Magnesium brick for blasting furnace System 1

Magnesium brick for blasting furnace

Ref Price:

Loading Port:: Qingdao

Payment Terms:: TT OR LC

Min Order Qty:: 1 pallet

Supply Capability:: 5000 pallet/month

Inquire Now

Chat Online

Add to My Favorites

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

You Might Also Like

Fireclay Brick RN40

High Alumina Brick ALP85

Insulating Fire Brick - GJM23

$Magnesium refractory bricks for cement kiln$

Magnesium refractory bricks for cement kiln

Corundum-Mullite Bricks for furnace

$Fused Magnesite/large crystal fused magnesia/LCFM/Magnesium carbon refractory bricks$

Fused Magnesite/large crystal fused magnesia/LCFM/Magnesium carbon refractory bricks

$High temprature insulation Fireclay Refractory brick$

High temprature insulation Fireclay Refractory brick

$China Supplier Fire Resistant Brick Zircon Glass Kiln Refractory Brick$

China Supplier Fire Resistant Brick Zircon Glass Kiln Refractory Brick

Features of Magnesium brick for blasting furnace

1.Resisting high temperature

2.Great bulk density

3.Low iron content

4.Good eroding resistance

Applications of Magnesium brick for blasting furnace :

1. Steel furnaces

2. Iron making furnaces

3. Glass kiln

4. Ceramic tunnel kiln

5. Cement kiln

Our competitive Advantage:

1.Competitive Price. Make the products competitive in your market.

2.Abundant Experience. Prevent cracks and twist in bricks.

3.Different Moulds. Save mould fees for you.

4.Lower ferric Oxide,porosity,higher refractoriness,density,higher CCS and exact tolerance.

5.Strict Quality Control. Meet clients’ quality requirement.

6.Safty packing,prompt delivery time,and excellent after-sales services.

7.Large stocks. Guarantee prompt delivery.

8.Professional Packing. Avoid damage and secure the goods in transportation

Specifications of Magnesium brick for blasting furnace :

Item	HA60	HA70	HA75	HA80
AL2O3(%)	≥60	≥70	≥75	≥75-80
SIO2(%)	32	22	20	≥18
Fe2O3(%)	≤1.8	≤1.8	≤1.8	≤1.8
Refractoriness °C	1790	>1800	>1825	≥1850
Bulk density,g/cm3	2.4	2.45-2.5	2.5	2.55-2.6
Softening temperature under load	≥1470	≥1520	≥1530	≥1550
Apparent porosity,%	22	<21	<21	<20
Cold Crushing strength Mpa	≥45	≥50	≥54	≥60

Phosphate bonded high alumina bricks

Item	LAP75	LAP77	LAP85
AL2O3 %	≥75	≥77	≥80-85
Fe2O3 %	≤3.0	≤3.0	≤1.8
Ca0 %	≤0.6	≤0.6	≤0.6
Refractoriness °C	≥1800	≥1800	≥1850
Bulk density g/cm3	≥2.65	≥2.70	≥2.80
Cold crushing strength MPa	≥60	≥64	≥110
Refractoriness under load 0.2MPa °C	≥1350	≥1300	≥1350
Application	Used for high temperature parts lining of cement rotary kiln	Used for Badly worn parts of cement rotary kiln

Q:With different capacitance magnesia brick brick: Burnt magnesia brick is made of high quality sintered magnesia as main raw materials, paper pulp as binder. After mixing and high pressure molding, it is fired in a high temperature tunnel kiln over 1550 degrees celsius.

Q:Manufacture of various refractory magnesia brick mainly comes from Magnesium Oxide, what kind of ore?: Manufacture of various refractory magnesia brick Magnesium Oxide, mainly from magnesite.

Q:Combined with the ordinary clay brick and magnesia brick as an example, the existence of impurities in minerals and refractories production main components of the formed liquid relative what affect the performance.: The main varieties of common magnesia brick, magnesia brick, magnesia brick, magnesia brick high pure grade. Product main mineral phase is periclase, volume has high stability and anti erosion ability. Literature is widely used in steelmaking, non-ferrous metal smelting and other high-temperature industrial furnace.

Q:Process for producing magnesia chrome brick: The fine powder compacts after calcination produced by magnesia - chrome ore grinding method, brick with magnesia coarse particles, are effective measures to eliminate the effect of loose. Compared with the common magnesia chrome brick, the magnesia chrome brick made by this method has lower porosity, higher compressive strength, higher softening temperature and higher flexural strength. Compacts with chrome magnesite powder, magnesia chrome brick by synthetic magnesia chrome sand made of high-temperature calcination, slag resistance and high temperature strength are better than other magnesite chrome brick.

Q:What is the ratio of magnesia refractory bricks to brine? For example, what is the difference between the 97 and 95 with 92 brick brick brick material mixed with brine ratio?: Different grades of burned magnesia brick is mainly made of magnesia binder with different taste, there is not a big difference. However, the physical and chemical properties of binders should be controlled well!

Q:How to identify the fused magnesia brick and sintered magnesia brick: Magnesia brick have high refractoriness, alkali slag good performance, high load softening temperature, but poor thermal shock resistance. The sintering magnesia brick brick magnesite as raw material, crushing, proportioning, mixing, forming, in 1550 ~ 1600 degrees firing, high purity products firing temperature is over 1750 DEG C. Don't add chemical bond magnesia brick is appropriate in magnesia, through mixing, molding and drying.

Q:The index of magnesia brick: indexMGe-20 MGe-16 MGe-12 MMGe-8 DBMK-A DBMK-B DBMK-C MgO≥（%） 40 45 55 60 80 80 80 Cr2O3≤（%） 20 16 12 8 6-8 6-8 6-8 SiO2≤（%） --- --- --- --- 2.0 2.5 3.0

Q:Refractory brick, high alumina brick, magnesia chrome brick, magnesia brick, clay brick, which type of high temperature refractory brick?: High alumina brick clay brick up to 1700 degrees above 1500 degrees -1750 degrees of magnesia brick and magnesia chrome brick 1500-1650 degrees, I is the production of clay brick, brick my temperature at 1500-1700 degrees. Specific depends on what kiln, brick is only part of it

Q:Brick price?: Refractory brick series sintered magnesia brick, magnesia chrome brick, magnesia brick, magnesia spinel brick, magnesia calcium brick, unburned magnesia chrome brick, magnesia brick, magnesia calcium brick, magnesia brick, and al2o3-mgo-c bricks.

Q:Magnesia brick: Mainly used for basic open hearth, furnace bottom and furnace wall oxygen converter steelmaking, the permanent lining of non-ferrous metal smelting furnace, high temperature tunnel kiln, calcined magnesia brick and cement rotary kiln, furnace bottom and furnace wall, glass furnace regenerator etc..

1. Manufacturer Overview
Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates
a) Certification Name
Range
Reference
Validity Period

3. Manufacturer Capability
a)Trade Capacity
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range