E-glass Woven Roving-800gsm

Ref Price:
Loading Port:
China Main Port
Payment Terms:
TT or LC
Min Order Qty:
16000 kg
Supply Capability:
160000kg Per Month kg/month

OKorder Service Pledge

Quality Product

Order On-line Tracking

Timely Delivery

OKorder Service Pledge

Credit Rating

Credit Services

Credit Purchasing

Share to:

Product Description:

Products Description

1.E glass woven roving 800gsm can be used for manufacturing all kinds of FRP products,such as FRP tank,FRP pipe etc.

2.Compatible with unsaturated polyester,vinylresin ,epoxy resin.

Characteristics
1.Consistent thickness and excellent surface treatment.
2. Rapid impregnating and good compatibility with resin.
3.Uniform tension,high dimensional stability and making handing easy.
4.Good mechanical properties and high strength of parts.

Technical Data Sheet

 

TEST ITEM

STANDARD

STANDARD VALUE

AVERAGE VALUE

RESULT

AREA WEIGHT (G/M2)

iso3374

800+/-5%

810

yes

WIDTH (MM)

iso5025

1250±20MM

1250

YES

FABRICS COUNT

(ENDS/10CM)

WARP

iso4602

18±2

18

yes

WEFT

iso4602

18±2

15

YES

TENSILE STRENGTH(N/50CM)

WARP

iso4606

4000

4015

yes

WEFT

iso4606

4000

4015

YES

moisture CONTENT (%)

iso3344

<=0.15

0.1

yes

LOSS ON IGNITION (%)

iso1887

0.4-0.8

0.5

yes

 

 

FAQ

Package and Storage:Eech roll is packed by polyester bag,and then put into a cardboard box or plastic wowen bag.The weight of each roll is between 20 to 85 Kg, The rolls are to be horizontally placed and could be in bulk or on pallet.Optimum storage conditions are between the temperature of 5~35℃ and with the humidity between 35%~65%.The product should be used within 12 months from the time of delivery and remain in theiroriginal packaging until just prior to use.



Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:Is fiberglass cloth antistatic?
Glass fiber cloth with conductive function according to the level of application of alkali content place is not the same, for example with high alkalinity can be used as wires.
Q:What is Teflon?
Generally refers to the Teflon PTFE - (CF2-CF2) n-- Teflon is divided into basic types PTFE, FEP, PFA, ETFE several.High performance special Teflon coating is fluorine coating resin with polytetrafluoroethylene, English name for Teflon, because the pronunciation of reason, commonly known as Teflon, Tie Fulong, Teflon, Teflon and so on (all Teflon transliteration). Teflon (Tie Fulong) coating is a kind of high performance coating is the one and only, with heat resistance, chemical inertness and excellent insulation stability and low friction, the comprehensive advantages with other coatings can not compete, the flexibility makes it can be used in almost all the shape and size of the products.
Q:What's the best form of roof waterproof?
Whenever the decoration of the owners all know that the roof waterproof is very important. Roof roof because of long-term acceptance of the sun and rain erosion, so waterproof requirements higher, both flexibility, can resist certain structural tensile deformation, and make waterproof layer is not easy to crack. Now let me tell you how to do waterproof roof.
Q:How do you do fiberglass fabric on latex paint?
A small area of their own to do the next experiment.
Q:What does "PCB" mean?
We can't transmit electrical signals just as insulation plates, so we need to cover the surface with copper. So we call the PCB board a copper clad substrate. In the factory, the common copper substrate in this code is FR-4, each card manufacturers which in general there is no difference, so we can think of everyone at the same starting line, of course, if it is best to use high frequency board, copper clad PTFE glass cloth laminate high cost. The process of copper is very simple, generally can be made by rolling and electrolytic solution, the so-called rolling is Gao Chundu (>99.98%) of the copper rolling method on the PCB substrate, because the adhesive has excellent epoxy resin and copper foil, copper foil adhesive strength and high working temperature, can be no bubble dip in the molten tin is 260 DEG C in. This process is like rolling dumpling wrappers, but the dumpling wrappers are thin and thin. The thinnest is less than 1mil (industrial unit: mil, 1/1000 inches, equivalent to 0.0254mm)! If the dumpling wrappers are so thin, the pot must leak! The so-called electrolytic copper in junior high school chemistry has learned, CuSo4 electrolyte can continuously manufacture a layer of "copper foil", this is more easy to control the thickness, the longer the copper foil the more thick! Usually the factory has strict requirements on the thickness of copper foil, usually between 0.3mil and 3mil, and has a dedicated copper foil thickness tester to test its quality. Like old radios and amateur PCB, copper is especially heavy, and the quality of the factory is far worse than the computer board.
Q:Glass fiber cloth can be made into handbags, requirements of high temperature 680 degrees or more
There are many kinds of glass fiber fabric, you can choose as long as you choose, such as medium and high strength glass fiber cloth".
Q:Difference and characteristics of fluorine glue glass fiber cloth and three yuan ethylene propylene glass fiber cloth
Fluorine rubber and three yuan ethylene propylene adhesive tape are a new kind of high temperature and corrosion resistant fluorine polymer elastomer, which is a new type of multipurpose composite material coated with glass fiber.
Q:Which is more durable, stone cotton or glass cloth?
Asbestos is a specialized mineral that can be obtained by processing. Glass fiber is usually fused with quartz and alkali. The more alkali is added, the worse the performance is. Many processes require alkali free fiberglass.If you want to talk, open another question
Q:What is the difference between glass fiber plain cloth and glass fiber grid cloth? What are the specifications and specifications of plain cloth and square cloth?
Plaid is especially woven fabric woven from roving. The warp and weft are interlaced with 90 angles. Roving refers to a fiber (monofilament with a diameter of 9 microns or more). At present, the industry is generally used, mostly mining 17 microns.
Q:What are the cracks between the brick wall and the beam column, the cracks between the planks and the cracks in the plasterboard?
You describe these cracks, are essentially composed of different materials in the influence of temperature and humidity of the physical changes now to solve this kind of problem is late with ductile material recovery, wall and ceiling like corner cracking the case, that is to do the above method.

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range