Insulating Fire Brick for various kilns

Ref Price:
Loading Port:
Tianjin
Payment Terms:
TT OR LC
Min Order Qty:
20 m.t.
Supply Capability:
20000 m.t./month

OKorder Service Pledge

Quality Product

Order On-line Tracking

Timely Delivery

OKorder Service Pledge

Credit Rating

Credit Services

Credit Purchasing

Share to:

Product Description:

Insulating Fire Brick Technical index

Product No.

IFB70

IFB60

IFB50

IFB40

Al2O3

68%-72%

58%-62%

48%-52%

38%-40%

Refractoriness (°C )

≥1790

≥1790

≥1790

≥1790

Bulk density (g/cm3)

2.50-2.60

2.35-2.45

2.20-2.30

2.10-2.20

Apparent porosity (%)

22

19-22

17-20

17-20

Cold Crushing strength (kg)

480-510

450-480

430-450

390-430

Application

Insulating Fire Brick are used for the lining of converter, alternating current arc furnace, direct Current arc furnace and the ladle slag line, etc.

 

Equipment 

1 unit of Ceramic Abrasive (SG Abrasive) pilot production line

2 units of Compact grain Abrasive pilot production lines

1 unit of high-end coated abrasives (abrasive cloth) production line

2 units of Boron Carbide production lines

3 large flexible crushing and sieving lines for grit production lines

2 units of 2000KVA furnaces for Boron Carbide fusion

6 units of 5000KVA-10000KVA dumping type electric arc furnaces for Brown Fused Alumina fusion

 

Company Advantage

(1)Long Insulating Fire Brick manufacture history: 25 years manufacturer 

(2)Advanced equipment

(3)Diversification of production standards: ISO ANSI FEPA JIS ASTM

(4)Flexible payment: T/T L/C D/P D/A

(5)Professional marketing team and after-sale service

(6)Free sample

 

 

 

Q1

 

What’s the transport method?

 

A1

FCL delivery goods with wooden pallet or wooden case by sea; If LCL delivery, must with wooden case; Sometimes need open top, flat rack or bulk cargo.

 

Q2

 

What’s the required payment term?

 

A2

Generally 30% TT as the prepayment, 70% TT before delivery. If need, 100% Irrevocable Letter of Credit or negotiation.

 

Q3

 

Which country are our products exported to?

 

A3

Apart from entire Chinese market, the US, Russia, Japan, Korea, Australia and some Southeast Asian Nations.

 

Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:What kind of refractory brick is suitable for 24*28m rotary kiln of 5,000 tons?
Magnesium spinel
Q:What are the differences between thermal insulation bricks and refractory bricks?
Thermal insulation brick is thermal insulative; refractory brick is high temperature resistant.
Q:does furnace use refractory cement to make refractory bricks?
consistence Mainly concern about the strength, generally masonry mortar does not consider the degree of fire resistance
Q:Why are the refractory bricks near to rotary kiln tyre easy to be short lives?
Q:Expansion ratio of light corundum fireproofing brick
And then the appropriate drying, the using temperature 1500~1700 degrees of light corundum brick, the porosity is 70% to 80% Now, use foaming method to produce light corundum brick, 3g/, shaped idiosome with mould dry for 4 days in 60 degree to 70 degree oast, it will demoulding, foaming method and evaporating method produce light corundum brick, the thermal conductivity is 0. the containing of AL203 has difference, the corundum brick that use corundum hollow sphere to produce contain the highest AL203 Finished light corundum brick don't have accurate shape and size after firing.8 1, so products need mechanical or manual cutting after the kiln, finally, firing in 1300 degree and 1550 degree, basically still meters with water forming, just add to burn: 50~60h, because its production methods and the introduction of additives are different, the total sintering time.17W/, light corundum fireproofing brick can be made into density is 0, withstand voltage strength is 4MPa, the containing of A1203 is no more than 99%.
Q:What's the reason of cracks in refractory bricks?
If it is made to refractory bricks,dry in the air naturally for 10 days, then put into the drying furnace, which is certainly better than the brick is put to the furnace directly, this is not easy to crack. After all, the moisture of brick will run in the air. See the semi-finished products (not crack is really no crack), but after drying, it has cracks, this is must because moisture runs quickly in a short time. If it cracks after high temperature heat treatment, the reason is very complicated, such as after high temperature burning, temperature decreases too fast, resulting in a large temperature change, then it cracks. Or in the process of high temperature heat treatment, the internal reaction is intense, and generate some volume expanding materials, resulting in cracks and so on. Mullite Petrochemical reaction, spinel reaction and so on, the reactions of a lot of materials are the volume expansion
Q:What types of refractory bricks are divided into?
Chimney and flue are places that high temperature gas of sulfur gathers, it should use acid material. Refractory material is divided into three major parts: acid, neutral and alkaline.
Q:several refractory brick of rotary kiln several is damaged, how many refractory bricks should be replaced?
In general, if the brick inside the kiln break or loose core, the bricks of whole circle should be replaced, if only mend by replacing a damage part is also ok, but the service life is shorter.
Q:Blend 12% fireclay and 88% refractory cement. Moderate water and mud are used to pile up firebricks?
Refractory bricks can irectly be liner. Lightweight mullite brick can be used for relatively longer time. If there is no mullite brick, use mud said above for some time, then continue to use by patching up.
Q:Is the waste of the fire resistant hazardous waste?
it mainly depends on whether the refractory bricks contain chromium, if not, we only need to properly dispose of them, it would cost less and assure that there is no bad effect on people and the environment, shoot two hawks with one arrow; if there is hazardous elements like chromium and mercury, it may cost much and be disposed as industrial waste(or construction waste) by local environmental protection department, it is ok if there is a large amount of waste, because the environmental protection department will not take those waste that is not obviously dangerous seriously, even if it is dangerous waste. If there is no suitable manufacturers. It is better to look for a refractory brick manufacturers to recycle it, the cost is acceptable if the amount is small. In general, these heavy metal containing refractory bricks need to be disposed by the company that has quality to dispose such hazardous waste.

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range