FUSED REBONDED MAGNESIA BRICKS

Ref Price:
Loading Port:
China Main Port
Payment Terms:
TT OR LC
Min Order Qty:
-
Supply Capability:
-

OKorder Service Pledge

Quality Product

Order On-line Tracking

Timely Delivery

OKorder Service Pledge

Credit Rating

Credit Services

Credit Purchasing

Share to:

Product Description:

Specifications

Spinel Alumina Magnesia Fire Brick
1.Good alkali resistance
2.Good corrosion resistance
3.High refractoriness under

Features

1. Good slag resistance

2. Excellent corrosion resistance

3. High refractoriness under load

Applications

Magnesia alumina spinel brick is widely used in transition zone of large dry-process cement rotary kiln, lining of ladle,and roof of EAF, etc.

Physical properties and chemical composition

                         Item

     

LMLJ-80

LMLJ-75

Standard

Typical Value

Standard

Typical Value

MgO, %

≥80

85.5

≥75

81.2

Al2O3 , %

8~15

10.2

8~15

9.83

apparent porosity, %

≤17(18)

16

≤18(19)

16

0.2MPa refractoriness under load °C

≥1700

1800

≥1650

1750

cold crushing strength ,MPa

≥40

57

≥40

68

Thermal expansion(1100°C,water cooling), times

≥20

≥20

≥5

≥16

Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:Magnesia brick
Magnesia brick (magnesite brick) basic refractories Magnesium Oxide content of more than 90%, with the main crystalline phase of periclase. General can be divided into sintered magnesia brick (also called burnt magnesia brick) and chemically bonded magnesia brick (also known as the two major categories of not burned magnesia brick). Purity and high firing temperature of magnesia, due to the direct contact of periclase grains, known as direct bonded magnesite brick; made of fused magnesia bricks called electrically fused magnesite brick.
Q:How to identify the fused magnesia brick and sintered magnesia brick
Magnesia brick (magnesite brick) basic refractories Magnesium Oxide content of more than 90%, with the main crystalline phase of periclase
Q:Brick price?
There are various series of unshaped refractory gunning, magnesia ramming material, mending material, coating material, dry lining material, composite refining agent, covering agent, tundish and tundish slag wall, ladle drainage sand and electric furnace taphole filler etc..
Q:With different capacitance magnesia brick brick
Fused magnesia brick brick has compact structure, high mechanical strength,It is mainly used for thermal storage of large glass furnaceHigh temperature area of the room.
Q:What is the ratio of magnesia refractory bricks to brine? For example, what is the difference between the 97 and 95 with 92 brick brick brick material mixed with brine ratio?
In addition to the brine binder burned magnesia brick and sulfite pulp waste liquid, Magnesium Sulfate solution binder is generally around 3%
Q:Process for producing magnesia chrome brick
The oxide of iron reacts to produce a loose effect caused by the expansion of the spinel. Also, the magnesia chrome brick can be made from the synthetic common sintered material. In addition, there are non burned magnesia chrome bricks, for example, non burned magnesia chrome bricks combined with inorganic magnesium salt solutions. The unfired magnesia chrome brick has the advantages of simple production process, low cost and good thermal stability, but the strength of the high temperature is far less than that of the burnt brick. In the late 50s, a so-called "direct bonding" magnesia chrome brick was developed. The characteristics of this brick raw material is pure, high firing temperature, periclase and spinel phase with high temperature directly, silicate and other low melting point phase for island distribution, therefore, significantly improve the high temperature strength and slag resistance of brick.
Q:Magnesite chrome brick, magnesia chrome brick indicators? What is the price?.
If you want to know the indicators of chrome brick, magnesia chrome brick must know you are in what furnace above, there is in what position
Q:High purity magnesia brick masonry mortar for what?
High purity aluminum is 99.99, the first is not pollution, the stove is high magnesia brick masonry, 95% and 97% purity magnesia brick is for a long time did not find a good bit of fireclay, do not know what to build, now used light burned US powder and heavy burned magnesium plus brine built, with 2 months a griddle doesn't stick on magnesium brick, a touch off, there is no good sintering
Q:The index of magnesia brick
Room temperature compressive strength≥(MPa)(15-25-)24.5-24.5-24.5-24.5-40-40-40
Q:How to identify the fused magnesia brick and sintered magnesia brick?
Magnesia brick (magnesite brick) basic refractories Magnesium Oxide content of more than 90%, with the main crystalline phase of periclaseGeneral can be divided into sintered magnesia brick (also called burnt magnesia brick) and chemically bonded magnesia brick (also known as the two major categories of not burned magnesia brick). Purity and high firing temperature of magnesia, due to the direct contact of periclase grains, known as direct bonded magnesite brick; made of fused magnesia bricks called electrically fused magnesite brick.

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range