Product Description:

Brief discription for Clay brick of refractory brick for Nonferrours Metals

CMAX Clay brick of refractory brick for Nonferrours Metals are classified according to alumina content ranging from 48% to 90%.

CMAX Clay brick of refractory brick for Nonferrours Metals are commonly used in blast furnace, hot blast furnace, the roof of electric furnace, teeming ladle, rotary kiln,regenerator, etc.



Brief features for Clay brick of refractory brick for Nonferrours Metals

Low thermal conductivity   

Excellent acid and base slagging resistance

High refractoriness

Excellent thermal shock resistance  

Excellent mechanical strength

Good spalling resistance and wear resistance.

Good corrosion resistance.

High-temperature creep rate is quite low.

Good volume stability at high temperature.

Low bulk density, low thermal conductivity, good thermal insulation performance.



Technical data for Clay brick of refractory brick for Nonferrours Metals

ITEM

UAL48

UAL55

UAL65

UAL75

UAL80

UAL85

ALP80

Refractoriness,  

1750

1770

1790

1790

1810

1810

1810

Apparent Porosity,%

22

22

23

23

20

20

18

C.C.S, Mpa 

39

44

49

53

55

60

100

Refractories Under   Load (0.2Mpa),℃ 

1420

1470

1500

1520

1500

1520

1550

Reheating Linear   Change,%

1450x2h              0.1-0.4

1500x2h              0.1-0.4

1500x2h              0.1-0.4

1500x2h         0.1-0.4

1550x2h              -0.5+0.5

1550x2h              -0.5+0.5

1550x2h              -0.5+0.5

Al2O3   Content , %

48

55

65

75

80

85

82

 

FAQ

Q1:Are you a manufacture or trader?

A:Factory+trade(mainly factories,at the same time,we operates other related products).

Q2:Can we visit your factory?

A:Sure,welcome at any time,seeing is believing.

Q3:What's the MOQ of trial order?

A:No limit,We can offer the best suggestions and solutions according to your condition.

Q4:Which payment terms can you accept?

A:T/T,L/C are available for us.

Q5:After an order is confirmed,when to deliver?

A:15-25days after deposit.

 

Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:What's the reason of cracks in refractory bricks?
If it is made to refractory bricks,dry in the air naturally for 10 days, then put into the drying furnace, which is certainly better than the brick is put to the furnace directly, this is not easy to crack. After all, the moisture of brick will run in the air. See the semi-finished products (not crack is really no crack), but after drying, it has cracks, this is must because moisture runs quickly in a short time. If it cracks after high temperature heat treatment, the reason is very complicated, such as after high temperature burning, temperature decreases too fast, resulting in a large temperature change, then it cracks. Or in the process of high temperature heat treatment, the internal reaction is intense, and generate some volume expanding materials, resulting in cracks and so on. Mullite Petrochemical reaction, spinel reaction and so on, the reactions of a lot of materials are the volume expansion
Q:Would you please tell me how to use the simple method to identify shale brick, clay brick?
Is the shale as raw material for high temperature baked bricks using shale and coal gangue, clay brick not dense surface, general clay brick for load-bearing structure, relatively thick, single shape; shale brick shapes, shapes with holes, in non bearing structure.
Q:When using high alumina refractory brick, what are the reasons leading to the decline of the performance of high alumina brick?
The excess air coefficient is controlled in 1, in order to prevent producing water cracks in the production of high aluminum refractory brick from, control the water absorption of 2 grade clinker of bauxite with high alumina below 4%-5%. 1-1,the water absorption of the tube mill should also be controlled below 6%, and adjust thermotechnical, making the high alumina refractory brick burning be in the stable weak oxidizing atmosphere. should be 2
Q:several refractory brick of rotary kiln several is damaged, how many refractory bricks should be replaced?
The life of refractory bricks in rotary kiln is generally short.
Q:Shale brick and clay brick? Answer before you know it
Is the shale as raw material for high temperature baked bricks using shale and coal gangue, shale sintered porous brick, hollow shale brick, shale brick, high insulation, water wall and other types of modular brick.
Q:Why can't gravity retaining walls be made of clay bricks?
The masonry of gravity retaining walls, of course, takes into account compression problems, and the use of clay bricks requires consideration of compression calculations and service life.
Q:What are needed to make refractory bricks with micro silica?
Micro silicon powder is used in mortar and concrete, the ore-smelting electric furnace produces a large amount of strongly volatile gases SiO2 and Si, bridges, seaports. It is ferroalloy. When smelt ferrosilicon and industrial silicon (metallic cilicon), micro silicon power is also called silica fume or condensed silica fume, dam, gas emissions and air condensate and deposit by rapid oxidation, water conservancy, airport runway, tunnel, high-rise buildings, subway, railway, highway and culvert. Application fields of silicon power are cement concrete pavement and mine roadway anchor reinforcement and etc.
Q:The shape and size of general used refractory brick
240mm * 115mm * 53mm. and the width is 115mm, the shape and size of mechanism red brick is: 230mm * 114mm * 65mm, the outline dimension of special refractory brick is of 65mm thickness according to the national standard: Length is 230mm. That is: Length is 240mm. General type refractory brick's outline dimension is of 114mm width. That is, thickness is 53mm: 345*328*97
Q:What is the clay used to make the refractory brick?
Lining brick of teeming ladle; refractory clay used in building materials industry to produce high alumina bricks for cement kilns and glass furnaces, as well as anti sliding, high alumina lining bricks and high alumina refractory clay. The hard clay in refractory clay is used for making blast furnace refractory material, which is used in agriculture as a fertilizer promoting agent and, and electron. High alumina clay is also used in the oil well, generally does not disperse in water. In metallurgy, accounts for 2/3 of abrasive products, and so on. Hard clay and semi hard clay can be used to manufacture daily-use ceramics. High alumina clay after calcination, which has high temperature resistance! Refractory clay refers to the degree of fire resistance is greater than 1580, the hardness and proportion is relatively big, the refractoriness is good. They except has relatively high refractoriness. Such as aluminum sulfate, its dosage accounts about 70% of all the refractory materials;
Q:How to built refractory bricks as fitting between square and circle ducts
Use rectangle at the bottom and knife type for the top. trapezoid for junction.

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range