High-Alumina Bricks with good resistance

High-Alumina Bricks with good resistance

Ref Price:
get latest price
Loading Port:
Tianjin
Payment Terms:
TT OR LC
Min Order Qty:
20 m.t.
Supply Capability:
20000 m.t./month

Add to My Favorites

Follow us:


OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

Description:

 

 

high alumina bricks are produced with selected bauxite chamotte by advanced process and strict quality control. The main mineral components are corundum and mullite phases. It(High Alumina Brick,Alumina Brick,Refractory Alumina) features excellent high temperature mechanics and chemical corrosion resistance.

 

 

 

High Alumina Brick,Alumina Brick,Refractory Alumina Features:

 

1. Resisting high temperature
2. Great bulk density
3. Low iron content
4. Good eroding resistance

 

 

Applications:

 

1. Steel furnaces
2. Iron making furnaces
3. Glass kiln
4. Ceramic tunnel kiln
5. Cement kiln

 

 

Specification:

Item                             Specifications

LZ-48

LZ-55

LZ-65

LZ-75

LZ-80

LZ-85

Al2O3 %

48

55

65

75

80

85

Fe2O3 %

2.5

2.5

2.0

2.0

2.0

1.8

Refractoriness°C

1760

1760

1770

1770

1790

1790

Bulk Density≥ g/cm3

2.30

2.35

2.40

2.45

2.63

2.75

Apparent porosity %

23

23

23

23

22

22

Refractoriness under load 0.2MPa°C

1420

1470

1500

1520

1530

1550

Cold crushing strength MPa

45

45

50

60

65

70

Permanent linear chang %

1500°C×2h

+0.1~-0.4

+0.1~-0.4

+0.1~-0.4

+0.1~-0.4

+0.1~-0.4

+0.1~-0.4


why us

1. We are a manufacturer, which can control the cost easilier than trade company also can give you anwer more quickly.

2. As a manufacturer, we know much in technique and can give you more support in technique problem.

3.We establish the company and began to produce refractory materials since 1988. We have longtime and mature experience  for entire production.

4.Our products are complete in specifications with various of sizes.

5. We enjoy a good reputation in the customers in domestic and overseas markets.


Q:What are the requirements for refractory materials in heat treatment furnace?
Refractoriness is the property of a refractory against high temperature, which means the temperature at which a refractory is softened to some extent after heating, but not its melting point. According to the degree of refractory, refractory materials can be divided into: General refractories, refractory degree is 1580 to 1770 DEG C; advanced refractories, refractory degree is 1770 to 2000 DEG C; special refractory material, refractory degree is greater than 2000 DEG C.
Q:What's the difference between a well type annealing furnace and a box type annealing furnace?
Box annealing furnace application: mainly used for quenching, normalizing, annealing and other conventional heat treatment equipment for steel parts. Features: 1, electric loading, high productivity, heat treatment is especially suitable for small and medium-sized parts, such as 30%, uniform temperature, intelligent digital display meter PID (pictured) automatic temperature control, high precision; 2, electric discharge loading convenient, as good; 3, door and seal the oven body is sealed automatically, without manual seal; 4, equipped with electric interlock protection device, and can prevent the fault accident due to the error. Bell type annealing furnace four bell type annealing furnace bell type annealing furnace is mainly used for annealing sheet metal in natural atmosphere and normalizing treatment of steel parts. 1, special steel, precision alloy large all fiber trolley type resistance furnace, strip, wire bright annealing. 2 、 annealing of special steel casting and forging. 3. Annealing of silicon steel sheet. 4, metal and non metal powder sintering pieces etc..
Q:What is the density of a super high alumina brick and what is the price?
Of course, the transaction price, please choose refractory brick manufacturer is better.
Q:What is the difference between high alumina brick and clay brick?
Lightweight high alumina bricks are usually made of high alumina bauxite clinker with a small amount of clay. After grinding, the bricks are poured and shaped in the form of slurry by gas or foam method. They are fired at 1300~1500 DEG C. Sometimes industrial alumina can be used instead of some bauxite clinker. Used for lining and insulation of masonry kilns, as well as for areas where there is no strong, high temperature molten material erosion and erosion. When contacting the flame directly, the surface contact temperature shall not be higher than 1350 degrees centigrade.
Q:The difference between ordinary and diatomite brick refractory brick
Refractory brick belongs to a large class, according to different materials used are divided into: high alumina brick, dolomite brick, magnesia chrome brick, magnesia spinel brick, phosphate brick, carborundum brick, brick, mullite bricks etc..
Q:Use of high alumina refractory bricks?
High alumina refractory brick in Al2O3 more, close to neutral refractory material, can resist acid slag and alkaline slag erosion, because it contains SiO2, so alkaline slag ability than acid resistance slag ability less.It is widely used in building blast furnace, hot blast furnace, furnace top, blast furnace, reverberatory furnace and rotary kiln lining. In addition, high alumina bricks are widely used as furnace regenerative checker, pouring system for plug nozzle, etc..
Q:What refractory material does cupola lining use?
A class of inorganic nonmetallic materials with a refractoriness of not less than 1580 degrees. Refractoriness is defined as the temperature of a sample of a refractory cone sample that resists high temperature without loading and does not soften and melt down. But only in terms of fire resistance can not be fully described refractories, 1580 degrees of temperature is not absolute.
Q:The difference between clay bricks and clay bricks
Clay brick is a small building with artificial bulk. Also called sintered brick. Solid clay brick is one of the oldest building materials in the world. It is a building material that is loved by the people.
Q:Density of high alumina bricks
The density of high alumina bricks is determined according to the price. The average density is between 2.3-2.5g/cm3. The higher the density, the higher the price, the higher the aluminum bricks are in the industry. More than 2.4 are required.
Q:How high can aluminum bricks expand at 80O degrees of heat?
The expansion of high alumina brick is not only related to temperature, but also related to its material composition. The refractory temperature of high alumina brick is above 1770 centigrade. The temperature of 800 DEG C has little influence on the expansion of high alumina brick.

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range

Send your message to us

This is not what you are looking for? Post Buying Request

Similar products

New products

Hot products