Graphite Electrode Manufacture in China

Ref Price:
Loading Port:
Tianjin
Payment Terms:
TT OR LC
Min Order Qty:
100 m.t.
Supply Capability:
1000 m.t./month

OKorder Service Pledge

Quality Product

Order On-line Tracking

Timely Delivery

OKorder Service Pledge

Credit Rating

Credit Services

Credit Purchasing

Share to:

Product Description:

Quick Details

Place of Origin:

China (Mainland)

Brand Name:

CMAX

Model Number:

JX-UHP

Type:

Electrode Block

Application:

steel smelting

Diameter:

Dia200-700mm

Length:

1800-2200mm

Grade:

UHP (Ultra High Power)

Resistance (μΩ.m):

11-13

Apparent Density (g/cm³ ):

more than 1.8

Thermal Expansion:

1.4-2.8

Round Size:

Dia350x450 dia400x450 dia500x450 dia585x600

Square Size:

400x400x400 400x400x500 400x400x600 900x540x260

Bulk Density:

more than 1.8

Product name:

uhp graphite electrode

Dimensions:

Dia350x450 dia400x450 dia500x450 dia585x600

Chemical Composition:

carbon and graphite



Packaging & Delivery

Packaging Details:standard package for exportation
Delivery Detail:15-25 days after confirmation

Technical Data

PROPERTY

JXRP

JXHP

JXUHP

1

2

1

2

1

2

Electric

resistance

μΩm ≤

electrode

 8.5

9.0

6.5

7

6.0

6.5

nipple

8.0

8.5

6.0

 6.5

5.0

5.5

Bending

strength

Mpa ≥

electrode

8.0

7.8

11.0

10.5

11.0

10.0

nipple

13.5

13.0

14.0

14.0

16.5

16.0

Elastic modulus

Gpa ≤

electrode

8.0

9.3

11.0

12.0

13.5

14.0

nipple

13.0

14.0

15.0

16.0

14.5

18.0

Bulk density

g/cm³ ≥

electrode

1.56

1.52

1.62

1.60

1.65

1.64

nipple

1.70

1.68

1.72

1.70

1.72

1.70

Ash content

% ≤

electrode

0.3

0.5

0.2

0.3

0.2

0.3

nipple

0.4

0.5

0.2

0.3

0.2

0.3

C.T.E

100-6/ ≤

electrode

2.8

2.9

2.4

2.4

1.5

1.5

nipple

2.7

2.8

2.2

2.2

1.4

1.4





























Graphite Electrode Manufacture in China



Graphite Electrode Manufacture in China

Graphite Electrode Manufacture in China

Graphite Electrode Manufacture in China

Graphite Electrode Manufacture in China


Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:What are the factors that affect the electrode wear rate of machine tools?
In the pulse peak voltage, current and pulse width decreased, the electrode loss increase, and the heat produced from the processing of large pulse width, is conducive to the adsorption of copper electrode graphitization induced by carbon, which is commonly referred to as the covering effect".
Q:How to solve the problem of graphite electrode being crushed during electrolysis
I can only use the experience of the past to tell you that if you want to save money easily, the time can be considered as the costA thick graphite stick; inexpensive
Q:Why is graphite conductive electrode oxidized?
Graphite electrode uses petroleum coke (carbon), pitch coke (carbon) as granule material
Q:MITSUBISHI machine graphite electrode processing, how does not accumulate carbon?
The three is difficult cold start, is sparking difficult, not easy car, and finally the combustion chamber carbon Yan will cause a heavy cylinder knock, low speed and acceleration noise, causing damage to the piston and crankshaft, causing the engine temperature which can seriously affect the automobile safety. Emission standards exceeded, not only through the annual inspection, but also directly aggravate the pollution of the environment
Q:Classification of graphite electrodes
A graphite electrode with a current density of 18~25A/ cm 2 is used, which is mainly used in steel-making of high power arc furnace.
Q:Carbon graphite electrode and what is the difference?
Graphite electrode is a mixture of natural graphite and petroleum coke and asphalt coke. After being treated by high temperature graphitization, the material is composed of graphite;
Q:Classification, uses and manufacturers of graphite electrodes
Graphite as electrode(1) the processing speed is faster: normally, the mechanical processing speed of graphite can be 2~5 times faster than copper, while the discharge processing speed is 2~3 times faster than copper;More material is not easily deformed: obvious advantages in the processing of thin electrodes; copper softening point at about 1000 degrees, easily deformed by heat; graphite sublimation temperature is 3650 degrees; the thermal expansion coefficient of copper is only 1/30.(2) lighter weight: the density of graphite is only 1/5 of copper. When large electrode is used for discharge machining, it can effectively reduce the burden of machine tools (EDM). It is more suitable for large-scale die applications.
Q:Iron and graphite as electrodes and Nacl as electrolyte solutions. Why do they produce electric current? Graphite and iron react not with solution, can they be connected by wires?
Because the metal activity order form sodium potassium calcium magnesium aluminum, zinc and tin lead (hydrogen), mercury copper silver platinum, iron in the front row because of water water hydrogen, ionized hydrogen ions by iron replacement
Q:Graphite graphite graphite graphite electrode what is the use?
Natural graphite electrode is the main raw material with graphite, high purity flake graphite powder or high carbon flake graphite powder as raw material, because carbon or graphite powder purity is high, the effect of conductive graphite powder is better in smelting alloy steel, iron alloy, electrode graphite powder as raw material. The electrode produced, then the strong current through the melting zone, the arc electrode into the electric furnace, the electrical energy into heat, the temperature rises to 2000 degrees Celsius, so as to achieve the purpose of melting or reaction.
Q:What are the losses in graphite electrode?
So tell, this problem is to answer a lot, graphite under high temperature oxidation, generally around 400 degrees, began a slight oxidation, but the human eye is to be observed, with the increase of temperature, the graphite oxide will increase, this time should be used to protect gas or vacuum to protect what you said is, nitrogen protection, and general protection of nitrogen can reach more than 2000 degrees, if the high temperature to 3800 degrees, will you say that vapor formed in graphite surface. To achieve this temperature, it is necessary to add inert gas to achieve, otherwise, can not reach, generally to 4350 degrees, the graphite began to soften.

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range