Q:After the long-term use of non stick pan, oil stains can not be effectively removed, over a long period of time in the non stick coating on the formation of a layer of coke, the effect of losing non stick. As a result of this layer of coke is relatively dense and smooth, scouring cloth has been ineffective, steel ball can not be used to damage the coating, what chemical or physical methods to remove this layer of coke?

After such a toss, the coke pot was removed, but the bottom layer of the so-called "nonstick layer" are often the early damage (normally always destroyed), it is impossible to. It's like trying to get rid of terrorists.If the bottom of the layer of carbon black is not easy to erase, even if, even with good. Some people may worry about eating into the carbon poisoning, I think there is no need to worry about this. Wenchuan earthquake hero, Mr. Zhu Jianqiang, light to eat charcoal for 36 days, you can see the toxicity of carbon nothing. Moreover, after cleaning the rice cooker in the layer of carbon black has very little

Q:The total amount of heat released by the fully burnt 200g coke is 60% by mass of 10kg water absorption [q coke =3.0 * 107J/kg, C water =4.2 * 103J/ (kg = C)], q:(1) how much heat is absorbed by water?(2) if the initial temperature of water is 10 degrees C, then, after absorbing heat, the temperature will rise to how much?

Dry water temperatures:Delta t=Q ceilingC water m water=3.6 x 106J4.2 x 103J/ (kg * c) * 10kgC = 85.7,At the end of a water temperature t=t0+ t=20 C +85.7 =105.7 oc,

Q:What kind of coke is needed for smelting special steel

3) skeleton: smelting process in blast furnace is gas rise and decline occurred in the opposite charge of movement and interaction, the core permeability is the key operation of blast furnace. In the upper column, gas flow distribution of coke layer; in the middle of the column material, the coke from the skeleton effect, support has been melting the iron ore, the normal gas rise; in the lower column, high temperature in the solid massive existing coke and has become liquid hot metal and slag mixed together, become loose skeleton gas rising and falling iron and slag.

Q:What is coke and how is coke classified?

Coke definitionBituminous coal in the absence of air is heated to 950-1050 DEG C, after drying, pyrolysis, melting, bonding, curing and contraction of the final stage of this process is made of coke, coking high temperature (high temperature carbonization). By high temperature coking coke for blast furnace smelting, casting and gas generated in the process of coking. After the recovery and after the purification of coke oven gas is not only a high calorific value of fuel, and is an important raw material for organic synthesis industry. Metallurgical coke is coke, coke, iron alloy coke and non-ferrous metal smelting coke for metallurgical coke collectively. More than 90% were used for blast furnace ironmaking blast furnace coke, so often referred to as metallurgical coke is coke. The special cupola molten iron and coke. Coke is the main fuel cupola molten iron. It is melting charge and molten steel overheating, the support column to maintain its good permeability. Therefore, coke should have Large blocks, low reactivity, porosity is small, with impact crushing strength, low ash and sulfur enough.

Q:the CO reduces the iron oxide, and the part of CO burns, and the whole process will release a lot of heatCheck information, combined with the knowledge of the professional knowledge, for reference purposes only!

Please see standard: metallurgical coke GB/T1996-2003, all clear

Q:The sulfur content of coal and coke in general, the coking process of sulfur content of coal into the output of sulfur content of coke compared to those who are high and low?

Of course, the sulfur content of coke is low. Coke quality requirements: two grade coke containing sulfur below 0.7%

Q:How to determine the maturity of coke or not?

The degree of fragmentation of coke: refers to the different levels of coke accounted for the percentage of total coke production. The particle size of coke is very important in blast furnace smelting. The coke block is uniform, the gap is large, the resistance is small, and the furnace condition runs well.Breaking strength of metallurgical coke (M40 drum index)The breaking strength of metallurgical coke is an index to reflect the breaking resistance of coke.Wear resistance of metallurgical coke (M10 drum index)The wear resistance of metallurgical coke is an index to reflect the wear resistance of coke.

Q:8 points will be isolated from the air to enhance the heat of coal, in addition to the main coke, but also the material listed in the following table: No.

The structure of benzene and toluene is similar, and the molecular composition is different from that of a CH2 atom cluster, which is called homologous;(5) the number of chloro compounds in the hydrogen molecule is equal to the number of hydrogen atoms in different environments, and toluene has four kinds of hydrogen atoms in different environments: methyl group on the top, the benzene ring on the top of the 3 species, and so on, there are 4 kinds of chlorine compounds in toluene,

Q:Coke and coal is one thing

Coke is bituminous coal under the condition of isolated air, heated to 950-1050 DEG C, after drying, pyrolysis, melting, bonding, solidification, shrinkage and other stages of the final coke, this process is called high temperature coking (high temperature carbonization).Coke is a deep processing of coal products.

Q:Why in the blast furnace ironmaking with coke instead of charcoal why coke can produce heat to improve the heat of the furnace how to produceWhy in the blast furnace ironmaking with coke instead of charcoal why coke can produce heat to improve the heat of the furnace how to produce

The reaction of the blast furnace ironmaking is the reduction reaction: the coke produces CO in the furnace, the CO reduces the iron oxide, and the part of CO burns, and the whole process will release a lot of heatCheck information, combined with the knowledge of the professional knowledge, for reference purposes only!