Magnesium Alloy Ingot Rod Good Quality Magnesium Metal Ingot

Ref Price:
Loading Port:
Tianjin
Payment Terms:
TT OR LC
Min Order Qty:
5 m.t.
Supply Capability:
20000 m.t./month

OKorder Service Pledge

Quality Product

Order On-line Tracking

Timely Delivery

OKorder Service Pledge

Credit Rating

Credit Services

Credit Purchasing

Share to:

Product Description:

1. Specification:The Mg Metal is a fairly strong, silvery-white, light-weight metal.

Magnesium Alloy Ingot Rod Good Quality Magnesium Metal Ingot


Form: ingot

ingot: (8 ± 0.5) kg / ingot 

Specifications: (50-55)cm×(11.5-13.5)cm×(7-7.5)cm


2. Application:

1. The high temperature at which magnesium burns makes it a useful tool for starting emergency fires during outdoor recreation. Other related uses include flashlight photography, flares, pyrotechnics and fireworks sparklers. 

2. To photoengrave plates in the printing industry. 

3. In the form of turnings or ribbons, to prepare Grignard reagents, which are useful in organic synthesis.

4. As an additive agent in conventional propellants and the production of nodular graphite in cast iron.                  

5. As a reducing agent for the production of uranium and other metals from their salts.                   

6. As a sacrificial (galvanic) anode to protect underground tanks, pipelines, buried structures, and water heaters.


3. Mg Alloys Metal (Ingot)

 

Mg ingot


Brand

chemical composition

 

Mg


Fe

Si

Ni

Cu

Al

Cl

Mn

Ti

others


Mg99.98

99.98

0.002

0.003

0.002

0.0005

0.004

--

0.002

--

0.02


Mg99.96

99.96

0.004

0.004

0.0002

0.002

0.006

0.003

0.003

--

0.04


Mg99.95

99.95

0.004

0.005

0.0007

0.003

0.006

0.003

0.01

--

0.05


Mg99.90

99.90

0.04

0.01

0.001

0.004

0.02

0.005

0.03

--

0.10


Mg99.80

99.80

0.05

0.03

0.002

0.02

0.05

0.005

0.06

--

0.20


 

4. Advantages:

Good Quality ............... The most important factor we care.

Competitive Price ........ For our mutual benefit.

Prompt delivery ........... Abundant production ability, storage ability and manpower.

Excellent Service ......... Customer always first.

Now our main markets in Asia and Europe, to the future we will set up sales network in more than 200 countries around the world. 

 

Magnesium Alloy Ingot Rod Good Quality Magnesium Metal Ingot

Magnesium Alloy Ingot Rod Good Quality Magnesium Metal Ingot

Magnesium Alloy Ingot Rod Good Quality Magnesium Metal Ingot

What is Magnesium Alloys?

Magnesium alloys are mixtures of magnesium with other metals (called an alloy), often aluminum, zinc, manganese, silicon, copper, rare earths and zirconium. Magnesium is the lightest structural metal. Magnesium alloys have a hexagonal lattice structure, which affects the fundamental properties of these alloys. Plastic deformation of the hexagonal lattice is more complicated than in cubic latticed metals like aluminium, copper and steel; therefore, magnesium alloys are typically used as cast alloys, but research of wrought alloys has been more extensive since 2003. Cast magnesium alloys are used for many components of modern automobiles, and magnesium block engines have been used in some high-performance vehicles; die-cast magnesium is also used for camera bodies and components in lenses.

 

Practically, all the commercial magnesium alloys manufactured in the United States contain aluminum (3 to 13 percent) and manganese (0.1 to 0.4 percent). Many also contain zinc (0.5 to 3 percent) and some are hardenable by heat treatment. All the alloys may be used for more than one product form, but alloys AZ63 and AZ92 are most used for sand castings, AZ91 for die castings, and AZ92 generally employed for permanent mold castings (while AZ63 and A10 are sometimes also used in the latter application as well). For forgings, AZ61 is most used, and here alloy M1 is employed where low strength is required and AZ80 for highest strength. For extrusions, a wide range of shapes, bars, and tubes are made from M1 alloy where low strength suffices or where welding to M1 castings is planned. Alloys AZ31, AZ61 and AZ80 are employed for extrusions in the order named, where increase in strength justifies their increased relative costs.

5.FAQ

We have organized several common questions for our clients,may help you sincerely: 

①How about your company?

CNBM, The Fortune 500. A world class manufacturer & supplier of magnesium alloys ingots plates&sheets, magnesium alloy bars, Magnesium alloy slabs,magnesium alloy wires,magnesium alloy tubes and etc.. bases in China.

②How to guarantee the quality of the products?

We have established the international advanced quality management system,every link from raw material to final product we have strict quality test;

We would like to offer free samples for your inspect and check.

