Graphite Electrode with Grade RP HP UHP Dia.40-600mm

Ref Price:
$1,700.00 - 1,950.00 / m.t.
Loading Port:
Tianjin
Payment Terms:
TT or LC
Min Order Qty:
100 m.t.
Supply Capability:
50000 m.t./month

OKorder Service Pledge

Quality Product

Order On-line Tracking

Timely Delivery

OKorder Service Pledge

Credit Rating

Credit Services

Credit Purchasing

Share to:

Product Description:

1. Specifications of Graphite Electrode

RP HP UHP Graphite Electrode
.Dia:40-600mm or1.6"-24"
.Length:250-2400mm or10"-96"
.Nipples:3TPI,4TPI
.ISO9001:2008


2. Applications of Graphite Electrode

Used in EAF and LF for steel making, as well as in electric smelting furnace for producing industrial silicon, phosphorus, etc.


3. Programmable properties
.Good electrical conductivity
.High resistance to thermal shock
.High mechanical strength


4. Grades: RP, RPI, HP, SHP, UHP

All graphite electrodes are offered with tapered nipples, i.e. 3 or 4 threads per inch, and meet the internationally accepted tolerances as per NEMA CG 1/ IEC 60239 / JIS R7201 standards.


5. Details of Graphite Electrodes

Item

Unit

Regular-power

Impregnated

φ75-
130

φ150-
225

φ250-
300

φ350-
500

φ75-
200

φ250-
350

φ400-
500

Specific Resistance (≤)

E

μ Ω·m

8.5

9

9

9

8

8

8

N

8

8

8

8

7.5

7.5

7.5

Bending Strength (≥)

 

E

MPa

 

9.8

9.8

7.8

6.4

10

9

8

N

13

13

13

13

15

15

15

Elastic Modulus (≤)

 

E

GPa

 

9.3

9.3

9.3

9.3

12

12

12

N

14

14

14

14

14

14

14

Bulk Density (≥)

 

E

g/cm3

 

1.58

1.52

1.52

1.52

1.58

1.58

1.58

N

1.63

1.63

1.68

1.68

1.68

1.68

1.68

C.T.E.(≤)
(100-600°C)

 

E

10-6/°C

 

2.9

2.9

2.9

2.9

2.7

2.7

2.7

N

2.7

2.7

2.8

2.8

2.5

2.5

2.5

Ash(≤)


%

0.5

0.5

0.5

0.5

0.3

0.3

0.3

 

Item

Unit

High-power

Super high-power

Ultra high-power

φ200-400

φ450-500

φ350-400

φ450-500

φ300-400

φ450-500

Specific Resistance(≤)

E

μ Ω·m

7

7.5

6.5

7

6.2

6.5

N

6.5

6.5

6

6

5.5

5.5

Bending Strength (≥)

 

E

MPa

 

10.5

9.8

10.5

10

10.5

10

N

15

15

16

16

16

16

Elastic Modulus (≤)

 

E

GPa

 

12

12

13

13

14

14

N

16

16

17

17

18

18

Bulk Density (≥)

 

E

g/cm3

 

1.6

1.6

1.62

1.62

1.65

1.64

N

1.7

1.7

1.71

1.71

1.72

1.72

C.T.E.(≤)
(100-600°C)

 

E

10-6/°C

 

2.4

2.4

2.2

2.2

1.5

1.5

N

2.2

2.2

1.8

1.8

1.4

1.4

Ash(≤)


%

0.3

0.3

0.3

0.3

0.3

0.3


6.Pictures of Graphite Electrodes

Graphite Electrode with Grade RP HP UHP  Dia.40-600mm

Graphite Electrode with Grade RP HP UHP  Dia.40-600mm


7FAQ

We have organized several common questions for our clientsmay help you sincerely 

How about your Warranty of Graphite Electrode 

 Warranty: 1-Year for the whole light. Warranty is based on correct storage, installation, using and maintenanc

How to guarantee the quality of the products of Graphite Electrode 

We have established the international advanced quality management systemevery link from raw material to final product we have strict quality testWe resolutely put an end to unqualified products flowing into the market. At   the same time, we will provide necessary follow-up service assurance. We have D&B report and you could check details information for our company.

How long can we receive the product after purchase of Graphite Electrode ?

In the purchase of product within three working days, We will arrange the factory delivery as soon as possible. 


Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:I used 12V direct current, graphite electrode electrolysis sodium sulfide solution, the anode produced a large number of black material, this is why ah?
The problem is this. I have done the test of electrolytic copper sulfate, and the anode produced the same phenomenon. Finally, the chemistry teacher told me that it was because the graphite was broken in the process of electrolysis
Q:Why should graphite paper be placed between the heater and the graphite electrode?
Determine the thickness of the graphite bowl, the thickness of the graphite bowl is generally 3 mm -6 mm, three, determine the diameter of the heater, according to the diameter of the crucible and the thickness of the graphite bowl, calculate the inner diameter of the heater. The gap in the quartz crucible diameter phi = +2 times is +2 times the wall thickness of stone bowl bowl and graphite heater if the graphite bowl wall thickness is a, graphite bowl gap and heater for B (b=5 mm), phi = Phi Phi +2a+2b= within the outer crucible outer crucible +2 (a+b) four, to determine the effective heater the height after practice, the effective length of the quartz crucible heater is high 1.6 to 1.8 times.
Q:Why graphite can be used as conductive material?
Graphite used in the electrical industry requires a high degree of particle size and grade. Such as alkaline batteries and some special electric carbon products, requiring graphite particle size control within the scope of the project, grade above, harmful impurities are required in the following. The graphite used in a picture tube for television is required below. As a wear-resistant and lubricating material, graphite is often used as a lubricant in the mechanical industry.
Q:What is the role of the Pt electrode? What is the difference between the graphite electrode and the graphite electrode?
Carbon electrodes, however, are less likely to be less controllable because of their microstructure, or have some effect on the electric field, if they are sensitive signals
Q:The reason why graphite is used as electrode
Good chemical stabilityGraphite has good chemical stability at room temperature. It can resist acid, alkali and organic solvent.
Q:How should carbon deposits be treated?
In this way, can keep the engine seal, to prevent oil because the gap is too large and rampant, buried carbon curse generation "".
Q:Do electroplating experiments, graphite as an electrode, graphite how to pre process to ensure that the coating will not fall, resulting in increased color of the solution
Use a tight filter cloth as an anode pack
Q:Specification for graphite electrodes commonly used in steel works
General specification for graphite electrode diameter Phi 300 Phi 500mm, Phi Phi 550 - the current usage of 800mm graphite electrodes is also great, the graphite electrode length was between 1600 and 2700mm.
Q:800KVA and 12500 EAF transformer data graphite electrode furnace.
Graphite project: Project Description: steel furnace and iron smelting furnace, ferrosilicon smelting, electrolytic aluminum and so on, all use large surface graphite electrode.
Q:The graphite electrode made by the machining center adopts cooling method, which is water cooled, oil cooled and blow cold. Which is good?
In addition, the infiltration of water on graphite is not good, can not get the effect of dust removal. Now there are special graphite machine, sealing system. Air-cooled can be used, after all, the best air-cooled.

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range