Metallurgical Coke Size 30-90mm

Ref Price:
Loading Port:
China Main Port
Payment Terms:
Min Order Qty:
Supply Capability:
100,000MT m.t./month

OKorder Service Pledge

Quality Product

Order On-line Tracking

Timely Delivery

OKorder Service Pledge

Credit Rating

Credit Services

Credit Purchasing

Share to:

Product Description:

Metallurgical Coke Size 30-90mm




Total Moisture  (As received basis)

5%  max

Ash (dry basis)

12.5% max

> 13.5%

Volatile Matter (dry basis)

1.5% max

> 1.8%

Sulphur (dry basis)

0.65% max

> 0.75%

Phosphorus (dry basis)

0.035% max

> 0.045%


7% max

> 9%


84% min



64% min



26% max

> 28%

Size 30-90   mm

90% min

+90   mm

5% max

> 8%


5% max

> 8%


To be used for blast furnace in steel plants

Main Features of the Product

   Low ash

   Low sulphur

   Ready to ship in stock


Inspectorate at loading port to be final to bothparties in quality and quantity

Packaging & Delivery

1. Packaging: in bulk

2. Delivery: loading rate of 8,000 mt PWWD SHINCat Tianjin port

Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:What is the main purpose of the use of coke
(2) reducing agent.The reduction of ore in blast furnace is accomplished by indirect reduction and direct reduction. The indirect reduction is about 400 degrees centigrade. The indirect reduction is rising gas CO reduction in ore, iron oxide from high iron gradually reduced low iron until the metal iron, while producing CO2:
Q:The difference between semi coke and coke
Coke is used for smelting iron alloy coke, and the coke is used in blast furnace and used for copper, lead, zinc, titanium, antimony, mercury and other non-ferrous metal smelting of blast furnace, reducing agent, heating agent and columnar skeleton.
Q:What is the difference between coke and coking coal
Coking coal is a kind of bituminous coal with a high degree of deterioration, and the thermal stability of the resultant colloid is good when the coke is produced separately. The block size of the coke is large, the crack is small and the strength is high
Q:What does the M40% and M25% mean in the analysis of coke?
(1) crushing strength (shatter strength): the ability of a certain particle size coal sample to fall under the condition of free fall.
Q:Who knows the proportion of pig iron and coke used in Cupola
There are doubts: blank parts output is too low.3, blank export rate: raw materials into melting after the formation of blank, under normal circumstances, the common casting investment for every 1 tons of pig iron, scrap steel and other major raw materials, the lowest to 85% iron, after casting output blanks, nozzle, nozzle, riser, riser for iron smelting water ratio of about 30%; blank standard export rate, nozzle, riser re melted continue after put into use; production enterprises invested 1 tons per dryer, iron scrap and other major raw materials to the lowest 85% of the hot metal, roughly the same with ordinary casting, casting blank after the (standard yield) for hot metal ratio is about 70%, water riser for hot metal ratio is about 15%, and the same outlet riser re melted after continued use.
Q:What does Coke test index M25 mean?
. Coke crushing strength refers to coke can resist foreign impact force without ability along cracks or defects at the broken, represented by the M40 value; wear strength of coke coke refers to the ability to resist external friction without surface of glass forming debris or powder, said M10. The cracking degree of coke affects the M40 value of its breaking strength, and the pore structure of coke affects the M10 value. There are many methods for determination of M40 and M10, our method using migon drum test in Germany.
Q:Why use coke instead of carbon in blast furnace ironmaking
The reaction of the blast furnace ironmaking is the reduction reaction: the coke produces CO in the furnace, the CO reduces the iron oxide, and the part of CO burns, and the whole process will release a lot of heatCheck information, combined with the knowledge of the professional knowledge, for reference purposes only!
Q:How coal is turned into coke in the coking chamber
The kiln chamber wall set to continue burning, and some heat incoming kiln (indirect heating). High temperature gas flow (800 DEG C, is mixed with coal pyrolysis, chemical products into the fabric of unburned.
Q:What's the connection between coking coal and coke
Coke: the quality is hard and the hole is thick, the short hair will be wiped awayCoking coal is a kind of bituminous coal with medium caking property and strong caking property. The title of bituminous coal with high degree of coalification. Main coking coal.
Q:How to remove the bottom of coke steel
Two, with cooking shovel (Mason's Pihui knife is best) to remove surface soft.Three, the same with a spade close to the bottom of the pot to eradicate. Until the last thing left is black.Four, wash the metal wire ball friction force discoloration, and always use water to clean out the dirt.

1. Manufacturer Overview

Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range