Product Description:

Usage of Calcined bauxite
1.Aluminium industry.

2.Precision casting.

3.Refractory industry.

4.Silicic acid aluminium firefibre

5.Mixed with magnesium oxide,it can be an nice bonding agent,especially for pouring entire steel teeming ladle lining

6.Manufacture bauxite cement,grinding abrasives.ceracmic industry,and chemical industry for making aluminium compounds

Packaging & Delivery

Packaging Details:within 15 days after receiving L/C or Payment
Delivery Detail:Packing in 25kg bag or 1mt big bag

Specifications

Bauxite 
1 Al2O3:>=85% 
2 Fe2O3:<=2.0% 
3.Bulk Density:>=3.0g/cm3 
5. refractory/welding industry

 AL2O3 85%min China Calcined Bauxite Manufacture

 

1. Calcined bauxite 
AL2O3:70% min.
FE2O3:2% max.
SIZE: 1-5MM 90% min.

china calcined bauxite manufacturer since 1999 
purity of al2o3 75%-90% 
rotary kiln calcined bauxite 
self-owned bauxite mines

 

 

Specifications of Calcined bauxite

 

Grade

AL2O3

SIO2

FE2O3

TIO2

K2O+Na2O

CaO+MgO

Bulk density

HX75

75min

≤17

≤3.0

≤4.0

≤0.3

≤0.5

≥2.70

HX80

80min

≤12

≤3.0

≤4.0

≤0.3

≤0.5

≥2.80

HX85

85min

≤8

≤2

≤4.0

≤0.3

≤0.5

≥3.00

HX86

86min

≤7

≤2

≤4.0

≤0.3

≤0.5

≥3.10

HX87

87min

≤6

≤2

≤4.0

≤0.3

≤0.5

≥3.20

HX88

88min

≤5

≤1.8

≤4.0

≤0.25

≤0.5

≥3.25

HX90

90min

≤3

≤1.8

≤4.0

≤0.25

≤0.5

 ≥3.3

Moisture(max)

0.50%

 

Size of Calcined bauxite

Section sand:0-0.3mm,0-0.5mm,0-1mm,1-3mm,3-5mm,5-8mm.

