FIRE CLAY BRICK

CMAX fireclay bricks are made from clinker clay. The alumina content ranges from 36% to 48%.

 

Application
CMAX fireclay bricks are commonly applied in blast furnace, hot blast furnace, teeming ladle, glass furnace, etc.

 

Features
Low thermal conductivity        High refractoriness  

High mechanical strength       Excellent thermal shock resistance

ITEM

UNF42

UNF46

ZGN42

RN40

TDL45-12

Refractoriness,

1730

1750

1750

1730

1760

Bulk Density, g/cm3

2.15

2.25

2.3

2.15

2.37

Apparent Porosity, %

22

20

15

24

12

C.C.S, Mpa

30

35

58

28

68

Refractories Under Load (0.2Mpa)

1400

1420

1450

1430

1500

Reheating Linear Change, %

1400x2h              0.1-0.4

1430x2h              0-0.1

1450x2h              0-0.2

1350x2h       0-0.3

1450x2h              -0.1+0.05

Al2O3 Content , %

42

46

42

40

45

Fireclay Brick with Al2O3 Content around 30%

Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:What is the color of the refractory brick to repair the same color as the 1400
carbonaceous refractory brick 186, heat preservation brick, firing under 1300 ~ 1400 degrees Celsius, calcium, 3373 in fact, there are many kinds of refractory bricks. The mineral composition of the clay brick is mainly kaolinite (2SiO2, 2H2O, Al2O3) and 6% to 7% impurities (potassium, according to a certain granularity requirements of the ingredients, fireclay brick, etc., after molding, titanium, dry.
Q:Tunnel kiln firing refractory brick by 0 against the good rely on
Modern advanced kiln has high temperature strength and good thermal shock resistance, better environmental protection, is the most economical and efficient kiln. (3), good resistance to gas erosion, due to tunnel kiln's flue gas discharge temperature is generally not higher than 250℃. In order to guarantee the normal temperature system and pressure system of the kiln. Its firing temperature is at 1200-1900℃: (1) or even higher, the requirement for the firebrick, compared with the intermittent kiln, is an important thermal equipment in refractory industry. It is a kind of energy-saving kiln. Tunnel kiln is a kind of kiln that can continuously produce and has high degree of automation.
Q:Do refractory bricks need to be sent to the lab to test after arriving the site?
Generally speaking, as long as the use of temperature is not higher than 1500 degrees, it is not required to do the test, even if the ordinary refractory brick temperature is about 1500. If the temperature is high, then you do test to determine what kind of texture of refractory brick you need
Q:What is refractory brick? What is refractory clay? ?
Fire clay refers to the light pouring material, raw materials adopt light porous clinker, bauxite, cenosphere, silicon dioxide ultrafine powder and alumina micropowder. Use calcium aluminate cement CA-80 as binder. Refractory brick is burned from stone powder and clay put in 1300 degrees' kiln
Q:What kind of refractory brick is used for industrial furnace?
What kiln? Glass kiln, ceramic kiln, or blast furnace?
Q:What's the reason of cracks in refractory bricks?
This is inorganic nonmetallic material
Q:Can red bricks be burned in tunnel kiln which used to burn refractory brick?
Of course. But the temperature to burn refractory brick is very high, the average temperature is above 1500 degrees. And the temperature to burn brick is not so high, about 1200 degrees. So you should control the temperature, the tunnel kiln to burn firebrick and the tunnel kiln to burn red brick are the same, there is just a little bit difference in the materials used to build the stove!
Q:The stove which made of refractory bricks and fireclays will produce cracks after being used. How to solve this problem?
The use of low expansion materials will be better. But as for the stove, the appearance of crack is attributed to the selected materials or the environment. And when the temperature is not high, there still seems to be crack, so through expansion joint reservation, not allowing itself to crack
Q:The difference between fireclay brick and refractory cilica brick in the application.
Good thermal shock stability, long-term use temperature is not higher than 1300 degrees, high temperature, high strength, low price of clay brick characteristics, thermal shock stability is the worst, a scrap, can be long-term used under the condition of high temperature (exceed 1400 degrees Celsius) . The temperature of silica brick's soft bearing is close to the melting point. Other industries basically don't use, but the comprehensive performance of high temperature is not good, widely used in low temperature parts of a variety of furnaces. The silica brick is generally used in the coke oven and glass kiln, but anti alkali erosion ability is poor
Q:does all the refractory refer to refractory bricks when making steel?
deoxidizer belongs to ferrous metallurgy auxiliary; refractory used during steelmaking is not only refractory bricks, but also foaming agent, refractory castable and Ladle filler sand.

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range