Quick Extruding Silane Cross-Linkable PE Compound for 3KV and Below Cable Wire

Ref Price:
Loading Port:
Shanghai
Payment Terms:
TT OR LC
Min Order Qty:
-
Supply Capability:
1000000kgs kg/month

OKorder Service Pledge

Quality Product

Order On-line Tracking

Timely Delivery

OKorder Service Pledge

Credit Rating

Credit Services

Credit Purchasing

Share to:

Product Description:

Description

Grade 4214Q is sioplas (two steps) silane XLPEcompound for low voltage cable with small cross sectional area, it is composed by silane crosslinkable low density polyethylene (compound A) and silane crosslinkable catalyst (compound B). Compound A is grafted by high activity silane and special PE compound, while compound B adopts the advanced cataly stsystem. The product has outstanding performance and major characteristics are

◆The product is suitable for the extrusion method of squeezing extrusion,half-tubing extrusion and tubing extrusion.

◆Cables made from the product have excellent performance in smooth cable surface, high extrusion speed and production efficiency.

◆Suitable for cable cross-sectional area less than 16mm2.

Standard

Performance test is in accordance with JB/T 10437-2004 standard. After crosslinked in the tepid water, the cable made from the product grade 4214Q can comply with the standard of IEC60502-2004, GB/T12706-2002.

Main Properties & Typical Values

Test items

Test method

Unit

Standard

Typical value

Tensile strength

GB/T1040.3

MPa

≥14.0

19.0

Elongation at break

GB/T1040.3

%

≥350

480

Heat ageing properties (Test temperature 135℃, 168hr)

Maximum tensile strength change

Maximum elongation at break change

GB/T8815

%

%

±20

±20

-12

-5

Heat elongation (200±3)℃x15minx0.2MPa)

Maximum elongation change under load

Maximum permanent elongation change after cooled

GB/T2951

%

%

≤80

≤5

68

-4

Dielectric strength

GB/T1408.1

MV/m

≥30

43*

Volume resistance (20℃)

GB/T1410

Ω.m

≥1.0×1014

3.5×1014*

Gel content

JB/T 10437

%

≥60

60

Typical values were tested on the 1mm sample strip by squeezing film extrusion after mixing compound of A& B (at percentage of 95:5) and be boiled in hot water at 90℃for four hours.

*Especially, these typical values were tested by press moulding sample under the condition of 180±2 ℃, 15min, and pressure over 15Mpa, then boiled in 90℃ water for four hours.

Recommended Processing Technique

1.   Extrusion Equipment

Most extruders for PVC and PE suit for 4214Q.

The recommended equipment and processing technique is as following.

Ratio of length and diameter                    18—25:1

Diameter                                                45—120mm

Ratio of compressing                              1.5—3.5

Ratio of elongation                                  1:1.0—1:1.5

Filtering mesh                                         40/60/40

2.   Extruder processing temperature and other related settings

Temperature Setting:  Specific processing temperature should bebased on different equipment and pressing conditions, reference settings are as following:

Feeding section(℃)

Compression Section(℃)

Measurement Section

(℃)

Die head and Mould

(℃)

150~165

165~175

175~190

190~200


Die head setting:
Squeezing extrusion style, half-tubing extrusion style and tubing extrusion style

Cooling water temperature: Should not beless than 25℃,gradual cooling water tank is recommended.

   

3.   Crosslink

After extrusion and cooling, the cable can be crosslinked by immersed in hot water (90℃) or exposed in low pressure vapour. The time required for crosslink is based on the thickness of the insulation and the coil size, the thicker the insulation and the greater the coil size, the longer the crosslink time required. The crosslink time canbe calculated according to the equation of 4hr/mm for 90℃.


Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range