Q:With the number of 1 tons of steel smelting coke

The use of coke pig iron smelting blast furnace, for each different, which is each blast furnace coke ratio (the ratio of the iron smelting a ton of coke by iron determined how many meals). The country or the world, the iron and steel enterprises coke are not the same, the coke rate is as low as possible, but there are many factors which restrict the level of coke, such as advanced level equipment, raw material and fuel quality, or the operator level, advanced process and so on many factors which influence

Q:What is coke and how is coke classified?

Types of cokeCoke is usually divided by use of metallurgical coke (including blast furnace coke, coke and iron alloy coke, calcium carbide and coke gasification etc.) with coke. The pressurized pulverized coal forming coal, coke carbonization etc. in the new postprocessing process called Formcoke.

Q:the CO reduces the iron oxide, and the part of CO burns, and the whole process will release a lot of heatCheck information, combined with the knowledge of the professional knowledge, for reference purposes only!

Thermal strength index: CSR CRIM40 M25 is the bigger the better, the smaller the better M10CSR the bigger the better the smaller the better CRISpecific standards to see the specific requirements of steel mills

Q:Braised meat burning coke, iron black layer, I do not know how to clean, please help answer

If the paste pot may wish to try the following several waysBrush pot1, with hot water can be, it is easy to wash, do not use wire brush the ball, put the pot brush bad, if it is aluminum brush used for cooking after eating on the body is very good. (if you must brush it, you can use the cloth to replace the steel ball)

Q:Coke is how to participate in the steel, and the pellets, sintering, a piece of the furnace in the furnace or in other containers

. It is necessary to add coke, pellet, sinter ore, ore and other materials into the blast furnace according to a certain proportion, batch and order

Q:Listen to a lot of people say that steel is now coke is not true?

With the rapid development of the domestic and international iron and steel industry, the demand for coking products is increasing rapidly, the investment is heating up, and the industry is expanding rapidly. But the coking industry of high resource consumption, production and emissions, especially the emissions of harmful substances, causing serious waste of resources and environmental pollution, brings great pressure to the sustainable development of national economy, which also hindered the rapid development of coking industry.

Q:What are the companies that produce coke

Very much, what kind of coke do you want, our company would like to buy coke particles

Q:Standard grade two grade coke standard

Quality index of cokeCoke is a solid product of high temperature carbonization, the main component is carbon, is a crack and irregular pore structure (or porous). The number of cracks has a direct impact on the strength and crushing strength of the coke, the index is generally measured in terms of crack degree (the number of cracks in the unit volume coke). The index of pore structure is mainly expressed by the porosity rate (the percentage of the total volume of coke), which affects the reactivity and strength of coke. Different uses of different coke porosity index requirements, the general requirements of metallurgical coke porosity in the 40 ~ 45%, 35 ~ 40% in coke, coke export demand in about 30%. Coke crack degree and the porosity level, and the coking coal has a direct relationship, such as coal based coke refining, crack, high porosity, low strength; with coal as the foundation of the coal refining coke crack less, low porosity and high strength. The strength of coke is usually represented by two indices of crushing strength and abrasion resistance. Coke crushing strength refers to coke can resist foreign impact force without ability along cracks or defects at the broken, represented by the M40 value; wear strength of coke coke refers to the ability to resist external friction without surface of glass forming debris or powder, said M10. The cracking degree of coke affects the M40 value of its breaking strength, and the pore structure of coke affects the M10 value. There are many methods for determination of M40 and M10 value method, commonly used in our country the German migon drum test.

Q:Who knows the proportion of pig iron and coke used in Cupola

Raw material inputs: the main raw material for casting pig iron, scrap steel, manganese, etc.. Under normal circumstances after the melting of ordinary cast iron scrap iron and scrap steel ratio of 9:1 or so, the drying enterprises use pig iron and scrap ratio of about 6:4, according to the requirements of the product. Because pig iron and scrap carbon content is not the same, the higher the carbon content of pig iron is about 4 ~ 4.3, low carbon steel scrap, about 0.8.

Q:What is the density of coke?

The true density of coke: 1.8 ~ 1.95kg/cm3; apparent density: 0.8 ~ 1.08kg/cm3; pile density: 400 ~ 500kg/cm3