Factory directly 87% al2o3 0-1mm calcined bauxite with competive price

Ref Price:
Loading Port:
China main port
Payment Terms:
TT OR LC
Min Order Qty:
25 m.t.
Supply Capability:
20000 m.t./month

OKorder Service Pledge

Quality Product

Order On-line Tracking

Timely Delivery

OKorder Service Pledge

Credit Rating

Credit Services

Credit Purchasing

Share to:

Product Description:

   Factory directly 87% al2o3 0-1mm calcined bauxite with competive price

 

 Calcined bauxite introduction :

Bauxite (aluminous soil; Bauxite) is also called the alumina or bauxite, main ingredients are alumina, 

hydrated alumina containing impurities, is an earthy mineral. White or gray, brown and yellow or light red by iron.

 From 4 to 3.9 g/cm3 density, hardness, 1 ~ 3 is not transparent, very brittle. Very difficult to melt.

 Insoluble in water, soluble in sulfuric acid, sodium hydroxide solution. Mainly used for aluminium, refractory material. 

 

 

Calcined bauxite use   

(1) aluminium industry. Used in national defense, aerospace, automotive, electronics, chemical industry,

 daily necessities, etc. 
2 precision casting. Alumina clinker made after the mould precision casting processed into fine powder. 

Used in military industry, aerospace, communications, instrumentation, machinery and medical equipment department. 
(3) is used for refractory products. High bauxite clinker refractoriness is as high as 1780, chemical stability strong, 

and good physical properties. 
(4) aluminum silicate refractory fiber. With light weight, high temperature resistance, good thermal stability,

 low thermal conductivity, heat capacity is small and the advantages of resistance to mechanical shock. 

Used in iron and steel, nonferrous metallurgy, electronics, petroleum, chemical, aerospace, atomic energy, 

defense and other industries. 

 

Calcined bauxiteSpecification :

 

 

GRADE

CHEMICAL CONTENT,%

PHYCICAL PROPERTIES

Al2O3

(%)

Fe2O3

(%)

DENSITY

(g/cm3)

Refractoriness

(℃)

GAL-70

≥70

≤2.0

≥2.75

>1790

GAL-80

≥80

≤2.0

≥2.90

>1790

GAL-85

≥85

≤1.8

≥3.10

>1790

 

 

 

 

 

 

 

 

 

 

 

