High Quality Bauxite High Alumina Refractory Brick Dry Pressed Block of CNBM in China

Ref Price:
Loading Port:
Tianjin
Payment Terms:
TT or LC
Min Order Qty:
11 m.t.
Supply Capability:
10000000 m.t./month

OKorder Service Pledge

Quality Product

Order On-line Tracking

Timely Delivery

OKorder Service Pledge

Credit Rating

Credit Services

Credit Purchasing

Share to:

Product Description:

1.Structure of Calcined Bauxite Description

Bauxite (aluminous soil; Bauxite) is also called the alumina or bauxite, main ingredients are alumina, hydrated alumina containing impurities, is an earthy mineral. White or gray, brown and yellow or light red by iron.  From 4 to 3.9 g/cm3 density, hardness, 1 ~ 3 is not transparent, very brittle.  Very difficult to melt.  Insoluble in water,  soluble in sulfuric acid, sodium hydroxide solution. Mainly used for aluminium, refractory material. 

 

2.Main Features of the Calcined Bauxite

Calcined bauxite is one of the principal ore of aluminum. Calcined bauxite contains hydrous aluminum oxides and aluminum

hydroxides, formed through the laterization of aluminous rocks in tropical and subtropical areas .Calcined bauxite is obtained by calcining (heating)superior grade bauxite at high temperature (from 85OC to 1600C) .This removes moisture there. By increasing the alumina content,compared to an alumina content of about 57%to 58% in raw bauxite, calcined bauxite has an alumina content of 84%to88%.The heating is carried out in rotary kilns. 

3.Main usage of the Calcined Bauxite

(1) aluminium industry. Used in national defense, aerospace, automotive, electronics, chemical industry, daily necessities, etc. 
(2) precision casting. Alumina clinker made after the mould precision casting processed into fine powder. Used in military industry, aerospace, communications, instrumentation, machinery and medical equipment department. 
(3) is used for refractory products. High bauxite clinker refractoriness is as high as 1780, chemical stability strong, and good physical properties. 

 

4. Calcined Bauxite Images

 

High Quality Bauxite High Alumina Refractory Brick Dry Pressed Block of  CNBM in China

High Quality Bauxite High Alumina Refractory Brick Dry Pressed Block of  CNBM in China

 

 

5. Calcined Bauxite Specification

 


     BRAND                                              INDEX          

High Alumina Brick for  BF

Fire Clay Brick for BF

GL-65

GL-55

GL-48

ZGN-42

GN-42

  Al2O3,  %                                                   ≥

65

55

48

42

42

  Fe2O3,  %,                                                 ≤

2.0

2.0

2.0

1.6

1.7

  AP  %                                           ≤

19

19

18

15

16

Refractoriness    °C                                            ≥

1790

1770

1750

1750

1750

 PLC                                      %  

0~-0.2

0~-0.2

0~-0.2

0~-0.2

0~-0.3

1500°C x 2h

1450°C x 2h

CCS  MPa                              ≥

58.8

58.8

49

58.8

49

 0.2MPa  RUL    °C        

1500

1480

1450

1450

1430

 

 

6.FAQ of Calcined Bauxite

1). Q: Are you a factory or trading company?

A: We are a factory.

2). Q: Where is your factory located? How can I visit there?

A: Our factory is located in ShanXi, HeNan, China. You are warmly welcomed to visit us!

3). Q: How can I get some samples?

A: Please connect me for samples

4). Q: Can the price be cheaper?

A: Of course, you will be offered a good discount for big amount.

 

Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:What is carbon composite refractories? I hope that the answer is in detail.
Q:The effect of a high content of water in liquid resin exerted on refractory material?
For one thing, Substandard whiteness, transportation, low quality and the storage of refractory material may account for this. For another, a high content of moisture reduced the performance of refractory material. A high content of moisture is equal to buy water with same money in terms of trade settlement. Based on this, we can’t consider the super-standard water content from a single aspect, because the water content in refractory material is definitely super-standard, and another problem is particle size. Many people hold the idea that excessive amount of water content may revive its original performance, but it tends to have influenced the quality of refractory material.
Q:how about the performance of aluminum silicate fire proof thermal insulation?
aluminum silicate fire proof thermal insulation board has a good performance. it is a artificial board that separates the wood and plant fiber by mechanical and chemical methods and mixed the adhesion agent and water-proofing agent, molding by high temperature and high press. MDF(medium density fibre board) structure is more even than natural wood. it avoids rot, moth-eaten and other problems, while medium density fiber board has small expansion and contraction, which is easy to be processed. Since the surface of medium density fibre board is smooth, the board is easy to paste a variety of finishings, which makes furniture more beautiful. A variety of decorative wood-based panel is to embellish their homes.
Q:who knows the technology of fireproofing material?
1, dealing mould, scrape and clean the thick liquid on the surface of mould with tin-coated steel scraper blade or plaster tool. 2, adjust laminator, according to the thickness of fireproof panel, adjust each roller, keep them parallel. 3, ingredient, according to the requirements of recipe, stir the raw materials uniform with agitator. (usually we should add bittern firstly, stir it with modifying agent for 5 minutes, then add filler and stir for 2-3 minutes, finally add grogs and stir it to uniform) note: the stirring speed should be kept in 60-80 r/min. 4, place the cloth, place a layer of non-woven fabric and two layers of glass fiber fabric (mechanical spread fabric). 5, flitch, place the materials after compounding and stirring into stop gauge of laminator, then you can start up and produce continuously, it's finished product after finishing. note: the distance between two templates is 2-4mm.
Q:The difference between refractory and thermal insulation material
In simple terms, refractoriness is different. The refractoriness of refractory is high while that of insulation material is low.
Q:whether the fire resistant level of aerated concrete building blocks can reach the grade one?
Aerated concrete building blocks is made by calcareous materials (such as cement, lime) and siliceous material (such as sand, fly ash, slag), adding aluminum powder ingredients as filling agent, by mixing with water, casting molding, gas - expansion, raising the pre-cut, and then the high-pressure steam curing of silicate building blocks. when aerated concrete is at the temperatures below 600 ℃, the compressive strength will be increased slightly, when the temperature is at about 600 ℃, the compressive strength is close to the compressive strength at normal temperature, so the aerated concrete, as building materials, the fire performance can meet the national fireproffing safety standards level.
Q:Refractory material, refractory brick
1, according to the degree of refractoriness:Ordinary refractory material: 1580 ~ 1770 DEG CAdvanced refractory material: 1770 ~ 2000 DEG CSuperfine refractory material: >2000 DEG C2, depending on the shape and size of the product:Standard type: 230mm * 113mm * 65mm;No more than 4 measurements, (size ratio) Max:Min<4:1;Profile: no more than 2 concave, (size ratio) Max:Min<6:1;Or an acute angle of 50~70 degrees;Specific type: (size ratio) Max:Min<8:1;Or not more than 4 or a sharp angle; 30 ~ 50 degrees;Special products: crucibles, vessels, tubes, etc.3, according to manufacturing methods, refractory materials can be divided into:Fired products, unfired products, unshaped refractories4. classification according to the chemical properties of materials:Acid refractory material, neutral refractory material, basic refractory material
Q:What are the classifications of refractory? Which category does steel ladle castable belong to?
Silmo brick, alumina-magnesia brick; 2. coke oven, aluminum silicate... 8 categories)& nbsp, teeming ladle, glass furnace ...... 7 categories) high alumina refractory products (blast furnace, electric furnace, cement kiln, magnesia, glass furnace; 3. high alumina refractory mortar (high alumina, glass kiln ...... 6 categories) special refractory products (magnesia-carbon bricks, aluminum-carbon bricks, MgO-C, shapeless refractory products& nbsp, light weight, sliding plate bricks, cement kilns: There are 26 categories in refractory products, clay, calcium silicate, ceramsite lightweight... 10 categories) & nbsp, air heating furnace, sheets; 1 refractory castable (alumina-magnesia, blocks, resistance furnace... 11 categories) alkaline refractory products (magnesia. First, thermal insulation refractory products (ceramic fiber; clay, diatomaceous earth, steel fibre reinforcement...14 categories) & nbsp, silicon carbide brick ...... 19 categories) Second, China is the largest refractory production country in the world, clay, non-water cannons mud, converter, siliceous, teeming ladle, profiled) siliceous refractory products (coke oven, dense shaped refractory products (all kinds of bricks, electric furnace roof, glass kiln ...... 5 categories) clay refractory products (blast furnace, high alumina ...... 4 categories) three
Q:How many hours of the fire endurance time of the rock wool laminboard?
Hello. The fire endurance now on the market is generally about two hours. The 50mm color steel sandwich version of Bo magnesium rock wool, with refractory time being five or six hours, is very good.
Q:How long is the fire endurance of Grade A fire resisting shutter
Fire door can be divided into Grade A, Grade B and Grade C fire door according to its fire endurance. Their fire endurance is not less than 1.20h, 0.90h and 0.60h respectively. Use fire resisting shutter as fire compartment separation in places where it is difficult to set firewall. When fire resisting shutter whose unexposed surface temperature rise is used as judging condition of fire endurance is used, its fire endurance should not be lower than 3h. When fire resisting shutter whose unexposed surface temperature rise is used as judging condition of fire endurance is not used, individual protection of  closed automatic water spray system shoule be set at two sides of the shutters and duration of water spray system should not be less than 3.0h. When the fire resisting shutter is used for fire compartment, fire endurance is 3h. When the fire resisting shutter is set at the opening part of firewall, fire endurance is 1.2h.

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  