Low Density And High Strength Kiln Fireclayinsulating Brick

Ref Price:
Loading Port:
Tianjin
Payment Terms:
TT OR LC
Min Order Qty:
1 m.t.
Supply Capability:
10000000 m.t./month

OKorder Service Pledge

Quality Product

Order On-line Tracking

Timely Delivery

OKorder Service Pledge

Credit Rating

Credit Services

Credit Purchasing

Share to:

Product Description:

fire-resistant  low porosity fireclay  brick 

Features:

1. Low bulk density, low thermal conductivity, good thermal performance.

2. Refractory category allow direct contact of fire, suitable for various atmosphere

3. Good integrity with furnace lining, long service life, easy operation, could be shaped freely

Typical Applications:

1. Furnaces of metallurgy industry, heat treatment furnace

2. Furnaces of chemical industry and construction industry.

3. Furnace of incineration of garbage, recirculating fluidized bed furnace 


Low Density And High Strength Kiln Fireclayinsulating Brick

Specification:

                        Low Porosity Fireclay Brick 

                Index 
Item                

                                               Low Porosity Fireclay Products

DN-10

DN-12

DN-15

DN-18

AL2O3 % ≥

45

 45

42

42

Fe2O3 % ≤

1.00

1.20

1.65

1.80

Bulk Density≥ g/cm3

2.40

2.35

2.30

2.25

A.P. % ≤

10

12

15

18

C.C.S (Mpa) ≥

70

65

60

48

    Refractoriness ≥ °C

     1750

1750

1750

1750

Reheating Linear Change%

1400°C×2h

-0.1~+0.05

1400°C×2h

-0.1~+0.05

1400°C×2h

-0.2~0

1400°C×2h

-0.4~0

0.2mpa Refractoriness under loadT0.6 ≥ °C

1500

1470

1450

1400



FAQ

Q3: Can you offer Door-to-Door delivery?

A3: Yes, but only for some countries such us U.S., UAE, Saudi Arabia, Iran, and Russia, etc.

 

Q4: What is the minimum quantity?

A4: There is no minimum order quantity. Depending on the item and processing, there may be a minimum production required, however we can offer a quotation based only on the quantity you need.

 

Q5: Can you give me a brief introduction of the application of your products?

A5: CNBM (China National Building Material) core refractory business comprises the production, sale and installation of high-grade refractory products, the development and implementation of customized system solutions as well as rendering outstanding services for the key industries in Glass, Iron& Steel, Petrochemical, Cement, Ceramic and Nonferrous Metals.


Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:Which is better for tunnel kiln suspended ceiling, refractory brick or ceramic fiber module ?
Refractory bricks is better.
Q:what is application of high alumina refractory brick?
reverberatory furnace 1, close to the neutral refractory, but because mullite crystallization has not formed the network organization, so the load softening temperature is not higher than silica brick. the refractoriness of high alumina brick is higher than fireclay brick and semi-silica brick, mainly used in blast furnace, nozzle brick,etc. it is up to 1790 C~ 1750, can resistance to acid slag and alkaline slag erosion. hot blast furnace, blast furnace, high alumina brick are widely used for producing open-hearth furnace regenerative bricks, because it contains SiO2, low impurity content, which belongs to high-grade refractory materials, electric furnace. 2, plug head used in pouring system . In addition. 3, because high aluminum products contains more Al2O3, forming less fusible vitreous body, so the high load softening temperature is higher than clay brick. because rotary kiln lining, slag resistance of high alumina refractory brick contain more Al2O3, so the ability of anti alkaline slag is weaker than anti acid slag. so it has a wide range of application. high alumina refractory brick due to the following performances
Q:the refractory brick in glass furnace burner was burning, the bricks on both sides of the fire hole were burning the blocked it, what will cause brick burning?
The firebrick in glass melting furnace is mainly consisted of zircon brick, other ordinary refractory materials can not effectively prevent the erosion of glass solution. Because the glass melting liquid is eutectic mixture compared to the refractory bricks, it penetrates into the refractory brick and reduces its original performance, simply speaking, the glass melting liquid dissolves the refractory bricks as eutectic mixture .
Q:Are refractory bricks necessarily needed to build a kitchen stove?
The kitchen stove is used to cook dinner, so refractory bricks are unnecessarily needed. It depends on the temperature.
Q:What is the meaning of the new type of dry rotary kiln refractory brick 620,320?
It should be the length of the turn. I'm not sure if it is right.
Q:Do cement kiln refractory bricks have quality guarantee period? can them still be used for a long time's pile?
They of course can be used. The plant will produce some bricks for standby application in advance, so they put for a period of time is completely no problem
Q:What is the advantage for ceramic fiber material compared with refractory brick?
Heat capacity; excellent thermal shock resistance, good chemical stability, bearing sudden cooling and heating, without oven heating and cooling ,high speed, energy saving, is 1/8 of refractory brick, construction is simple. ceramic fiber materials and refractory brick belong to refractory insulation materials; low thermal conductivity: Low bulk density, ceramic fiber material is a new type of lightweight thermal insulation material, is one of the 10 points of lightweight refractory brick,
Q:How to make the adhesion between refractory brick and the inner wall of the boiler more firm?
High temperature resistance can also extend its service cycle. If there are conditions for the user heat resistant steel welding nails. By using high temperature high alumina brick, expansion joints can not be too large, with high-temperature adhensive paste masonry, recommend that you use the refractory brick, add the amount of long pieces of brick or rachel brick
Q:Why is there cracks in the use of refractory bricks?
Several reasons for the emergence of cracks: (1) temperature difference stress (2) mechanical stress (3) crystal type change stress
Q:how much fireclay is needed for 10000 refractory bricks?
The amount of mud used for T-3 refractory brick is 0.3KG. if the tiler is skillful, the furnace should have joint of 2mm.

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range