Best Quality Natural Flake Graphite Products

Ref Price:
Loading Port:
Qingdao
Payment Terms:
TT OR LC
Min Order Qty:
500 m.t.
Supply Capability:
1000 m.t./month

OKorder Service Pledge

Quality Product

Order On-line Tracking

Timely Delivery

OKorder Service Pledge

Credit Rating

Credit Services

Credit Purchasing

Share to:

Product Description:

Specifications

F.C:80%min-98%min Size:+80mesh,+100mesh,-100mesh.

1. Description & Application

    Widely applied to high quality fire resistance material and coating of metallurgy industry,hot working

    material stabilizer of military industry,lead of light industry,carbon brush of electrical industry,electrode of

    battery industry,and catalyzer and additive of fertilizer industry.After further process,scale graphite can be

    made into the following high-tech products such as graphite colloidal graphite,graphite compacting material

    and composite material,graphite products,and graphite anti-friction additive,which are becoming important

    nonmetal mineral materials in every industry.

2. Technical Specification


    

ITEM

F.C %(min)

V.M %(max)

ASH %(max)

MOISTURE

%(max)

SIZE

-198

98

1.0

1.0

0.5

-100mesh

+198

98

1.0

1.0

0.5

+100mesh

-197

97

1.2

1.8

0.5

-100mesh

+197

97

1.2

1.8

0.5

+100mesh

-196

96

1.2

2.8

0.5

-100mesh

+196

96

1.2

2.8

0.5

+100mesh

-195

95

1.2

3.8

0.5

-100mesh

+195

95

1.2

3.8

0.5

+100mesh

-194

94

1.2

4.8

0.5

-100mesh

+194

94

1.2

4.8

0.5

+100mesh

-193

93

1.5

5.5

0.5

-100mesh

+193

93

1.5

5.5

0.5

+100mesh

-192

92

1.5

6.5

0.5

-100mesh

+192

92

1.5

6.5

0.5

+100mesh

-190

90

2.0

8.0

0.5

-100mesh

+190

90

2.0

8.0

0.5

+100mesh

-185

85

2.5

12.5

0.5

-100mesh

+185

85

2.5

12.5

0.5

+100mesh

-180

80

3.0

17.0

1

-100mesh

+180

80

3.0

17.0

1

+100mesh

+897

97

1.2

1.8

0.5

+80mesh

+896

96

1.2

2.8

0.5

+80mesh

+895

95

1.2

3.8

0.5

+80mesh

+894

94

1.2

4.8

0.5

+80mesh

+892

92

1.5

6.5

0.5

+80mesh

+890

90

2.0

8.0

0.5

+80mesh

 

Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:About the market issues of thermal insulation material and refractory material.
After all, most people have the characteristics of being accustomed with something and it will not change easily ; second, the South has few material manufacturer, but in the Northeast, there are thermal insulating and refractory material manufacturers, which is in shortage, however, but irt is in the minority, and in many areas it is not suitable for exploitation of mineral (due to heavy industry and agriculture land and other reasons). I hope that my answer will help you. first, in the Northeast, the refractory material is not very rich, but the thermal insulating and refractory material demand is very large; third; fourth, which material is used more relived, after all, we should take the transportation costs into account, and it will depend on the kilns construction engineers being willing to use which kind of material, and the thermal insulation material procurement in northeastern region is mostly from the north.
Q:How to make use of waste refractory materials whose main elements are alumina and mullite?
Crushing and pressing refractory bricks, or refractory parts . Such as welding positioner tracks use disposable tools.
Q:What is the function of refractory in ceramics?
In addition, the quality of refractory determines the finish and color of ceramic glaze.
Q:Fire rating of decoration materials
All light steel keel gypsum board is considered level A; if the wood finishes up to B2 grade fire rating depends on the proportion of the use of wood veneer and the proportion of this wood veneer fire grade, if the proportion of wood veneer is small,it can be considered level A
Q:What a blast furnace refractories generally?
Common refractories often use silica brick, semi-silica brick, fireclay brick, high alumina brick, magnesia brick, etc. special materials often used are AZS brick, corundum brick, directly bonded magnesia-chrome brick, carborundum brick, silicon nitride bonded silicon carbide bricks, nitrides, silicides, sulfides, borides, carbides and other non-oxide refractory materials; calcium oxide, chromium oxide, aluminum oxide, magnesium oxide, beryllium oxide refractory insulating refractory frequently used. material diatomite products, asbestos products, insulation boards. monolithic refractories have fettling frequently used, refractory ramming mixes, refractory castable, fire-resistant plastic, refractory clay, refractory gunning refractory projection material, refractory coatings, lightweight refractory castable, stemming etc.
Q:What needs to be paid attention to in the construction of high- temperature refractory mortar?
In the construction of high-temperature refractory mortar, the following matters should be noted: 1. Take out the organic fire blocking material and knead it into tha shape of a ball. If the temperature is too low, the blocking material along with the package can be put into 40-70℃ warm water and heated before any other operation. 2. During the use of high-temperature daub masonry stove, the minimum mortar joint should be 0.5mm and general mortar joint should be 3-5mm, which can solve the processing and fine grinding of refractory brick on the brick grinder. Besides, it is conducive to the health of workers, and can reduce the masonry effort, ensure the quality and speed up the construction progress. 3. When making urgent repair on the stove, if the joint is much too large, 2-3mm refractory pieces can be appropriately added into the high- temperature refractory mortar, and stirred to fill the joint so as to shorten the repair time and ensure normal production. 4. High- temperature refractory mortar can be painted inside various furnace body, and it should be guaranteed that the surface of the furnace body has no dust or debris before painting. The holes should be cleaned up before plugging. Lay, embed, and fill the blocking material into the gap of holes evenly. For larger holes, flame screen can be used as the framework to increase strength.
Q:Who knows that among refractory materials, insulation boards from which refractory material industry is superior in quality?
Using high temperature insulation material during casting process .In the molding, assembly the insulation board on the ingot head or install heat insulation cap . There are three ways to install the molded steel insulation board and install insulation board on at the head of the ingot, namely, clamping, nail fixation and mosaic technique.Compared with clay-based liner, the use of insulating board will improve high steel billet rate up to about 5% to 10%.
Q:How many types of fire-resistant material?
1. Acid fire-resistant material refers to one with more than 93% SiO2. It is featured by resistance to the corrosion of acidic slag ad high temperature and easy to react with alkaline molten slag. 2. Alkaline refractory material generally refers to one with magnesium oxide or magnesium oxide and calcium oxide as the main component. It has high refractoriness and strong resistance to basic slag. 3. Silicate aluminum refractory material refers to one with SiO2, Al2O3 as the main component. According to the content of Al2O, it can be divided into three categories: half siliceous (15-30% Al2O3), clay (Al2O3 30 ~ 48%), high aluminum (more than 48% of Al2O3). 4. Fused cast refractory material refers to shaped refractory products made by high temperature melting and casting.
Q:Procedures for producing common refractory materials?
The general procedures of producing refractory materials include calcination of raw materials, selection of raw material , crushing, grinding, screening, mixing, ageing mixture, molding, drying, burning and etc. At present, the refractory factory usually purchases the calcined clinker, so the calcination of raw material is no longer a consideration of common refractory plants.
Q:What is the common inorganic fireproof and thermal inuslation matertial?
Ceramic foam insulation board is made from clay tailings, ceramic broken flake and river silt, which is the closed ceramics material with high porosity roasted in high temperature by advanced production technology and foam technology. Products have fire retardant, small deformation coefficient, aging resistance, stable performance, good environmental protection, good compatibility between wall base and plastering layer, good safety and soundness and a lifetime as long as the building itself.

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range