Fine powder:100#-0,200#-0,325#-0

Moh’s hardness: 7-8

Melting point:1770-2000 C


AL2O3 85%min China Calcined  Bauxite  Manufacture


Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:what's the seal of fireproofing material?
Folded organic putty takes organic material as bond,it has certain flexibility or plasticity while using, and it's products are thick liquid or cement shaped object. Folded WXY-II is powered solid that takes inorganic materials as main components, it has certain workability while used with admixture. Folded fire retardant bag is the packaged object made by fireproofing material, and it's suitable for fireproofing seal of larger openings or fire separation of cable bridge(fire retardant bag also refers to fireproof bag) Folded fire retardant module is the solid made by fireproofing material with certain shape and size, and it is easy for cutting and drilling, suitable for fireproofing seal of opening and cable bridge. Folded seal board is made by fireproofing material, it's easy for cutting and drilling, suitable for fireproofing seal of large opening. Folded foam seal is a kind of fireproofing material that can automatically expand and foam and sealed by opening after injecting the foam into opening. Folded sealing strip is a product or flexibility coiled material mede by fireproofing material with certain geometry shape. Folded sealing gum is a kind of liquid fireproofing material that has a function of fireproofing and sealing. Folded fire retardant bag is soft and windable tape-shaped product made by fireproofing material, it is winded on the external surface of plastic pipe and fixed with steel belt or other proper methods, it's the expansion, squeezing and softening pipe after contacting with fire, opening left by burning or soften of seal plastic pipe. Folded fire retardant ring is the product made by fireproofing material and metal shell, it's covered on the external surface of the plastic pipe, expanding and sealing after contacing with open fire, the opening left by burning and soften of plastic pipe when it passes through the opening of wall and floor.
Q:What's the difference of fire-resistant material's density, specific gravity and bulk specific gravity?
It usually used to test lightweight refractory. Density can be divided into apparent density (usually called as density) and true density: apparent density includes blow hole inside the sample; Unit weight is using quality to divide volume of sample and specific weight is used to represent liquid.
Q:Which refractory material is better in China? Industrial furnace, mainly in non-ferrous industries, glass kiln, cement kiln business.
Such solid nano microporous insulation material with nano inorganic refractory powder special, with a huge surface area, nano particles contact between the minimum point contact point contact thermal resistance is very large, the heat conduction effect of the material becomes very small, resulting in heat conduction coefficient of solid such nano porous insulation materials very small; nano pores formed of nanoparticles, the average size of 20 nm, and the average free path of molecular thermal motion at room temperature under static air is 60 nm, thus locking the air molecules in powder within nano pores, making the micro convection heat transfer effect between the stationary air molecules disappeared. The room temperature thermal conductivity of solid such nano microporous insulation material is lower than the static air; at high temperature, the main effect of heat transfer heat radiation, Good energy-saving insulation materials with nano microporous infrared additive special, stop at a high temperature and reflected infrared radiation, reduce the heat radiation effect to the lowest point, the radiation heat transfer coefficient of materials under high temperature is reduced to the lowest value.
Q:I would like to ask a friend that how much is the fire endurance of level A fireproofing glass?
Fireproofing doors can be divided into Class A, Class B and Class C by the fire endurance, the fire endurance is seperately not less than 1.20h, 0.90h and 0.60h. Fireproofing glass is a kind of special glass which can retain its integrity and insulation in the prescribed fire test, it can be divided into three categories according to fire resistance rating: class A is the fireproofing glass with refractory integrity and refractory thermal insulation. Such glass has the properties of transmittance, fireproofing (smoke insulation, fire insulation, heat radiation shielding), sound insulation and shock resistance, which is suitable for architectural steel and wood fire doors, windows, partition walls, daylighting roof, ceiling screen, perspective floor and other building components required both transparent and fireproofing. Class B is a fireproofing glass with refractory integrity and thermal radiation intensity. Such fireproofing glass is mostly composite fireproofing glass with transmittance, fireproofing and smoke insulation. Class C is a fireproofing glass with refractory integrity. Such glass has the features of transmittance, fireproofing, smoke insulation and high strength. it can used in partition wall, fire window and outdoor curtain wall without the thermal insulation requirements. fireproofing glass can be divided into composite fireproofing galss and monolithic fireproofing glass by the structure.
Q:Who knows about roof fireproofing materials?
Roof water proofing materials: synthetic polymer waterproof rolls, high polymer modified asphalt waterproof coiled material, sheet metal, synthetic polymer waterproof coating, one-component water curing polyurethane waterproof coating, penetration crystalline waterproof coating. Secondly, we have to choose materials that are suitable for roof water proofing. The right waterproof materials have better waterproof performance, TS-3B one-component water curing polyurethane waterproof coating is very suitable and the performance is good. Since traditional roof waterproofing materials have requirements on the moisture content of the formation level which should be less than 9%. It is really important to choose which materials to repair leaking roofs. Kitchens and toilets are moisture, the formation levels of buildings are hard to satisfy requirements, thus, waterproof layer and formation level are easily get separated and are ineffective in waterproofing.
Q:What are the differences between first-level fire-resistant materials and second-level fire-resistant materials?
Level B1: building materials with flame retardancy: this kinds of materials have good effect in flame retardation. Under the case of open fire or high temperature, it is not easy to be ignited and spread quickly, and when the fire source is removed, fire would stop immediately. Level B2: combustible building materials: combustible building materials also have effect in flame retardation. It will get burnt as soon as it meets open fire or high temperature, so it can easily give rise to rampant fire, such as wooden pillars, wood roof trusses and wooden stairs.
Q:How many kilns using refractories are needed? What are the furnaces respectively?
Kiln and five hundred-degree centigrade thermal equipment need to use refractories, glass furnaces, electric arc furnaces, mixer, cement rotary kiln, open hearth furnace and limestone kiln; in fact, when the temperature is more than four, the mesh belt furnace, blast furnace, cupola oven, stove, pushing plate kiln, furnace, heat treatment furnace, roller kiln, down draft kiln, ladle, coke, shuttle kiln,etc.
Q:How long is the duration of fire resistance that fireproof door of level B can endure?
The national standard for fireproof door of level B is 1.5h, which must be achieved. The data GB12955-2008 means that the door leaf of raw material is 0.8mm-1.2mm in thickness and door frame is 1.2mm-1.5mm in thickness. And other metal melting temperature shall not be less than 950℃, the duration of fire resistance shall not be less than 0.9 hours. Fire department will check and accept based on the manufacturer's inspection report, so you have to refer to manufacturer's inspection report if you want to know more in detail.
Q:What are the advantages and disadvantages of new external wall fireproof and thermal inuslation matertials?
STP has a certain chance to self-destruct. After the sealing layer is damaged, the property will be bothered. When filling the foam glass, burst foam cement and low-strength glass fiber, the structural requirements are very high with big spraying limitations. As everyone knows that rock wool absorb organic matters, and the government do not allow us to use self-insulation, so it is not the mainstream with too low adoption rates. In fact the owners shouldn't worry about this problem. Since the developers have installed it for you, it is useless to worry about it. The other is that for those who want the original balcony closed up, if you want to shovel the original balcony wall insulation, you must pay attention to ask the construction team before you start. Because it is common that the cold bridges formed thereby will cause water seepage and moisture condensation in the balcony.
Q:Is there a worker in (Jigang refractory plant)?
Units in this way, it is necessary to slowly boil it, wages will come up. You are a labor worker, and can not share with the stock system staff. There's a difference between salary and vacation.

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range