Brown fused aluminum

Ref Price:
Loading Port:
China Main Port
Payment Terms:
TT OR LC
Min Order Qty:
-
Supply Capability:
-

OKorder Service Pledge

Quality Product

Order On-line Tracking

Timely Delivery

OKorder Service Pledge

Credit Rating

Credit Services

Credit Purchasing

Share to:

Product Description:

Specifications

high hardness , high strength , impact resistance, hightemperature resistance , anti-oxidation, corrosion resistance, low creep

BFA / brown fused aluminum oxide for refractory & abrasives

Brow fused alumina ,Brown Corundum, also known as carborundum , TianZhen Brown corundum , with high-quality abrasive grade bauxite as main raw material , made by arc melting temperature above 2000 degrees ,from the mill crushed plastic , magnetic separation to iron ,sieve into a variety of particle size, its dense texture and high hardness, formation of spherical particles . The main chemical composition of the corundum AL2O3, its content of 92.5% -97% , and the other containing a small amount of Fe , Si , Ti , and so on .


Performance :


high hardness , high strength , impact resistance, high temperature resistance , anti-oxidation, corrosion resistance, low creep .

suppliers brown fused aluminum Technical Data Information:

Using

Specifications

The Main Chemical Components%

Magnetic Contents%

Al2O3

Fe2O3

SiO2

TiO2

Abrasive

F

4#-80#

95.0

0.25

1.5

2.3

0.05

90#-150#

95.0

0.03

180#-240#

95.0

0.02

P

8#-80#

95.0

0.25

1.2

2.5

0.05

100#-150#

94.0

0.03

180#-220#

93.0

0.3

1.5

2.5

0.03

W

90#-150#

92.5

0.4

1.8

3

Refractory

Size Sand

0-1mm

1-3mm

3-5mm

5-8mm

8-12mm

95.0

0.25

1.5

2.3

25-0mm

10-0mm

50-0mm

30-0mm

95.0

0.25

1.5

2.3

Powder

180#-0

200#-0

320#-0

94.5

93.5

0.3

1.5

3

Note: according to user needs , Any specific products can be produced by your special request.  

Any questions please kindly let me know, Tony Chen will always here to help you.

Packing:

· 25kg/bag,1000kg/big bag;

· 1000kg/big bag;

· 1000kg/big bag with the pallet;

· Othe packing is allowed as required

suppliers brown fused aluminum Applications:

