Ductile iron manhole cover C250 Square

Ref Price:
Loading Port:
China Main Port
Payment Terms:
TT OR LC
Min Order Qty:
-
Supply Capability:
-

OKorder Service Pledge

Quality Product

Order On-line Tracking

Timely Delivery

OKorder Service Pledge

Credit Rating

Credit Services

Credit Purchasing

Share to:

Product Description:


Packaging & Delivery

Packaging Detail:standard wooden pallet or as your requirement
Delivery Detail:as per your oder

Specifications

ductile iron Manhole Cover
1.material:ductile iron/cast iron
2.EN124
3.type:A15 B125 C250 D400 E600 F900
4.service:OEM


Light Duty Ductile Iron  Manhole Cover

Product Description:

1) standard: EN124

2) material: cast iron, ductile iron,

3) type:round / square/ triangle

4) producing: sand casting

5) class: A15 B125 C250 D400 E600 F900
6) shape: round/rectangle or asper your requirements

7) color: black/ grey or asper your requirements
8)  size: according to your requirements

9)  service: OEM


Packing&Shipping:

packaging: standard wooden cases with bubble plastic bags for each item or as per your requirements

 delivery detail: 25-30 days


Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:Casting parts, anodizing 20
Yes, the cast aluminium is polarized and gray, but the key problem is to guarantee the quality of the aluminium casting, and the quality of the other aluminium casting is not good.
Q:How to improve the surface roughness of casting parts?
One is to improve the accuracy of the model; the two is to improve the molding sand mesh. How much is the other relationship?.
Q:What's the effect of casting copper?
Copper is one of the main corrosion resistant alloys. When the mass fraction of copper in cast iron is from 0.25% to 1%, the corrosion resistance of copper in the industrial atmosphere can be obviously increased. But copper has very little corrosion resistance in lye or salt solution.Copper can increase the flowability of molten iron and improve its casting ability remarkably.Copper can increase the coercive force and residual magnetic force, but the permeability is not affected.Combined use of copper with other alloy elements, such as copper chromium, copper chromium molybdenum, copper molybdenum, copper manganese, copper vanadium, can achieve greater results.
Q:The cause of fracture and why there is no toughness
This question is too broad, see what the casting casting Oh in order to reduce the wayward cast steel, ductile iron, gray iron and white iron, you can choose the material according to their own requirements.
Q:What's the cause of the choking of the casting?,
Causes of choking fire:1., casting material in the pouring of gas;
Q:What kind of flaw detector is better for casting parts?
If the casting is very small, can be used for fixed magnetic detection machines, of course with fixed magnetic powder the testing machine, the best first contact the manufacturers, because the fixed magnetic particle testing machine belongs to the non-standard equipment, according to the workpiece size, different shape, manufacturing daily inspection and measurement.
Q:What foundry factories are used in the casting parts of China's major automobile manufacturers?
For example Changchun FAW, under a casting, two casting and other casting plant, but there are more than half of all outsourcing in Tianjin Hebei Shandong purchase, many automobile enterprises to casting foundry.
Q:How can the casting be plated with ordinary zinc plating? The coating is too thin and requires 0.08 thickness
Hot galvanizing doesn't seem to workThe zinc layer is 275g/ square meters of material coating is 0.019mm (mm), up to 0.08 thick.
Q:What is normalizing, annealing, tempering, quenching? What is the difference between forging parts and casting parts?
The aim is to make the grain fine and distribute the carbide evenly. The difference between normalizing and annealing is that normalizing cooling rate is slightly faster than annealing cooling rate, so normalizing structure is finer than annealing structure, and its mechanical properties are also improved. In addition, normalizing furnace cooling does not occupy equipment and has higher productivity. Therefore, normalizing may be used instead of annealing as much as possible. The main application areas of normalizing are as follows: for low carbon steel, after normalizing, the hardness is slightly higher than that of annealing, and the toughness is better. It can be used as the pretreatment of cutting. Used for medium carbon steel, instead of quenching and tempering, as the final heat treatment, or as an induction heating method before surface hardening. Used for tool steel, bearing steel, carburizing steel, etc., it can eliminate or restrain the formation of network carbide, so as to obtain the good organization of spheroidizing annealing. For cast steel, the microstructure can be refined and the machinability can be improved. Used for large forgings, which can be used as final heat treatment, so as to avoid larger cracking tendency during quenching.
Q:Can the casting part be phosphating with the phosphating solution of the pickling board?
If it is Phosphating for painting, it is not necessary, because the surface of the casting is rough and can be firmly bonded with the paint film.

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range