China Supplier Offer Calcined Bauxite With Best Grade

Ref Price:
Loading Port:
China main port
Payment Terms:
TT OR LC
Min Order Qty:
25 m.t.
Supply Capability:
2000 m.t./month

OKorder Service Pledge

Quality Product

Order On-line Tracking

Timely Delivery

OKorder Service Pledge

Credit Rating

Credit Services

Credit Purchasing

Share to:

Product Description:

Quick Details

Place of Origin:

Shaanxi, China (Mainland)

Shape:

Powder

Material:

Bauxite

SiO2 Content (%):

-

Al2O3 Content (%):

85%,84%,89%

MgO Content (%):

-

CaO Content (%):

-

Refractoriness (Degree):

1770°< Refractoriness< 2000°

CrO Content (%):

-

SiC Content (%):

-

Model Number:

JT-88

Brand Name:

CNBM

Fe2O3:

2% max

TIO2:


K2O+Na2O:

0.3%max

CaO+MgO:

0.5%max

Bulk Density:

3.0min



Packaging & Delivery

Packaging Details:Packing in 25kg pp bags or 1MT/1.25MT bulk bags
Delivery Detail:within 15 days against the contract

 

China Supplier Offer Calcined Bauxite With Best Grade

China Supplier Offer Calcined Bauxite With Best Grade


Product Description

 

Application

1) The bauxite for aluminum industry in defense, aerospace, automotive, electrical, chemical, and daily supplies.

2) Bauxite clinker processed into fine powder and made after the casting mold. Used in military, aerospace, communications, instrumentation, machinery and medical equipment sector.

3) The bauxite can be used in refractory products. The refractoriness of high-alumina clinker is up to 1780 ℃. Its features are chemical stability strong, and physical properties of sound.

4) It can be raw material for alumina cement, abrasive materials and aluminum compounds.

Technical data sheet

Item

AL2O3

FE2O3

TIO2

K2O+Na2O

CaO+MgO

Bulk density

GAL70

≥70

3.0

≤4.0

≤0.6

≤0.6

≥2.7

GAL75

≥75

≤2.5

≤4.0

≤0.5

≤0.5

≥2.8

GAL80

≥80

≤2.5

≤4.0

≤0.3

≤0.5

≥2.9

GAL85

≥85

≤2

≤4.0

≤0.3

≤0.5

≥3.0

GAL86

≥86

≤2

≤4.0

≤0.3

≤0.5

≥3.1

GAL87

≥87

≤2

≤4.0

≤0.3

≤0.5

≥3.2

GAL88

≥88

≤1.8

≤4.0

≤0.25

≤0.5

≥3.25

GAL90

≥90

≤1.5

≤4.0

≤0.25

≤0.5

≥3.4

China Supplier Offer Calcined Bauxite With Best Grade

China Supplier Offer Calcined Bauxite With Best Grade



Company Information

CNBM International Corporation (CNBM International) is the most important trading platform of CNBM Group Corporation, a state-owned company under the direct supervision of State-owned Assets Supervision and Administration Commission of the State Council.

Since 2004, the trading volume of CNBM International has been doubled in 5 successive years owing to the support of superior corporations and effort of all staff. Meanwhile, we have established strategic partnerships with hundreds of domestic manufacturers and sound business relations with clients from over 120 countries. Currently, we have wholly-owned overseas subsidiaries and branches in 5 countries with a view to realize localization, which also represents an essential progress in our globalization target.