We have advanced manufactured equipments,such as hot rolling equipment. We resolutely put an end to unqualified products flowing into the market. At the same time, we will provide necessary follow-up service assurance.

③What is your main markets?

Our main markets are from Europ, America and Aisa. Such as Germany,Czech, Poland, England, Canada, Korea, Turkey etc.

Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:What is magnesium aluminum alloy and what is its use?
Magnesium alloy molecular formula: Mg4Al3 molecular weight: 178.22 color is brown, the proportion is about 2.15g/cm3, the melting point of 463 DEG C, when combustion temperature reaches 2000 DEG -3000 DEG. In fireworks production process plays a very important role in reducing agent, can also be used as white lighting agent and agent.
Q:Will the enterprises that produce sponge titanium use magnesium ingots?
The essence of magnesium reduction is at 880 DEG ~950 DEG under argon atmosphere, let four titanium chloride and magnesium were obtained by the reaction of sponge titanium and magnesium chloride, magnesium chloride removal in titanium sponge and excess magnesium by vacuum distillation to obtain pure titanium by distilled condensate molten metal recovery magnesium, magnesium chloride by molten salt electrolysis recovery of magnesium and chlorine. The process of producing titanium from refined four titanium chloride is divided into two steps: reduction and distillation. For a long time, reduction and distillation are all step by step, but now they are tending to be combined and large-scale.
Q:Causes of high manganese content in magnesium ingot
Potassium Permanganate heat decomposition of potassium manganate, manganese dioxide and oxygen, and the quality of solid oxygen generating surplus.
Q:The industrial application of magnesium and the main title and technical difficulty of producing magnesium products with magnesium chloride as raw material
The chemical property of magnesium is active, in the metallurgical industry by using, steel and non-ferrous metal casting, with magnesium as desulfurization agent, cleaning agent, as reducing agent in the production of rare metal. In the chemical industry, magnesium can be used as a dehydrating agent of organic compounds or directly with organic compounds and preparation of magnesium powder. In recent years, in the use of magnesium powder spray, coating, anticorrosion industry is more and more big, the amount of silicon and polysilicon and powder metallurgy die casting is also great.
Q:What are the generally feasible surface treatment methods for magnesium alloy die castings?
You ask is the appearance of the surface treatment of magnesium alloy, magnesium alloy because of the limited potential difference, so the appearance of the surface treatment on magnesium alloy or zinc alloy as Aluminum Alloy appearance easy or style, the general appearance of the 1 surface treatment) surface temperature paint, 2) anodic oxidation treatment, 3) chemical nickel plating, plating surface treatment, 4) 5) 6) electrophoresis surface treatment, surface coating treatment, 7) PVD appearance. As for the surface of phosphoric acid, chromic acid, manganese and other chemical immersion solution or to do what should be included in the sandblasting, surface oxidation treatment, and drawing, engraving and so on processing is additional processing surface appearance of another way. Basically, it looks like aluminum alloy or zinc alloy, but the key point is that the process is different from the technical complexity. So the reason why the general magnesium alloy is more difficult to produce is that it is here.
Q:What is the black powder on the surface of magnesium ingot AM50A?
AZ91D, the most widely used magnesium alloy, has high strength and excellent casting performance. It is used in motorcycles, computer parts, housings, and lids
Q:What harm does magnesium alloy have to human body?
The main element of magnesium aluminum alloy and AZ91D is magnesium. As long as it is not dust (flammable or explosive), direct contact with magnesium ingot is harmless
Q:What are the differences between aluminium magnesium alloy, aluminum alloy and plastic steel?
An alloy based on aluminum. The main alloying elements are copper, silicon, magnesium, zinc and manganese. The minor alloying elements are nickel, iron, titanium, chromium, lithium and so onAluminum alloy low density, but relatively high strength, close to or higher quality steel, plastic good, can be processed into various profiles, with excellent conductivity, thermal conductivity and corrosion resistance, widely used in industry, the use of only steelAluminum Alloy divided into two categories: cast Aluminum Alloy, cast under; deformation Aluminum Alloy, can withstand the pressure processing, mechanical properties than cast. Aluminum Alloy material can be processed into various forms and specifications. Mainly used in the manufacture of aviation equipment, daily necessities, building doors and windows.
Q:What are the surface defects of magnesium alloy rolling?
When the deformation rate is too large, it is easy to cause serious cracking.
Q:Why the cost of ferrosilicon production will lead to a rebound in the price of magnesium ingot?
75# ferrosilicon in pidgeonmagnesiumprocess often used in high temperature smelting process of magnesium metal, will be replaced from CaO.MgO mg, each ton of magnesium will consume 1.2 tons of ferrosilicon, plays a big role in magnesium production.

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range