Application

Vitrified tools        

Lapping          

Resinoid tools        

Blasting          

Polishing            

Scrubing        

Tumbling              

Deburring      

Self-tumbling      

Non-slip          

Lapping compound

Wire saw


Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:What are fireproofing materials?
Plants often use the fireproof sealing material with steel structures without much modification. All the panels that meet the first-order fire protection requirements can be fireproofing materials. Like gypsum boards, aluminum sheets and so on. . Coatings are usually those with fine powder, high density and good sealing. Hardeners mainly depends on specific requirements. .
Q:What 's the highest temperature can magnesium plate glass resist ?
Glass magnesium plate (commonly known as magnesium oxide or glass magnesium plate) is a magnesium jointing material with stable performance made by adding modifier and processing ternary system composed of magnesium oxide, magnesium chloride. It is a new non-combustible decorative materials comprounded by moderately alkaline fiberglass net as enhanced material and lightweight material as filler. 1, Applications Wall panels, ceiling panels, fire-resistance boards, water-proof boards, boxes, etc.. It can replace wooden plywood panel and be made into dado, door panels, furniture, etc., or into distemper paint water paint to one's need, and can akso be processed into various types of plate surface. It is also applicable to projects undertaken in damp environment such as basement, civil air defense, mines. It can be comprounded with a variety of thermal insulation materials into compround thermal insulation materials 2, Product features: Magnesium plate glass is high temperature resistant, sound absorbing, and capable of preventing water, pests, dampness, corrosion, poison, pollution. Paint can directly be applied to the surface of the plate. Air nails are usable for the plate, to which ceramic tile can also be applied with good pigmentation High strength, flexibility when bending, convenient for decoration. It can be sawed, nailed, and glued. 3, the use of glass magnesium plate: Glass magnesium board is a basic intermediate materials Main occasions for applications: HPL Series: Top of the tunnel ceiling. Decorative plate series: Decoration in hotels, office buildings, residential buildings Board series: Ceiling, partitions, fire proof doors and other products. Sound-absorbing panels: Subway, railway stations, theaters, factories and other public buildings.
Q:What's the fire resistance rating of the exterior fire retardant coating?
Current fireproofing material is mainly classified into five grades: A class: Incombustible building material which is almost incombustible. A1 class: It is noncombustible and cann't cause open fire. A2 class: It is noncombustible but needs to measure the smoke it will cause and that should be qualified. B1 class: Flame-retardant building materials: Good in fire retardation, it is non-combustible when meeting open fire in the air or under high temperature, and it is difficult for the fire to spread quickly. Besides, when the fire source is removed, combustion stops immediately. B2 class: Combustible building material: It has certain fire retardation. In the case of open fire in the air or at high temperature, it will immediately burst into flames, and easily lead to the spread of fire, such as the spread to wooden pillars, timber roof truss, timber beams, wood stairs, etc. B3 class: Flammable building material has no fire retardation effect at all. It is highly combustible with big fire risk. Besides, the classifications of fire resistance rating of building materials are different according to different standards: dDIN4102: A1, A2, B1, B2, B3; x0dEN13501-1: A1, A2, B, C, D, E, F. Hope it helps.
Q:who knows the fire resistant levels of fireproofing glass?
According to the fire resistance levels, it can be divided into three categories: Class A: a kind of fireproofing glass that can satisfy the requirements of refractory integrity, refractory and thermal insulation at the same time. Including composite flameproof glass and perfusion type fireproofing glass . This kind of glass has the properiyies of transmittance, fireproofing ( smoke insulation, fireproofing, and keeping out thermal radiation), sound insulation, shock resistance, and it's suitable for steel and wooden fire door of building decoration, windows, varnishing, partition walldaylighting roof,ceiling screen,perspective floor and other construction components demading for transparency and fireproofing. Class B: Marine fireproofing glass, including porthole fireproofing glass and rectangular window fireproofing glass, surface glass pane is tempered safety glass, the inner surface glass pane material can be arbitrary selection. Class C: it's a kind of monolithic fireproofing glass that only satisfies the requirements of refractory integrity. This kind of glass has characteristics of transmittance, fireproofing, smoke insulation and high strength,etc. It's suitable for fireproofing glass partition wall, fire Windows, outside curtain wall and other places without insulation requirements.
Q:What are the applications of refractory in petroleum?
It can be used in chemical filler.
Q:What refractories are used in various parts of the blast furnace.