China Supplier Offer Calcined Bauxite With Best Grade

China Supplier Offer Calcined Bauxite With Best Grade


Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:What are the features of construction class A fire resistant door ?
1, Save space and reduce cost. Feature of Nanjing Cathay Class A external wall thermal insulation materials : the thickness is between 60mm--180mm, so compared with the traditional block thickness, it saves architectural space greatly. At the same time, the weight is only 1/10 of that of the traditional wall, thus reducing coast in terms of architectural structure. 2, Fireproof and green. Features of Nanjing Cathay class A fireproof external wall thermal insulation materials: fire endurance under high temperature of 1000℃ is 4 hours, and non-combustible performance can reach state A level, without any toxic gas in full compliance with international environmental standards. 3, Waterproof. Features of Nanjing Cathay Class A fireproof external wall thermal insulation materials: no slightest leakage when it is being used in containers for water without any waterproof finishing. It can be used in kitchens, bathrooms, basements and other wet areas. 4, Sound insulation. Features of Nanjing Cathay class A fireproof external wall thermal insulation materials: internal materials and EPS polystyrene foam granule have good properties of sound insulation and sound absorption. 90mm-thick wall can insulate 40dB sound, in line with national standard of sound insulation for residential building. 5, Thermal insulation. Features of Nanjing Cathay Class A fireproof external wall thermal insulation materials: main raw material is frezing resistant and thermal insulating material which is environmentally friendly and energy saving. With good effect of thermal insulation, it can keep indoor temperature at a constant level, so as to make the environment more comfortable.
Q:How should fireproof building materials be ranked?
According to our national standard GB8624-97, the combustion performance of building materials are divided into the following levels: A class: Incombustible building materials: the material is almost incombustible. B1 class: Flame-retardant building materials: they are better in fire retardation. It is non-combustible when meeting open fire in the air or under high temperature, and it is difficult for the fire to spread quickly. Besides, when the fire source is removed, combustion stops immediately. B2 class: Combustible building material: It has certain fire retardation. In case of open fire in the air or at high temperature, it will immediately burst into flames, and easily lead to the spread of fire, such as the spread to wooden pillars, timber roof truss, timber beams, wood stairs, etc. B3 class: Flammable building material: It has no fire retardant effect at all, but is highly flammable with high fire risk. Hope my answer can be accepted.
Q:What are the requirements for the performance of refractory materials?
Refractory materials should have very high refractoriness, high temperature heat load and resistance to softening, melting; with high volume stability, resistance to high temperature and heat load, volume shrinkage and only uniform expansion; high strength at room temperature and high temperature strength, high load softening temperature, under the joint action of heat load and heavy load, no loss of strength, creep collapse; Electric furnace analysis should have good resistance to thermal shock, resistance to rapid temperature changes, no crack, not flaking; with excellent slag resistance.
Q:Is the linear change on reheating the same as heating permanent linear change of refractory material?
“+”represents expansion. the afterexpansion and aftercontraction after cooled to be at room temperature. The change may significantly damage the masonry of thermal kiln. There are regulations on the linear change on reheating of common refractory material in the national standard. Some physical chemical changes may continue. It is defined as the change from being heated to the specified temperature of refractory material sample. Heat preserving for a while till afte cooling to be at room temperature, then the residual will expand or contract in its length, heat preservation for a while, organization vitrification, the irreversible changes of its length refers to heating the firing refractory to be at high temperature, so as to make the volume of refractory materials expand or contract, due to the influence of uneven temperature or lack of time, otherwise it will cause the deformation of the refractory ball and make this indicator within standard even reach smaller value, so firing control must be strengthened in product production. But it is should not be too high. For refractory materials with same chemical composition, the linear change on reheating is produced in the heating process. Properly increasing sintering temperature and prolonging the holding time is an effective process measures, make its firing inadequate. When subjected to high temperature, it can reduce the thermal shock resistance. Minus sign "-" represents contraction. The permanent line rate refers to heating the fire refractory ball to the specified temperature. Linear change on reheating, also known as residual linear change, is an important indicator to assess the quality of refractory in the long time use. To control the permanent line rate within the standard or reach the minimum value.
