Product Description:







Al2O3,%               不小于





耐火度,℃           不低于
Refractoriness        min





荷重软化开始温度,℃ 不低于
RUL                   min





重烧线变化 % 1450℃x2h



显气孔率,%          不大于
A.P.                 max





常温耐压强度         不小于
CCS                  min






Product characteristics; General use high-alumina brick use yangquan bauxite clinker with high quality combined with clay and additives made from. Product has high refractoriness, good acid and alkali erosion resistance, high temperature strength, good thermal shock stability etc, and widely used in metallurgy, light oil, chemical industry, building materials, machinery, processing, thermal technology equipment of military industry and other industries.

Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:What bricks are used for constructting refractory bricks tunnel kiln what is the material of each burning zone brick
Refractory brick tunnel kiln, but if you want fire magnesia-chrome bricks, it may soon be finished, but the energy saving effect is good, using mullite bricks to sinter high alumina brick tunnel kiln burning zone is ok. Of course, if sintering is different, the refractotry bricks require different the kiln shape of tunnel kiln, preheating zone and cooling zone use high alumina brick and clay brick. what kind of products will be sintered in the future, clay brick firing zone had better use alumina hollow ball brick and mullite bricks How high the daily design capacity to achieve, thermal insulation can not be ignored, if firing silica brick, then I am afraid there are only few finished burning bricks, what 's the purpose of the actual operation of the tunnel kiln you will build Different design of tunnel kiln use different brick, generally sintering high alumina brick and clay brick require good kiln, the cost is also very different, for example, because although the cost is higher, in addition operation is very important for the using effect and service life of the furnace, but the design of kiln type must be reasonable, otherwise it can not reach the expected effect, for example, the highest sintering temperature to achieve
Q:Can thick steel plate be used instead of the furnace inside the refractory brick?
It depends on the temperature. The steel plate is a kind of heat conduction material which hasn't heat insulation, which should be based on the working environment.
Q:the refractory brick in glass furnace burner was burning, the bricks on both sides of the fire hole were burning the blocked it, what will cause brick burning?
The firebrick in glass melting furnace is mainly consisted of zircon brick, other ordinary refractory materials can not effectively prevent the erosion of glass solution. Because the glass melting liquid is eutectic mixture compared to the refractory bricks, it penetrates into the refractory brick and reduces its original performance, simply speaking, the glass melting liquid dissolves the refractory bricks as eutectic mixture .
Q:What's the reason of cracks in refractory bricks?
The relative density is high, and high temperature heat treatment and increase the strength of qualitative brick, for 10 days, then only the shorter time for heating and drying and dehydrating, you can smash a brick if it's a long time! There will be a stress loose phenomenon making bricks now, the internal density of these crack bricks are not the same, in addition to the effective drying, dehydrating and heating treatment, the time distance is small, basic bricks and finished bricks adopt line production, when drying, the water is also evaporated at the same time, the central density should be high ! The reason is very simple, the greater extrusion force the brick bears in the molding, the closer to the edge, the smaller density is, the better to keep forming, the shorter residence time, the higher the rate of finished product is, which belongs to the natural drying, this phenomenon is more obvious
Q:High alumina refractory bricks (Universal arc) weight for hot metal ladle
Climbing, C23B ladle generally use T3 ladle bottom brick, brick wall with C23 package, C231 Some permanent layers are built from high alumina bricks, and some are built from castable refractory, T82, T43. Specific size can be checked according to the type of brick
Q:air-cooled razheng times of magnesia-alumina spinel refractory bricks
The ingredients are magnesium, oxygen, and aluminum. the components of spinel refractory can be magnesia-alumina spinel with excessive aluminium oxide, or magnesia-alumina spinel with excessive magnesium oxide. excessive magnesium oxide and aluminium oxide can form magnesia-alumina spinel in above 1700 degrees.
Q:application of phosphate refractory bricks
The 4 properties of phosphate refractory bricks: (1) high strength wear resistance (2) and chemical erosion (its alkali resistant ability is better than that of clay brick and high alumina brick) (3) and good thermal shock resistance (4) high load softening temperature in rotary kiln, kilneye, kiln Zone door cover, cooling machine and lining refractory brick falling parts easy to loose
Q:What kind of refractory brick is suitable for 1400 degrees shuttle kiln?
Corundum mullite is also the principle about.2 can be. use high aluminum brick, which heat storage capacity is big, but the price is more expensive, and the chilling and heating performance is not good, the .
Q:Can refractory bricks be used to pave roads or build a wall?
Complete refractory brick has standard size and it is heavier than ordinary red brick. the volume ratio is shrinking with change of temperature to crack and strength of brick with brick walls down enough for new
Q:What is the difference between the refractory brick and the thermal insulation brick
Refractory bricks are used in the stove, in order to prevent from burnouting the stove under high temperature. Thermal insulation brick is used for preserving heat, is to heat preservation

1. Manufacturer Overview

Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range