Product Description:

Description:

The products are fused magnesia as main raw material, after a reasonable size distribution, high pressure forming, high-temperature sintering. The product has strong resistance high temperature dimensional stability. Mainly used in glass furnace regenerator, the upper part.

 

It is a kind of alkaline refractory product with perriclase as main phase magnesia alumina spinel clinker as basic material .The product has such characteristics as good temperature vibration, good strength and volume stability in high temperature.

 

Application:

 1. The regenerative chamber for the ceramic frit kiln, sodium silicate and glass furnace;

2. The furnace lining of iron and steel industry, such as ferroalloys furnace, metal mixer;

3. The non-ferrous metallurgy industrial furnace lining, such as the furnace copper, lead, zinc, tin, etc;

 

Advantage:

1.Competitive Price. Make the products competitive in your market.

2.Abundant Experience. Prevent cracks and twist in bricks.

3.Different Moulds. Save mould fees for you.

4.Lower ferric Oxide,porosity,higher refractoriness,density,higher CCS and exact tolerance.

 

Typical features:

Magnetite bricks, magnetite-alumina bricks and magnetite-zircon bricks etc are the main products of basic refractories. The products have the properties of bearing high temperature, high refractoriness under load and good resistance to alkali. They are widely used in the basic zone of metallurgical furnaces, nonferrous furnaces and regenerator of glass furnaces.

 

 

Technical data:

 .png

FAQs:

Q1  What’s the transport method?

A1  FCL delivery goods with wooden pallet or wooden case by sea; If LCL delivery, must with wooden case; Sometimes need open top, flat rack or bulk cargo.

Q2  What’s the required payment term?

A2  Generally 30% TT as the prepayment, 70% TT before delivery. If need, 100% Irrevocable Letter of Credit or negotiation.

Q3  Which country are our products exported to?

A3  Apart from entire Chinese market, the US, Russia, Japan, Korea, Australia and some Southeast Asian Nations


Magnesite Alumina Spinel Brick for Firing Zone, Magnesia Alumina Spinel Bric

Magnesite Alumina Spinel Brick for Firing Zone, Magnesia Alumina Spinel Bric


Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:Refractory brick, high alumina brick, magnesia chrome brick, magnesia brick or clay brick, which type of high temperature refractory brick?
High alumina brick clay brick up to 1700 degrees above 1500 degrees -1750 degrees of magnesia brick and magnesia chrome brick 1500-1650 degrees, I is the production of clay brick, brick my temperature at 1500-1700 degrees. Specific depends on what kiln, brick is only part of it
Q:Manufacture of various refractory magnesia brick mainly comes from Magnesium Oxide, what kind of ore?
The ore quality requirements of MgO = 41%, CaO = 6%, SiO2 = 5%. The resources of magnesite in China are rich. The types of deposits include sedimentary metamorphic deposits, sedimentary hydrothermal metasomatic deposits and weathering leaching deposits.
Q:What is the ratio of magnesia refractory bricks to brine? For example, what is the difference between the 97 and 95 with 92 brick brick brick material mixed with brine ratio?
In addition to the brine binder burned magnesia brick and sulfite pulp waste liquid, Magnesium Sulfate solution binder is generally around 3%
Q:The index of magnesia brick
Room temperature compressive strength≥(MPa)(15-25-)24.5-24.5-24.5-24.5-40-40-40
Q:High purity magnesia brick masonry mortar for what?
High purity aluminum is 99.99, the first is not pollution, the stove is high magnesia brick masonry, 95% and 97% purity magnesia brick is for a long time did not find a good bit of fireclay, do not know what to build, now used light burned US powder and heavy burned magnesium plus brine built, with 2 months a griddle doesn't stick on magnesium brick, a touch off, there is no good sintering
Q:Process for producing magnesia chrome brick
The fine powder compacts after calcination produced by magnesia - chrome ore grinding method, brick with magnesia coarse particles, are effective measures to eliminate the effect of loose. Compared with the common magnesia chrome brick, the magnesia chrome brick made by this method has lower porosity, higher compressive strength, higher softening temperature and higher flexural strength. Compacts with chrome magnesite powder, magnesia chrome brick by synthetic magnesia chrome sand made of high-temperature calcination, slag resistance and high temperature strength are better than other magnesite chrome brick.
Q:How to identify the fused magnesia brick and sintered magnesia brick
Burnt magnesia brick is made of high quality sintered magnesia as main raw materials, paper pulp as binder. After mixing and high pressure molding, it is fired in a high temperature tunnel kiln over 1550 degrees celsius. It has good thermal stability, corrosion resistance and spalling resistance. Widely used in converter, arc furnace and other industrial furnace lining refractory.Fused magnesia brick brick has compact structure, high mechanical strength, low impurity content, mainly used for the storage of large glass kilnHigh temperature area of the room. The fused magnesia is made of high quality magnesia as raw material. It is made by melting. The English name is fused magnesite. Magnesium hydroxide from magnesite or brucite or from sea water is calcined at high temperature. Strong hydration resistance.
Q:Magnesia brick
Magnesia brick have high refractoriness, alkali slag good performance, high load softening temperature, but poor thermal shock resistance. The sintering magnesia brick brick magnesite as raw material, crushing, proportioning, mixing, forming, in 1550 ~ 1600 degrees firing, high purity products firing temperature is over 1750 DEG C. Don't add chemical bond magnesia brick is appropriate in magnesia, through mixing, molding and drying
Q:Magnesite chrome brick, magnesia chrome brick indicators? What is the price?.
If you want to know the indicators of chrome brick, magnesia chrome brick must know you are in what furnace above, there is in what position
Q:With different capacitance magnesia brick brick
It has good thermal stability, corrosion resistance and spalling resistance. Widely used in converter, arc furnace and other industrial furnace lining refractory.

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range