30mm-130mm Good Wear-resistant Forged Grinding Ball From China

Ref Price:
Loading Port:
Qingdao Port
Payment Terms:
TT or LC
Min Order Qty:
25M.T. m.t.
Supply Capability:
200000M.T./Year m.t./month

OKorder Service Pledge

Quality Product

Order On-line Tracking

Timely Delivery

OKorder Service Pledge

Credit Rating

Credit Services

Credit Purchasing

Share to:

Product Description:

Chemcial Elements of 30mm-130mm Good Wear-resistant Forged Grinding Ball From China

Type

Name

C

Mn

Si

Cr

S

P

F01

20MN

0.12-0.22

1.00-1.60

0.60-0.80

≤0.25 

≤0.035 

≤0.035 

F02

45#

0.42-0.50

0.50-0.80

0.17-0.37

≤0.25 

≤0.035 

≤0.035 

F03

50MN

0.48-0.56

0.70-1.0

0.17-0.37

≤0.25 

≤0.035 

≤0.035 

F04

60MN

0.57-.0.65

0.70-1.0

0.17-0.37

≤0.25  

≤0.035 

≤0.035 

F05

65MN

0.60-0.70

0.90-1.20

0.17-0.37

≤0.25  

≤0.035 

≤0.035 

F06

B2

0.70-0.85

0.70-0.80

0.17-0.37

0.2-0.7

≤0.03 

≤0.035

 

Specification and Hardness of 30mm-130mm Good Wear-resistant Forged Grinding Ball From China

Type

Name

Impact Test AK.J/cm2

Endurance Test  Times(5m)

Dia 25mm-60mm

Dia 70mm-100mm

Surface

Core

Surface

Core

F01

20MN

≥12

≥10000

≥42

≥48

≥40

≥45

F02

45#

≥12

≥10000

≥52

≥48

≥53

≥46

F03

50MN

≥12

≥10000

≥56

≥50

≥55

≥50

F04

60MN

≥13

≥12000

≥58

≥52

≥58

≥50

F05

65MN

≥15

≥12000

≥62

≥54

≥58

≥52

F06

B2

≥15

≥12000

≥62

≥55

≥58

≥52

 

Size and Weight of 30mm-130mm Good Wear-resistant Forged Grinding Ball From China

SPECIFICATION(mm)

EACH WEIGHT (Kg)

NO/MT

φ25

0.063

15873

φ30

0.11

9091

φ40

0.257

3891

φ50

0.5

2000

φ60

0.867

1153

φ70

1.37

729

φ80

2.05

487

φ90

2.9

345

φ100

4

250

φ110

5.3

188

φ120

6.8

147

 

 

 

Send a message to us:

Remaining: 4000 characters

- Self introduction

- Required specifications

- Inquire about price/MOQ

Q:Cast iron, casting parts 5
1, qualified enterprises will directly iron ore into molten iron, and then poured into the mold, such a good product performance. I work in the cast iron industry, which I can tell you for sure.2, this, like the Great Wall Motor Company has its own parts production department, as well as the corresponding mold center, so it will be their own casting. If the manufacturer does not have these departments, they can only place orders for others to do.
Q:What should I pay attention to when designing a casting structure?
The basic structure of unit 3 in the design of metal casting casting and its parameters are selected, usually should also pay attention to: (1) because of the metal type heat quickly, so the metal type casting minimum wall thickness should be bigger than the sand casting casting casting; (2) the inner wall of the internal ribs and the thickness of a should be connected the outer wall thickness of 0.6 to 0.7, or as the inner wall (rib) cold slowly, cracks in the wall at the junction in the casting shrinkage; (3) to prevent generating white grey cast iron, in addition to taking measures in the process, must make the wall thickness is not too thin (some information that cast fillet at the corner of the wall thickness of 15mm or more, with metal casting casting must be in the corner, for Aluminum Alloy, metal casting magnesium alloy castings shall not be less than 3 ~ 4m; (4) because of the metal type and the core that, for To facilitate the extraction of castings and casting out type, slope casting should be suitably large than sand casting metal casting, the general should be 30% ~ 50%, it should be pointed out that in addition to the height of the slope of casting size and alloy type, wall, is also related to the casting surface position, where the cooling and contraction of the metal type the surface of casting surface can be designed from the tendency of small inclination, while casting shrinkage tend to be pressed on the surface of metal casting type should be given greater inclination.
Q:How to get rid of casting sand inside casting parts?
Are you saying that in the sand casting cavity? We use the manual blast, he is like a pipe will be automatic shot out of the grit, into the casting cavity, to remove the internal cavity in the purpose of casting sand!
Q:The difference between cement sand castings, resin sand castings and vacuum casting parts
The clay wet sand castings casting weight from a few kilograms until tens of kilograms, but the clay dry type of casting production can be weighed dozens of tons.For medium and large castings, cast iron, cast steel can be self hardening sand with resin can be water glass sand production, can obtain the precise size, smooth surface castings, but casting precision, surface roughness, density and microstructure, mechanical properties and material cost of sand casting production is often poor, so when the higher performance requirements of castings, should adopt other casting methods, such as casting (lost wax casting), die casting, low pressure casting.
Q:When the blank is a casting, the margin is evenly distributed, how should rough machining? Twenty
Problem one,1, according to drawings, castings, material requirements and machine power, choose the right diameter of roughing tools, and can process this material blade type.2, according to the actual size of the casting blank, calculate the number and path of the knife, pay attention to small cutting depth, large feed, cutting width, to ensure that the tool diameter 80 - 90%, the amount of not full knife cutting, this tool and machine tool damage.Question two,If they can not change the casting blank allowance under the condition that the quantity large diameter cutter, such as milling cutter main angle 7560 degrees can give reasonable processing parameters, the same cutting depth should not be too large, because in the same machine power, tool diameter increases, cutting depth will need smaller.
Q:The casting sand is going on
Dispersed sand inclusion is common on the surface and subcutaneous of steel castings, often concentrated on the outer surface of the upper box and the inner surface of the lower case, and a few of them are inside the cast steel parts.
Q:Why do casting parts have air holes?
There are many reasons for casting porosity, mainly due to:1. smelting process is unreasonable, metal liquid absorbs more gas;2. the gas in the mold invades the metal liquid;3. from the mold is more water brush, core dry;4. the casting has poor ventilation;5. ladle tools are not dry.Wait。
Q:What is the casting material?
Kdl1588n said in detail, casting a lot of material, steel, iron, aluminum, copper, zinc, etc. can be, valuable, as well as gold and silver, the most common on cast steel and cast iron, cast aluminum and so on.
Q:Heat treatment process and purpose of casting parts
Methods: artificial aging or natural aging (also called normalization) treatment.Artificial aging: heating to 2-3 Baidu, it is best to apply mechanical vibration, and maintain a period of time.
Q:Explain the heat treatment effect of casting parts, forging parts and welding parts
Good welding of low carbon steel (alloy), probably because the weld workpiece rigidity, fast cooling, the weld internal crystallization of brittle microstructure (martensite), so after welding or welding process welding using self heat, reasonable arrangement of weld, welding seam and heat affected zone heat treatment. The welding heat treatment is often used to preheat before welding, after welding withasbestos cloth covering slow cooling annealing, reach the purpose, its main function is to reduce the internal stress, improve the weld microstructure of martensite formation, reduce brittle tendency, preventing welding cracks.
Milling Queen was founded in 2012, located in Hushi Town, Jiangyin City, Jiangsu Province. Our company is next to the beautiful Yangzi River and the China first village-Huaxi Village. It is about 2km distance from expressway, 8 km from the Changjiang port, 60km from the Wuxi International Airport with convenient traffic extending all directions.

1. Manufacturer Overview

Location Jiangyin City, Jiangsu Province, China
Year Established 2012
Annual Output Value Above US$100 Million
Main Markets South America; Oceania; Eastern Europe; Africa
Company Certifications ISO9001;IS014001 Certificate

2. Manufacturer Certificates

a) Certification Name  
Range  
Reference  
Validity Period  

3. Manufacturer Capability

a)Trade Capacity  
Nearest Port Qingdao Port; Tianjin Port; Shanghai Port
Export Percentage
No.of Employees in Trade Department 5 - 10 People
Language Spoken: English; Chinese; Spanish; Portuguese; Russian
b)Factory Information  
Factory Size: 10,000-30,000 square meters
No. of Production Lines Above 10
Contract Manufacturing Grinding Ball; Grinding Rod; Cylpeb; Grinding Media; Ball Mill Ball
Product Price Range Average