Size:0-1mm,1-3mm,3-5mm ,200mesh,325mesh or as buyer’s request

Factory directly 87% al2o3 0-1mm calcined bauxite with competive price

Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:How to distinguish the fire resistant level of the rubber and plastic thermal insulation material?
Fire rating grading of external wall thermal insulation materials. 1, China's national standard GB8624-97 divides the combustion performance of building materials external insulation materials into the following grades. Level A: Incombustible materials: Almost no burning materials. Level B1: Incombustible materials: Flame-like material has good fire-retardant effect. In case of fire in the air or at high temperature, it is difficult to fire and doesn't spread quickly, and when the fire source is removed after combustion, it stops immediately. Level B2: Incombustible materials: Combustible materials have a certain flame resistance. In case of fire in the air or at high temperature, it will immediately burst into flames, and easily leads to the spread of fire, such as poles, wooden frame, wooden beams and wooden stairs,ect. Level B3 : Incombustible materials: No flame-retardant effect, hidhly flammable and high fire risk. 2, The external wall thermal insulation materials could be divided according to the fire rating. 1) thermal insulation material that has the level A combustion performance: Spraying inorganic fiber, glass wool, foam glass, ceramic foam, rock wool, foam cement and perlite obturator, and so on. 2), The thermal insulation material that has level B1 combustion performance: Special processed extruded polystyrene board (XPS) / special processed polyurethane (PU), phenolic and polystyrene powder. 3), Thermal insulation materials that have level B2 combustion performance: Molded polystyrene board (EPS), extruded polystyrene board (XPS), polyurethane (PU), polyethylene (PE), etc.
Q:What are the characteristics of the carbon composite refractories?
The features of carbon composite refractories: 1. It is with an aggressive high thermal shock resistance 2. Good resistance to molten steel and slag
Q:What are the fire protection standards of insulation materials?
The combustion performance of thermal insulation materials for exterior walls of all civil buildings, within the scope of fire design auditing and fire control acceptance, should be brought into the auditing and acceptance. As for the "Management Regulations on Supervisions of Fire Prevention and Control for Building Projects" (Ministry of Public Order No. 106) , all civil buildings which are out of the scope of Article 13 and 14 are included in the random check. Before the release of new standard, it must be strictly implemented the Article II of the "Fire prevention Interim Provisions on civil external wall insulation system and external wall decorative" ([2009] No. 46), namely, the insulation materials of civil buildings must use materials with A-level combustion performance.
Q:what needs to be noted when choosing and using blast furnace fireproof materials?
it depends on the size of the blast furnace. below 200 cubic meters alumina bricks and carbon brickcan be used. 200 cubic meters and above are currently integrated bottom, not the same as the size of the cubic level, varying in the use of refactory. I hope my answers above are helpful to you and your ideal anwers.
Q:What is the fire resistance thickness of the thin fire-retardant coatings?
Our thin steelwork fireproof coatings: the fire resistance is 2.5 hours, the thickness is 4.9 mm, the fire resistance is 2.0 hours, the thickness is 3.5 mm, the fire resistance is 1.5 hours, the thickness is 1.75 mm, the fire resistance is 1.0 hours, the thickness is 1.17 mm.
Q:Urgent question: could you tell me that the export of refractory materials to Vietnam is to be packed in wooden cases or smoked?
Why is the apple screen so small?
Q:How to understand qualitative and qualitative refractory materials?
Such as amorphous refractory castable, referred to as bulk loading, cast material, ramming material, refractory clay etc., utensils and other special products. Amorphous refractory material products, refractory heat insulating bricks and experimental and industrial crucible, spraying materials, such as burning bricks, electric melting brick, turn it into required shape and process heat treatment in where it is used.
Q:How to classify the grade of wall fireproof and thermal inuslation matertial?
The level classification of wall fireproof and thermal inuslation matertial: Grade A: incombustible building material: Material almost with no combustion. Grade B1: nonflammable building material: Nonflammable material has good flame resistance. It is difficult to fire in case of fire in the air or at high temperature. It is not easy to quickly spread. After the fire source is removed, combustion stops immediately. Grade B2: combustible building material: Combustible materials have a certain flame resistance. It will immediately burst into flames in case of fire in the air or at high temperature and is easy to lead to the spread of fire, such as wooden column, timber roof truss, timber beam, wooden stairs, etc. Grade B3: Flammable building material: It has no flame-retardant effect and is highly flammable. Fire hazard is very large.
Q:what's the fire endurance of fireproof panel?
non-asbestos calcium silicate board, fireproof panel partition will excced over 4 hours, two single 75 keel. 12 mm fireproofing calcium silicate board partition, through the monitoring of national fireproof construction materials quality supervision center, it's security and refractory time will reach over 4 hours.
Q:What are the requirements for the performance of refractory materials?
Performance requirements for electric furnace lining refractory: 1, sufficient refractoriness and softening point. Because of eletric arc, the inner surface temperature of lining can be as high as 1500 to 1800 degree. 2, strong resistance to slag. Because the dust penetrate into the furnace through pore lining, and the refractory material subject to loss, leading to spalling. 3, good thermal and shock resistance. Because during steelmaking, opening door and lifting of the furnace will lead to sudden changes in the temperature of the furnace lining refractory material, so spalling and cracking may occur, damaging the lining premature. 4, enough strength, because the lining is impact during charging, tilted when vibration,and eroded by metal, slag and airflow. 5, the thermal conductivity shall be small, and the conductivity shall be low. The commonly used furnace refractories are dolomite brick, magnesia brick, high alumina brick, silica brick and magnesia ramming etc.. Because of different working conditions of the various parts of the furnace, the refractory materials are not the same.

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range