abrasive white fused alumina (WFA) for sand blasting 72 mesh

Ref Price:
Loading Port:
China Main Port
Payment Terms:
TT OR LC
Min Order Qty:
-
Supply Capability:
-

OKorder Service Pledge

Quality Product

Order On-line Tracking

Timely Delivery

OKorder Service Pledge

Credit Rating

Credit Services

Credit Purchasing

Share to:

Product Description:

Packaging & Delivery

Packaging Detail:25kg/plastic bag, 1mt/jumbo bag or as you require
Delivery Detail:within 7 days after sign the contract or your deposit

Specifications

white fused alumina
Direct Manufacturer
lapping & polishing media
Ceramic grinding wheels

                       72 mesh abrasive white fused alumina (WFA) for sand blasting

White Fused Alumina/ WFA

White Fused Alumina, a kind of high-grade refractories, was made from the high quality alumina by melting above 2000 in the electric arc furnace and cooling. It is white with the main crystal phase alpha-Al2O3.The white alumina produced in titling electric arc furnace has the advantage of high bulk density and low porosity and the volume stability and thermal shock resistance can be improved.

Advantages

Flexible price policy

Equipped full line of test method.

Brilliant produce&supply&delivery ability

We passed the certification of ISO9001:2000

White fused alumina has Al2O3 content 99% min

All products will be supplied according to customers different requirement.

The laboratory is certified by government Inspection Bureau, that assures its quality stability.

Technical Data:

Application

specification

major chemical content %

AL2O3

Na2O

SiO2

K2O

Fe2O3

abrasive

F

8#-60#

99.5min

0.26max

0.08max

0.06max

60#-100#

99.5min

0.26max

0.09max

0.06max

120#-150#

99.5min

0.26max

0.10max

0.06max

180#-220#

99.5min

0.26max

0.12max

0.10max

230#-800#

99.3min

0.32max

0.15max

0.10max

1000#-3000#

99.1min

0.35max

0.18max

0.10max

refractory

Section sand

0-1mm

99.5min

0.29max

0.30max

0.02max

0.06max

1-3mm

3-5mm

5-8mm

10-20mm

0.3-1mm

0-0.3mm

1-2mm

0.5-1.5mm

Fine powder

100#-0

99.0min

0.40max

0.30max

0.03max

0.20max

Moh's hardness

≥9.0

true density(g/cm3)

≥3.95

propotion

≥3.6

porosity

≤8.5

As refractoriness

White Fused Alumina is the main starting material to produce high-grade unshaped and shaped refractoriness and is widely used in the field of iron-steel industry,ceramics,petrochemical industry etc. It is the ideal material to produce the unshaped refractoriness such as large ladle castables,medium and high grade BF trough castables,gunning material,pre-cast shapes and is the main material to produce alumina products such as corundum bricks, corundum and mullite-corundum sagger,refined porous plug bricks, monolithic lance composite nozzle, lining material for high temperature industrial furnaces,etc.

As abrasives

White Fused Alumina can be used as consolidation & coating abrasives, wet or dry sprayed grit, suitable for ultra-precise grinding and polishing in the crystal and electronic industry and can be used to produce high-grade refractoriness. It is suitable to machine high stiffness &high tensile strength materials such as chilled steel, alloyed steel, high-speed steel, high carbon steel, etc. In addition, it can be used as catalyst, insulator, precise foundry sand, etc.

Size available:

Abrasive tool: F10-F220,F230-F1200;P12-P220;

Refractory  : 0-1mm,1-3mm,3-5mm,5-10mm;100mesh,325mesh;

Other size is available as required;          

Packing:

25kg/bag,40bags/big bag;

1000kg/big bag;

1000kg/big bag with pallet packing;

Other packing is allowed as required.

Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:How to divide fire resistant level of fire door?
The classification of fire resistant level of fire door: Grade A is not less than 1.2h. Grade B is not less than 0.9h. Grade C is not less than 0.6h. It is suitable for fire door with different levels: Grade A: Equipment room (such as fire-pump room,power distribution room, generator room, smoke control fan room, etc) door, fire compartment, door on firewall; Grade B: Eclosed staircase, front door of stair room, smoke-proof staircase and fire elevator share lobby door, front door of fire elevator, household door which directly opens to front room or shares room; Grade C: The vertical shaft door, such as strong electric wells, weak electric wells, pipe shaft door and air conditioning facilities. I hope this information can help you.
Q:How long is the duration of fire resistance that fireproof door of level B can endure?
The national standard for fireproof door of level B is 1.5h, which must be achieved. The data GB12955-2008 means that the door leaf of raw material is 0.8mm-1.2mm in thickness and door frame is 1.2mm-1.5mm in thickness. And other metal melting temperature shall not be less than 950℃, the duration of fire resistance shall not be less than 0.9 hours. Fire department will check and accept based on the manufacturer's inspection report, so you have to refer to manufacturer's inspection report if you want to know more in detail.
Q:What's the A grade fireproofing material?
A grade fireproofing material: 1. fire-proof plate; 2. fireproof wooden door; 3. fireproof wooden window frame; 4. fire resisting shutter; 5. fireproof and mothproof wood; 6. fireproof glove compartment; 8. fire retardant coating; 9. fire-proof sealing material.
Q:What crusher is used for raw material of broken refractory material? What is the rough crushing process? What are the materials? Thank you!
Common faults and causes of magnetic separator. 1. Motor of magnetic separator is overheated and its sound is not normal. Reasons for this failure are: 1) lubrication of bearing is bad or badly worn; 2)fan blade falls off or wears; 3)bad contact of switching circuit or disconnected to run a single phase; 4) voltage is too low. 2. Reasons for this failure due to overheated speed reducer are: 1) lack of oil or poor kerogen; 2) wear between gear and worm, or poor mesh; 3)poor lubrication of bearing or serious wear. 3. The sound of magnetic separator during operation is abnormal, lattice ball mill. Cylinder is stuck by obstacle, and even the cylinder can not rotate. The bottom box vibrates. Reason for this failure is often that it is stuck by objects in drag flask, otherwise magnetic patch falls off so that the cylinder screaks and pierce tube when it is serious. At this time, car should be stopped for maintenance and troubleshooting. Only when we master common faults and reasons of magnetic separator can we timely identify problems and solve problems. Better maintenance and repair of magnetic separator equipment are an important prerequisite to properly use equipment and ensure the construction.
Q:How long is the fire-fighting time of A class fire resisting window?
Fire resisting window' duration of fire resistance: A class window, fire insulation ≥1.50h and fire resistance integrity ≥1.50h. Fire resisting window can be divided into three kinds: 一. window frame and sash framework adopt fire resisting window with steel manufacture ; 二. window frame and sash framework adopt fire resisting window with wooden manufacture; 三. window frame adopt steel and sash adopt wooden material or window frame adopt wooden material and sash framework adopt fire resisting window with steel material.
Q:Who knows the fire rating of fire partition with steel stud?
1 hour. It is in line with the fireproof test standards of national building materials . CaSo4.2H2O is molecular structural formula of gypsum which contains 20% water, crystal water and free water. When 10% water slowly evaporates on the flame surface, there is still 10% crystal water. Itself is grade A fire retardant material. It can reach up to four hours at most.
Q:How is the grading of the level A new material fire insulation material?
The standard to distinguish level A and level B is the different fireproofing coefficient. The level A is non-combustible. The level B is divided into B1, B2 and B3. B1 is flame retardant, B2 combustible and B3 flammable. The level A is commonly phenolic aldehyde, rock wool, thermal mortar, foam ceramics, foam glass and foam concrete on the current market. Among the advantages of level A materials, the biggest one is foam concrete currently, also known as foam cement, which the Xuzhou Green Year EEB company's main produces.
Q:Could you tell me the fire-resisting time of class B fire proof door?
Could you tell me the fire-resisting time of class B fire proof door?
Q:What refractories have good mechanical property resistance and heat expansion and cold contraction property?
Aluminium oxide ceramics. I would like to know that what kinds of refractory materials can combine together and what kind of masonry way can be used for these materials so as to achieve the perfect combination.
Q:Which kind of refractory floor is easy to use? ?
Recommend: Yong Wei fireproof board Henan Yong Wei Anfang Co., Ltd., located in Qinbei industrial agglomeration area, Qinyang City, Henan Province, was founded in 1995. It strated from the initial one fire decorative plate production line. After years of development, it has become the biggest fireproof decorative board production base with 25 fireproof board production lines.

1. Manufacturer Overview

Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information  
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range