Blast furnace from top to bottom has the throat, hearth staves, waist, bosh, hearth and furnace bottom. the specific structure is as follows: The throat is the first to be affected by the impact and abrasion, generally use high-density alumina bricks. the upper and central portion of temperature furnace is only 400 ~ 800 ℃, the area with high alumina bricks and silicate bricks. The lower part of furnace is subject to erosion and dust erosion alkali metal vapor due to high temperatures, it is required in such case to use high quality clay brick,high alumina brick,carborundum brick,corundum brick that is slag resistance and alkali resistance, temperature resustant and wearproof. Furnace bosh temperature reached 1400 ~ 1600 ℃, serverly eroded by slag,vapor, flush. so we use carborundum brick and reaction-bonded silicon carbide brick. Bosh temperature reaching1600 ~ 1650 ℃, using alumina brick, corundum brick or silicon carbide brick. the temperature of Hearth near the upper portion of the outlet zone at 1700 ~ 2000 ℃, use of silicate bricks and corundum castable graphite filler, silicon carbide bricks. In 1450 Silly twitch bottom temperature sealing die of hunger slander bet phoenix astringent preserved Grade ~ 1500 ℃, use of graphite bricks and microporous carbon bricks, now use more corundum brick, corundum mullite brick and synthetic mullite brick. x26lt;P class x3d "share-btn"x26gt;
Q:What are included in wall fireproofing material?
Wall fireproofing materials include dry wall and gypsum block. Dry wall is made into board material through process by using building plaster as main material, adding an appropriate amount of additive and fiber to make board core and using tailor-made board paper as protection surface. Dry wall ia characterized by light weight, sound insulation, heat insulation, strong processing performance and easy construction method. Gupsum block is lightweight building plaster product made by using building plaster as main raw material, adding water, stirring, moulding by casting and drying. Fiber reinforced material or lightweight aggregate are allowed to add during the production and foaming agent can also be added. It is soundproof, fireproof, convenient to construct and many other advantages. It is a kind of new wall material with low carbon, environmental protection, health and in line with the development requirements of the times.
Q:Which are fire proofing thermal insulation materials?
Fire proofing thermal insulation materials include: fire proofing heat insulating brick, fire proofing thermal baffle, fire proofing thermal insulation paper, fire proofing thermal insulation felt, fire proofing blocking, fire proofing fiber bulker, castable refractory, etc. Yizhen Decoration wish you a happy life!
Q:What is the appropiate thickness if fire resistant time for ultra thin steel structure coating is 2.5 hours?
According to the "code for fire protection design of tall buildings", the fire resistance time of the component is at the first level: 3 hours, beam: 2 hours, floor: 1.5 hours;if fire resistance level is level the requirement for time of fire resistance component is the column: 2.5 hours, beam: 1.5 hours, floor: 1 hours. For fire resistant coating, fire resistance time for ultra-thin fire retardant coating is shorter than 1.5 hours. If the time exceeds 1.5 hours, thick fire resistive coating should be used. Steel structure can adopt surrounding concrete or brick, fireproof coating, fireproof board coating and composite structure for its fire resisitance. Fire resisitance board can be divided into thick fire protection plate and thin plate, the thickness of the plate thickness of the fire is between 20 ~ 50mm, mainly includes calcium silicate fireproof board and expansion boring stone fire board, the main varieties are KB board, CF; thin fireproof plate is between 6 ~ 15mm thick, the main varieties include enforced short fiber cement plate, ordinary enforced fiber silicate calcium board and glass cloth reinforced inorganic board. As is known to all, steel structure usually will lose bearing capacity usually in 450 to 650 degree, leading to deformation, steel column and beam bending, and be no longer usable at last. Generally fire resistant limit of unprotected steel stucture is about 15 minutes. 1.5 hours;if fire resistance level is level the requirement for time of fire resistance component is the column: 2.5 hours, beam: 1.5 hours, floor: 1 hours. Steel structure an use surrounding concrete (or masonry), fire retardant coating, fire retardant plate and compround structure to achieve the required refractory limit. Hope my answer will help you.
Q:Who knows how to divide the building fire grade and fire resistance grade?
I hope to help you building fireproof rank division is one of the most basic measure in building fire safety technical measures, Building's fireproof rank is divided into class one, two, three, four according to China's architectural design specification. Fire-resistant capability of the highest level is the strongest; Fire resistance of four level of the weakest. The fire resistance level of a building depends on the combustion performance and fire resistance of the building components that comprise the building. The so-called building component refers to a series of basic components, such as wall, foundation, beam, column, floor, stair, ceiling and so on. The judgment condition of the fire resistance There are three conditions for components' fire resistance limit to be reached, namely, the fire resistance limit of the building component: Loss of support and integrity; loss of time to fire the role of the time; as long as any of these three conditions is met, it will reach its limit of fire. Hope my answer will help you.

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range