Q:Which fireproofing materials factory is the best in Xiangyang?
Xiangyang Shenglaide Door Technology Co., Ltd. Location: Taibai Road, Fancheng District, Xiangfan, Hubei Province Xiangyang Ai'ruite Door Technology Co., Ltd. Location: Scientific and Technical Pioneering Park, Xiangcheng District, Xiangfan, Hubei Province Xiangyang Innovation and Ideal Manufacturing Co., Ltd. Location: Xiangyang Xiangfan state Jianshe Road, Xiangzhou District, Xiangyang, Hubei Province
Q:What are the types of advanced refractory?
According to the chemical composition of minerals,refractory can be divided into eight categories: 1, siliceous material. 2, aluminosilicate materials. 3, magnesia materials. 4, dolomite materials. 5, chromium materials. 6, the carbonaceous material. 7, zirconium materials. 8, special refractories. 1. refractories according to chemical properties can be divided into three categories: 1, acidic refractory materials. 2, neutral refractories. 3, basic refractories. 1. refractories according to chemical properties can be divided into three categories: 1, ordinary refractories, refractoriness is 1580-1770 degrees. 2, advanced refractories refractoriness is 1770-2000 degrees. 3, super refractories refractoriness higher than 2000 degrees. 3. refractory according to the forming process can be classified into seven categories: 1, natural rock molding process. 2, compression moulding refractories. 3, moulding refractories by casting. 4, plastic molding refractories. 5, ramming molding refractories. 6, injection molding refractories. 7, extrusion molding refractories.
Q:Does hardware construction materials contain refractory?
refractory includes one kind of building materials. It is a special material and not commonly used.
Q:What is the appropiate thickness if fire resistant time for ultra thin steel structure coating is 2.5 hours?
According to the "code for fire protection design of tall buildings", the fire resistance time of the component is at the first level: 3 hours, beam: 2 hours, floor: 1.5 hours;if fire resistance level is level the requirement for time of fire resistance component is the column: 2.5 hours, beam: 1.5 hours, floor: 1 hours. For fire resistant coating, fire resistance time for ultra-thin fire retardant coating is shorter than 1.5 hours. If the time exceeds 1.5 hours, thick fire resistive coating should be used. Steel structure can adopt surrounding concrete or brick, fireproof coating, fireproof board coating and composite structure for its fire resisitance. Fire resisitance board can be divided into thick fire protection plate and thin plate, the thickness of the plate thickness of the fire is between 20 ~ 50mm, mainly includes calcium silicate fireproof board and expansion boring stone fire board, the main varieties are KB board, CF; thin fireproof plate is between 6 ~ 15mm thick, the main varieties include enforced short fiber cement plate, ordinary enforced fiber silicate calcium board and glass cloth reinforced inorganic board. As is known to all, steel structure usually will lose bearing capacity usually in 450 to 650 degree, leading to deformation, steel column and beam bending, and be no longer usable at last. Generally fire resistant limit of unprotected steel stucture is about 15 minutes. 1.5 hours;if fire resistance level is level the requirement for time of fire resistance component is the column: 2.5 hours, beam: 1.5 hours, floor: 1 hours. Steel structure an use surrounding concrete (or masonry), fire retardant coating, fire retardant plate and compround structure to achieve the required refractory limit. Hope my answer will help you.
Q:What are the materials of class A fire resistant window?
Environmentally friendily, non-poisoned non-peculiar smell, non-radioactive; non-combustible, fireproof, moisture-proof, corrosion-resistant; easy to operate, lightweight, high strength, themal insulation, sound insulation; able to be cut, planed, sawed and carved. It also meets GB8624 -2006A1 level non-combustible standards. Lightweight, high strength, anti-aging, corrosion resistance; meeting the GB / T20285-2006 Opium (AQ1) safety and environmentally friendly products; Foamed fire door core board specifications: 2100 × 900 × (26 ~ 65) mm; 2050 × 850 × (26-65), and many other specifications. I hope my answer can help you.
Q:For refractory, what is critical particle size? Thank you.
For example, in refractory technology, if there is an express of equal to or lower than 0.008mm, 0.008 refers to critical particle size. The main criterion for judging performance of three major continuous casting is the major three normal temperature indexes (compressive strength and anti bending strength at normal temperature, apparent porosity and bulk density). Does this criterion have any defect? How to do multiple test if high-temperature index introduced? Carbon bond is one of the three major castings. How does it form? What do you think of it? Hope someone explains it for me. Thanks a lot!

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range