Magnesite Cassani Polishing Brick with High Efficiency

Ref Price:
Loading Port:
Qingdao
Payment Terms:
TT OR LC
Min Order Qty:
10 m.t.
Supply Capability:
100000 m.t./month

OKorder Service Pledge

Quality Product

Order On-line Tracking

Timely Delivery

OKorder Service Pledge

Credit Rating

Credit Services

Credit Purchasing

Share to:

Product Description:

Dry processing direct bonded chrome magnesite bricks Description:

It is mainly made of top class silica, via shaping and burning under the high temperature,

Possesses high temperature resistant, high strength and low impurities, etc.

It is mainly used for blast furnaces and hot blast stove.

 

Dry processing direct bonded chrome magnesite bricks Advantage:

1) Silicon oxide is above 95%.

2) Good acid erosion resistance.

3) High softening point

 

Dry processing direct bonded chrome magnesite bricks Applications:

Light weight silica bricks are primarily used for furnaces and kilns in metallurgy, steel, power, chemical industry, and electric power and machine building etc areas 

 

Dry processing direct bonded chrome magnesite bricks specifications:

 

 

Direct-Bonded Magnesia-Chrome Brick

Main Application:It’s mainly applied to line the sintering zone of the new dry-processing of cement kilns and glass tank furnaces as checkers and the other industrial furnaces.

Chemical & Physical Data

Brand

MgO %

Cr2O3 %

SiO2 %

A.P. %

BDg/cm3

CCS.MPa

R.U.L ℃

DBMGe-8A

≥74

≥8

≤1.5

≤18

2.98

≥40

1660

DBMGe-8B

≥74

≥8

≤2.0

≤18

2.98

≥35

1600

DBMGe-12A

≥66

≥12

≤1.5

≤18

3.1

≥40

1660

DBMGe-12B

≥66

≥12

≤2.0

≤18

3.1

≥35

1600

DBMGe-16A

≥60

≥16

≤1.5

≤18

3.15

≥40

1660

DBMGe-16B

≥60

≥16

≤2.0

≤18

3.15

≥35

1600

 

 

Rebonded Magnesia-Chrome Brick

Main Application:It’s suitable for lining of the slag zone area of refining furnaces of VOD,SKF.

Chemical & Physical Data

Brand

MgO %

Cr2O3 %

SiO2 %

A.P. %

BDg/cm3

CCS.MPa

R.U.L ℃

RBMG-16A

≥65

≥16

≤1.2

≤16

3.1

≥45

1750

RBMG-16B

≥60

≥16

≤1.6

≤16

3.1

≥40

1700

RBMG-20A

≥60

≥20

≤1.2

≤16

3.15

≥45

1750

RBMG-20B

≥60

≥20

≤1.2

≤16

3.15

≥40

1700

 

 

Semi-Rebonded Magnesia-Chrome Brick

Main Application:It’s widely used for every industrial furnaces of the metallurgical and building materials industry.

Chemical & Physical Data

Brand

MgO %

Cr2O3 %

SiO2 %

A.P. %

BDg/cm3

CCS.MPa

R.U.L ℃

SBMG-16A

≥60

≥16

≤1.5

≤17

3.1

≥40

1750

SBMG-16B

≥60

≥16

≤1.8

≤17

3.1

≥35

1700

SBMG-20A

≥55

≥20

≤1.5

≤17

3.15

≥40

1750

SBMG-20B

≥55

≥20

≤1.8

≤17

3.15

≥35

1700


Magnesite Cassani Polishing Brick with High Efficiency


FAQ

Q2: What`s the lead time for my order?

A2: It depends on customers’ requirements and our production schedule. And usually we need 30-60 days for refractory bricks,10-25 days for unshaped refractory materials and 10-20 days for ceramic fiber blankets.

 

Q3: Can you offer Door-to-Door delivery?

A3: Yes, but only for some countries such us U.S., UAE, Saudi Arabia, Iran, and Russia, etc.


Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:Can the fire clay to be reused?
Refractory soil cannot be reused.Clay refractory soil 1, characteristics and uses: Clay refractory brick is a weak acid refractory material, its thermal stability is good, suitable for hot air furnace, all kinds of boiler lining, and flue, smoke room, etc.. 2, product specifications form: standard shape, general, special-shaped and special-shaped brick. Physical and chemical properties of fireclay bricks.
Q:What material is good for refractory brick?
1, silicon aluminum refractory bricks mainly include the following.(a) is the main varieties of acidic silica brick, refractory brick. It is mainly used for coke oven building, also used in furnaces all kinds of glass, ceramic and carbon calciner, refractory brick arches and other load-bearing parts, is also used in high temperature bearing part of hot blast stove, but should not be used in thermal equipment below 600 DEG C and the temperature fluctuation in the.(two) clay brick is a refractory brick commonly used in blast furnaces, hot blast furnaces, heating furnaces, power boilers, lime kilns, rotary kilns, ceramics and refractory bricks.(three) the mineral composition of high alumina refractory brick and high alumina refractory brick is corundum, mullite and glass phase. The raw materials are high alumina and sillimanite natural ore. They are also made of fused alumina, sintered alumina, synthetic mullite and calcined alumina in different proportions with clay. It is produced by sintering process. But the products are casting brick, brick, brick fused grain and unshaped refractory brick. High alumina refractory brick is widely used in iron and steel industry, non-ferrous metal industry and other industries.
Q:What are the specifications for brick?
Ordinary brick size of 240 mm * 115 mm * 53 mm, according to compressive strength (Newton / square millimeter, N / mm2) size is divided into MU30, MU25, MU20, MU15, MU10, MU7.5, these intensity levels. Clay brick materials, cheap, durable, and fire prevention, heat insulation, sound insulation, moisture absorption and other advantages, is widely used in civil engineering. Waste brick can also be used as aggregate of concrete. In order to improve the shortcomings of ordinary clay bricks, such as small, self important and waste of soil, they are developing in the direction of light weight, high strength, hollow and big blocks.
Q:Outside wall tile (whole body smooth surface has small hole split brick) has cement pollution, with what product cleaning (cement, mortar, cleaning agent)?
Ordinary brick size of 240 mm * 115 mm * 53 mm, according to compressive strength (Newton / square millimeter, N / mm2) size is divided into MU30, MU25, MU20, MU15, MU10, MU7.5, these intensity levels. Clay brick materials, cheap, durable, and fire prevention, heat insulation, sound insulation, moisture absorption and other advantages, is widely used in civil engineering. Waste brick can also be used as aggregate of concrete. In order to improve the shortcomings of ordinary clay bricks, such as small, self important and waste of soil, they are developing in the direction of light weight, high strength, hollow and big blocks.
Q:What's the use of refractory bricks?
Refractory bricks are mostly used in the lining of furnaces of high temperature industries. Such as iron and steel industry, blast furnace, hot blast furnace, converter, colored reverberatory furnace, rotary kiln, etc.
Q:How are qualitative and qualitative refractories understood?
Shaped refractory products, such as fired brick, fused brick (Rong Zhuzhuan), refractory insulation bricks, as well as experimental and industrial crucibles, utensils and other special products.
Q:What are the forming methods of refractory materials?
Casting molding is suitable for casting brick, electric melting brick and so on. And the machine press forming is the most widely used. The common refractory brick, clay brick and other sintered brick are adopted this method.
Q:What is the weight of the refractory bricks?
Fireclay refractory bricks: 3.4kg-3.8kg - according to the quality of raw materials, prices ranging from 1 yuan to 2.7 yuan, high alumina refractory brick: three, high aluminum in 3.9kg or so. Ordinary T-3 firebrick weight calculation method: 230*114*65*2.2/2.1.
Q:What is brick power, half brick power and full brick power difference?
Power module. Small size, high power. General use should order additional storage energy, heat dissipation, etc.. Dimensions such as brick, so called brick power supply. Half brick power supply is half the size of all brick power supply.
Q:What are kiln bricks?
Referred to as refractory brick. Refractory made from refractory clay or other refractory material. Light yellow or brownish. The utility model is mainly used for laying smelting furnaces, and can withstand high temperature between 1580 DEG C and 1770 DEG C. Also called brick. Refractory material of a certain shape and size. According to the preparation process can be divided into bricks, brick, electric melting brick (Rong Zhuzhuan), the refractory insulating bricks; according to the shape and size can be divided into standard brick, brick, brick and other specific type. It can be used as high temperature building materials and structural materials for construction kilns and various thermal equipments, and can undergo various physical, chemical and mechanical changes at high temperature. For example, refractory clay brick, high alumina brick, brick, brick etc..

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range