Dilatable High Alumina Brick CNBM Made in China

Ref Price:
Loading Port:
Shanghai
Payment Terms:
TT OR LC
Min Order Qty:
5000 m.t.
Supply Capability:
50000 m.t./month

OKorder Service Pledge

Quality Product

Order On-line Tracking

Timely Delivery

OKorder Service Pledge

Credit Rating

Credit Services

Credit Purchasing

Share to:

Product Description:

Specifications

ISO9000 Certificate

brandXLG80XLG75XLG70
Al2O3, %807570
Fe2O3 , %1.51.51.5
refractoriness/°C179017901790
BD ,g/cm3202022
AP, %2.802.702.65
CCS, MPa757070
refractoriness under load/°C162016001580
reheating linear change PLC ( 1500 °C× 2h ),%+ 0.2+0.2+0.3


Zibo HITECH Material CO.,LTD is a specialized manufacturer and supplier of refractory material in China.Details are following:


1-- Ordinal Refractory Product.

     Fireclay brick, silicon brick, mullite brick, high alumina brick, and magnesia brick.

2--Glass Refractory Product.

    Including Oxidized Fused Cast AZS Brick, Fused Mullite Brick, Dense Zirconia Brick,

    High Tin Pot  Bottom Brick etc

3--Steel Iron Refractory Product.

    Including High alumina brick, fireclay brick Magnesia Chrome Brick, Magnesia Alumina BriCK,

    Magnesia Carbon Brick, and some other related.

4--Refractory Castable/Precast---- LCC castable ULCC, SFC.

    Silica Castable, Corundum Castable, High Alumina Castable, Zircon Castable Mix,Fireclay  castable,Light Fireclay Castable, High Alumina Mortar, Mullite Mortar, Corundum Mortar etc

5--Ceramic fiber.

Dilatable High Alumina Brick CNBM Made in China

Dilatable High Alumina Brick CNBM Made in China


Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:Ask for help about the phase of refractory material
Binding phase. The binding phase is the phase outside the main crystal phase or the main crystal phase and the sub crystalline phase. The binding phase can be made up of either a fine crystal or a glass phase or a composite of the two. Such as the combination of magnesia brick, magnesia chrome brick, magnesia brick and other basic refractories in phase is composed of crystal matrix; silica brick, clay brick is made of glass phase in the form. When the matrix is formed at high temperature, the liquid phase is low, and the viscosity of the liquid phase is low and the quantity is large, the production and properties of refractory products are essentially controlled by the substrate.
Q:Zirconium corundum 25 content and 40 content, how to distinguish in appearance?
The fused zirconia corundum brick is mainly made of fused zirconia and corundum. ZrO2-Al2O3-SiO2 three element system fused brick, containing Al2O3:40% to 50%, ZrO2:30% to 50%, SiO2:10% to 17%.From the point of view of data analysis, there is no radioactive substance in it, and it will not cause harm to the human body.
Q:What are the main constituents of refractory bricks
Clay brick and clay brick are mainly composed of mullite (25% ~ 50%), glass phase (25% ~ 60%) and square quartz and quartz (up to 30%). Usually with hard clay as raw material, pre calcined mature material, and then with soft clay, semi dry or plastic molding, the temperature at 1300~1400 C fired clay brick products. Can also be added a small amount of water, glass, cement and other binders to make non burning products and amorphous materials. It is a refractory brick commonly used in blast furnaces, hot blast furnaces, heating furnaces, power boilers, lime kilns, rotary kilns, ceramics and refractory bricks.
Q:What is the difference between corundum and high alumina?
The main components of high alumina brick are high alumina bauxite, mullite and partial corundum sand.The difference between them lies in the content of alumina and the alumina refractory products with alumina content higher than 48%The content of Al2O3 is higher than 90%, which is called corundum brick.
Q:What refractory materials are adopted in each part of the blast furnace
Bosh temperature reaches 1600~1650, high alumina brick, corundum brick or silicon carbide brick. The upper hearth tuyere zone near the temperature at 1700~2000 Deg. C, the use of sillimanite brick, corundum and silicon carbide refractory filler, Shi Mozhi. Bottom temperature at 1450~1500 Deg. C, the use of graphite bricks and microporous carbon brick, now also used corundum brick, Gang Yumo brick and synthetic mullite brick.
Q:Expansion ratio of lightweight corundum refractory bricks
Now with the production of lightweight foam corundum brick, basically still meters with molding casting, moulding after together with die in the drying room drying in 60~70 C 4 days of release, then the appropriate drying, finally after 1300 and 1550 C firing, the total burning time: 50~60h. Light corundum brick after firing is usually not the size and shape of accurate, so that products after the kiln to mechanical or manual cutting, can be made into a density of 0.8 - 1.3g/cm3, 4MPa compressive strength and porosity, the thermal conductivity of 70%~80% 0.17W/ (M - K), light-weight corundum brick use temperature of 1500~1700 DEG C.
Q:What kind of fused corundum corundum brick should be used for each part of the glass furnace?
The compact microstructure of AZS33# zirconia corundum brick makes the bricks resistant to glass liquid corrosion, and it is difficult to produce stone or other defects in the glass kiln. It is the most widely used product in the glass furnace. It is mainly applied to the upper structure of the melting pool, the wall brick of the working pool and the paving brick, the material way, etc..
Q:How do corundum bricks bind?
High temperature bonding clay can be used for bonding masonry
Q:What are the advantages of refractories?
Special refractories are new inorganic non-metallic materials developed on the basis of traditional ceramics and refractory materials. For example, AZS brick, corundum brick, magnesia chrome brick, silicon carbide, silicon nitride bonded silicon carbide, nitrides, silicides, sulfide, boride, carbide and other non oxide refractory materials; calcium oxide, chromium oxide, alumina, Magnesium Oxide, beryllium and other refractory materials. Often used insulation refractories are diatomite products, asbestos products, insulation panels and so on
Q:What's the jade stove for?
Is it a furnace made of corundum or a furnace for smelting corundum?Corundum brick stove is commonly used as a refractory material sintering furnace, can be fired refractoriness in refractories, below 1700 degrees such as brick, corundum brick, brick, alumina hollow ball and so on

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range