OKorder Service Pledge

Quality Product

Order On-line Tracking

Timely Delivery

OKorder Service Pledge

Credit Rating

Credit Services

Credit Purchasing

Share to:

Product Description:

CMAX Brand Silica fume is a byproduct of producing silicon metal or ferrosilicon alloys.It consists primarily of amorphous silicon dioxide (SiO2),its average granule diameter is 0.15~0.20 µm,specific surface area is 15000~20000 m2/kg.

1.      Very low permeability to chloride and water intrusion.

2.      Extremely high electrical resistivity.

3.      Increased abrasion resistance on floors,highways,marin structures.

4.      Superior resistance to chemical attack from chlorides,acids,sulfates.

 

Grey Densified and undensified Silica fume for cement

Analysis

Result

SF85

SF88

SF90

SF92

SF94

SF96

SF97

SF98

SiO2(%)(min.)

85.05

88.05

99.05

92.05

94.05

96.05

97.5

98.5

Fe2O3 (%)

0.78

0.44

0.21

0.25

0.20

0.20

0.10

0.20

Al2O3 (%)

0.29

0.20

0.21

0.25

0.20

0.20

0.20

0.20

CaO (%)

0.39

0.30

0.36

0.30

0.30

0.30

0.30

0.30

K2O+ Na2O (%)

0.29

0.24

0.22

0.20

0.20

0.20

0.20

0.20

Moisture (%)

3.05

2.55

2.05

2.05

1.85

1.25

1.00

1.00

Loss on Ignition (L.O.I) @975OC (%)

 

Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:what's the classification of fireproof and thermal inuslation matertial?
1. thermal insulation material with A class combustion performance. Rock wool, glass wool, foam glass, foamed ceramics, foam cement, hole-closed perlite (2) thermal insulation material with B class combustion performance: extruded polystyrene board after special processing (XPS)/ polyurethane after special processing (PU) , phenolic aldehyde, gelatine powder polyphenyl granule. 3,thermal insulation material with B2 class combustion performance: molding polystyrene board(EPS), extruded polystyrene board(XPS), polyurethane (PU), polyethylene (PE),etc. sea capacity module and vitrified micro bead(cooperate with the innovator of vitrified micro bead, Liu Weihua) fireproofing issues have been completely solved.
Q:What refractories have good mechanical property resistance and heat expansion and cold contraction property?
Explain that where you use it for and what requirements you have. Follow-up: I use it in metallurgical furnaces with the features of strong stirring and acidic residue.
Q:What's the fireproof specification for constrcution external wall thermal insulation materials?
incombustible material: Class A1 (homogenous): such as YT inorganic active insulation material for wall thermal, foam glass, rock(ORE) wool, glass wool, insulation board of aerogel,expanded perlite series, expaned glazed hollow bead, foam insulation boards, ETC. Class A2 (non-homogeneous composite): such as phenolic foam, gelatine powder polyphenyl granule thermal insulation material, inorganic coating materials and other nonflammable material. phenolic foam insulation board, urea resin foam and board, high flame-retardant polyurethane rigid foam and board, high flame retardant polystyrene cystosepiment, gelatine powder polyphenyl granule heat insulating slurry and other combustible materials. Requirements for combustion levels of common antiflaming EPS, common inflaming retarding XPS, common antiflaming rigid PU foam board: Class A is incombustible material (product); B1 nonflammable material (product); B2 combustible material (product); B3 combustible material (product).
Q:What's the commonly used refractory material for ladle?
1. According to the refractoriness, it can be classified as follows: common refractory: 1580℃ ~ 1770℃; high grade refractory: 1770℃ ~ 2000℃; superrefractory: 2000 ℃; 2. According to the shape and demension of the product, it can be classified as follows: standard form : 230mm×113mm ×65mm of no more than four measuring scale, (demension ratio) Max: Min
Q:I wanna ask about the thermal insulation material fire resistant level?
1. The thermal insulation material of level A combustion performance: Rock wool, glass wool, foam glass, foamed ceramics, foam cement, hole-closed perlite, etc. 2. combustion performance is level B1 insulation materials: Extruded polystyrene board (XPS) after special treatment / Special treatment of polyurethane (PU), phenolic aldehyde and gelatine powder polyphenyl granule 3, combustion performance is level B2 insulation material: Molding polystyrene board (EPS), extruded polystyrene board (XPS), polyurethane (PU), polyethylene (PE), etc. See the 2009 edition construction technical measures 4.3.6 Level A insulation material is only for fireproofing, but its thermal insulation performance is not better than organic XPS \\ EPS and other materials. Thanks
Q:What are first rate fire resistant window materials?
class A window not less than 1.2 hours, class B window not less than 0.9 hours, Class C window not less than 0.6 hours. technical requirments: 1, materials and accessories (1) the window frame is made with a certain strength sufficient to safeguard the integrity and stability of the steel frame or wooden frame. (2) steel frame and mound layer can choose the galvanized steel plate or stainless steel plate. Its selection standards is in line with GB12955 "Steel Fireproof Door General Technical Condition" provisions of Article 5.1. (3) wood frame and mound layer material selected from the standard should be consistent with GB14101 "General Technical Conditions of Wooden Fireproof Door" in the provisions of Article 5.1.1. (4 ) steel, wood frame the inside filler material should be incombustible material. (5) fireproofing glass can be used without affecting the fire windows fire resistance test approved product. light transmittance of glass should not less than 75% of commom sheet glass which is the same number of layers. ( 6) a sealing material between the frame and the fire-resistant glass flame retardant materials should be used, which can play the role of fireproofing and smoke insulation in case of fire (7) hardware fitting should be tested as approved supporting product
Q:What refractories can withstand high temperature above 2100 degrees?
But the price is more expensive, while the insulation performance is not as good as common materials. Is there a material that can withstand 2100 ℃? Currently, the long-term use temperature of the best refractory bricks is about at 1800 ℃, while materilas that can withstand a temperature of 2100 ℃ are relatively rare in the production.
Q:Who knows about the fire endurance of A grade fireproofing glass doors?
The fire endurance of grade A fire resistance rolling shutter doors should be no less than three hours. Fire doors can be divided into A, B and C grades according to their fire endurance which should be no less than 1.20 h, 0.90 h and 0.60h respectively. Places where are difficult to set fire-proof bulkheads can use fire resisting shutters as partitions of fire compartments. The fire endurance of fire resisting shutters that include unexposed surface temperature rise as judging condition should be no less than 3 h. Fire resisting shutters that exclude unexposed surface temperature rise as judging condition should set up independent protection of closed automatic water spray system on both sides of shutters, and the duration of water spray system should be no less than 3.0 h.
Q:What is fire retardant coating mainly used for?
Fire retardant coating is a coating which is applied to the surface of buildings and structures and can form a protective layer of fire retardancy and thermal insulation. It can reduce the flammability of the coated materials and block the rapid spread of fire so as to improve fire endurance of the coated materials. Features of fire retardant coating: (1) Fire retardant coating itself has a flame-retardancy or non-inflammability, and it can prevent the protected substrate from direct contact with the air, and delay ignition and reduce the burning speed of the objects. (2) In addition to flame retardancy or non-inflammability, the fire retardant coating itself has a a low thermal conductivity, which can delay the transfer of flame temperature to the substrate to be protected. (3) When heating, fire retardant coating decomposes non-combustible inert gas to dilute the combustible gas decomposed by the protected, making it difficult to burn or slow down the burning rate. (4) Fire retardant coating containing nitrogen will decomposite NO, NH3 and other basic groups, which compound with the organic radicals and interrupt the chain reaction so as to reduce the temperature. (5) intumescent fire retardant coating will expand and foam when heating, and form a carbon foam insulation to block the protected objects, thus delaying the transmission of heat to the substrate.
Q:What refractories are accessible with ease in daily life?
Refractory mortar. Thermal insulation refractory materials include diatomite products, refractory castables, monolithic refractories, carborundum bricks, gun-mix refractories, semi-silica bricks, borides, beryllia, silicide, calcium oxide, high alumina refractory brick, refractory coatings, corundum bricks, fireclay bricks, silicon nitride bonded silicon carbide bricks, chromium hemitrioxide and other refractories. What refractories can be found mostly in the market? Common refractories. Common refractories include silica bricks. The mostly used unshaped refractories include fettling, ramming refractories, castable refractories, plastic refractories, refractory clay, gun-mix refractory, sling refractories, refractory coatings, lightweight refractory castables, stemming etc. The mostly used insulating refractories include diatomite products, asbestos products, insulation panels, etc. The mostly used special refractories include AZS bricks.

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range